Mg-Nd-Zn-Zr alloy material containing Y and preparation process thereof

A technology of alloy material and preparation process, which is applied in the field of Y-containing Mg-Nd-Zn-Zr alloy material and its preparation process, can solve the problems of less impact research, achieve obvious grain refinement, and increase elongation , The effect of improving the mechanical properties

Inactive Publication Date: 2016-04-27
黄晓艺
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, there are many studies on Gd and Y in Mg-Zr system at home and abroad, but there are few studies on the effect of adding higher content of Y on the structure and properties of Mg-Nd-Zn-Zr alloy with low zinc content.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Mg-Nd-Zn-Zr alloy material containing Y and preparation process thereof
  • Mg-Nd-Zn-Zr alloy material containing Y and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0008] The materials used in the experiment are pure magnesium (99.96% mass fraction), pure zinc (99.92%), magnesium zirconium master alloy (30% Zr) and magnesium yttrium master alloy (31.72% Y). The design alloy composition is shown in Table 1. The alloy is smelted in a resistance crucible furnace. RJ-2 covering agent is used for smelting. The smelting temperature is 770 °C. After the alloy is completely melted, it is left for 15 minutes. The diameter×height of the obtained alloy ingot is 60mm×130mm. The mechanical properties of the samples were tested by CSS-44100 universal electronic testing machine, and the tensile rate was 2 mm / min.

[0009]

[0010] Table 2 shows the room temperature mechanical properties of each alloy as-cast. It can be seen from Table 2 that when the content of rare earth element Y is 4% and 6%, the tensile strength, yield strength and elongation of the alloy gradually increase, and when the content of Y element is 6%, the alloy shows the best perf...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an Mg-Nd-Zn-Zr alloy material containing Y. The Mg-Nd-Zn-Zr alloy material is characterized by comprising the following components in parts by mass: 0.2 of Zn, 0.4 of Zr, 2.0 of Nd, 4-8 of Y, and the balance of Mg. A preparation process is characterized in that pure magnesium, pure zinc, 30% of Zr magnesium zirconium intermediate alloy and 31.72% of Y magnesium yttrium intermediate alloy are smelted by using a RJ-2 covering agent at a smelting temperature of 770 DEG C, are stood by 15 minutes after being totally molten, are poured in an iron mold, preheated to 200 DEG C, at 720 DEG C, and are molded by pouring.

Description

technical field [0001] The invention relates to a Y-containing Mg-Nd-Zn-Zr alloy material and a preparation process thereof. Background technique [0002] Magnesium alloy is currently the lightest metal structural material available in industry. It has the advantages of small mass, high specific strength and specific stiffness, good thermal conductivity and vibration damping, and easy machining. It is widely used in aerospace and aviation industries. At present, the low strength and plasticity of magnesium alloys are one of the main bottlenecks restricting the development and application of magnesium alloys. Adding rare earth elements can effectively strengthen and purify the alloys, improve the casting properties, and improve the high-temperature strength and plasticity of the alloys. Mg-Zn-Zr alloys are commonly used wrought magnesium alloys. The typical representative is ZK60 magnesium alloy with high zinc content. However, due to high zinc content, poor heat resistance a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C23/06C22C1/03
Inventor 黄晓艺
Owner 黄晓艺
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com