A super-flat glaze frit and a method of manufacturing super spar from the same

A technology of ultra-flat glaze and super crystal, which is applied in the field of preparation of super crystal, can solve problems such as making breakthroughs, achieve high initial melting point, increase the transparency of the glaze surface, and have a good effect of transparency

Active Publication Date: 2016-05-04
江西宏瑞新材料有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The surface is smooth and smooth, and the glazed surface has a good sense of transparency. It has not been able to make a breakthrough in technology.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A super-flat glaze frit and a method of manufacturing super spar from the same

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] An ultra-flat glaze frit is prepared from the following raw materials in parts by mass: potassium feldspar: 53 parts, wollastonite: 25 parts, calcined talc: 15 parts, and barium carbonate: 7 parts.

[0028] The firing method of frit is:

[0029] (1) Weigh the raw materials and mix them evenly;

[0030] (2) Melt at a temperature of 1500-1600°C and keep warm for 2-3 hours;

[0031] (3) Water quenching and drying to obtain frit with high initial melting point and low expansion coefficient.

[0032] A super-flat glaze, which is made of the above-mentioned frit and raw material in a ratio of frit:raw material=80:100.

[0033] The composition of the raw material is: 45 parts of quartz, 8 parts of potassium feldspar, 10 parts of wollastonite, 7 parts of burnt talc, 10 parts of barium carbonate, 10 parts of zinc oxide, 3 parts of strontium carbonate, 4 parts of clay, and 3 parts of burnt soil , in parts by mass.

[0034] A preparation method of super crystal, the steps are ...

Embodiment 2

[0037] An ultra-flat glaze frit is prepared from the following raw materials in parts by mass: 60 parts of potassium feldspar, 18 parts of wollastonite, 15 parts of calcined talc, and 7 parts of barium carbonate; the firing method is as in Example 1 .

[0038] A super-flat glaze, which is made of the above-mentioned frit and raw material in a ratio of frit:raw material=80:100.

[0039] The composition of the raw material is: 45 parts of quartz, 8 parts of potassium feldspar, 10 parts of wollastonite, 7 parts of burnt talc, 10 parts of barium carbonate, 10 parts of zinc oxide, 3 parts of strontium carbonate, 4 parts of clay, and 3 parts of burnt soil , in parts by mass.

[0040] A preparation method of super crystal, the steps are as follows:

[0041] Apply a layer of bottom glaze on the biscuit, adopt the glaze pouring process, and the glaze is 400g; then apply a layer of the above-mentioned super flat glaze on the green body with the bottom glaze, the glaze is 1050g, and it...

Embodiment 3

[0043] An ultra-flat glaze frit, prepared from the following raw materials by mass: potassium feldspar: 65 parts, wollastonite: 13 parts, calcined talc: 15 parts, barium carbonate: 7 parts; the firing method is as described in the examples 1.

[0044] A super-flat glaze, which is made of the above-mentioned frit and raw material in a ratio of frit:raw material=80:100

[0045] The composition of the raw meal is:

[0046] 45 parts of quartz, 8 parts of potassium feldspar, 10 parts of wollastonite, 7 parts of burnt talc, 10 parts of barium carbonate, 10 parts of zinc oxide, 3 parts of strontium carbonate, 4 parts of clay, and 3 parts of burnt earth, in parts by mass. A preparation method of super crystal, the steps are as follows:

[0047] Apply a layer of bottom glaze on the green body of 890×890mm, adopt the glaze pouring process, the glaze is 400g, and then apply a layer of the above-mentioned super flat glaze on the green body with the bottom glaze, the glaze is 1050g, 1180...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a super-flat glaze frit and a method of manufacturing super spar from the same. The super-flat glaze frit can allow glazes to have good viscosity and fluidity at high temperature. The frit and a raw material are used in match according to a mass ratio of (50-100):100. The super-flat glaze frit plays a large role in glazes to allow flatter glaze surfaces with high hardness and good transparency after firing. The frit has a high beginning melting point so as to avoid generation of gas bubbles. The cost of the super-flat glaze frit is 25% of the cost of one-firing minicrystal frit dry particles, thus greatly saving the cost.

Description

Technical field [0001] The present invention involves a method of super flat glaze melting and prepared by it. Background technique [0002] With the increasingly enrichment of material and culture, people have put forward higher requirements for tiles.Due to the luxurious decorative effect, the bright and flat glaze has always been a more preferred decorative material for consumers, and it is also a popular research topic in the ceramic industry.Due to the limitations of production technology technology, ceramic glazes are not pure, and their surfaces are more or less slightly uneven.The surface of the surface is smooth and flat, and the transparent glaze has not been able to make a breakthrough in technical. Invention content [0003] One of the purpose of the present invention is to provide an ultra -flat glaze melting block with a lower melting point with a higher melting point. [0004] Another purpose of the present invention is to provide an ultra -flat glaze containing t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/04
CPCC03C8/04
Inventor 刘晶徐新民
Owner 江西宏瑞新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products