aluminum alloy ingot

A technology for aluminum alloy ingots and impurities, applied in the field of aluminum alloy ingots, can solve the problems of aluminum alloys prone to cracks and corrosion, low aluminum alloy density and high strength, and achieves improved casting appearance, excellent corrosion resistance, and good high-temperature mechanical properties. Effect

Active Publication Date: 2018-01-02
肇庆南都再生铝业有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The density of aluminum alloy is low, but its strength is relatively high, which is close to or exceeds that of high-quality steel, and its plasticity is good. Therefore, aluminum alloys are mostly used in casting products. The existing aluminum alloys are prone to cracks and corrosion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • aluminum alloy ingot
  • aluminum alloy ingot

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] An aluminum alloy ingot, comprising the following components in weight percentage: Si: 7.2%, Cu: 1.2%, Mg: 0.1%, Fe: 0.2%, Zn: 1.2%, Ni: 0.2%, Sn: 0.1%, Sr : 1.2%, Ti: 2.1%, B: 2.1%, Sb: 1.2%, As: 0.3%, RE: 0.22%, LaCe: 0.4% and Pr: 0.3%, the balance is Al and unavoidable impurities, and Impurities ≤0.1%.

Embodiment 2

[0019] An aluminum alloy ingot, comprising the following components in weight percentage: Si: 11.4%, Cu: 1.5%, Mg: 0.3%, Fe: 0.4%, Zn: 1.4%, Ni: 0.4%, Sn: 0.3%, Sr : 2.4%, Ti: 2.4%, B: 2.4%, Sb: 1.4%, As: 0.5%, RE: 0.44%, LaCe: 1.4% and Pr: 0.5%, the balance is Al and unavoidable impurities, and Impurities ≤0.1%.

Embodiment 3

[0021] An aluminum alloy ingot, comprising the following components in weight percentage: Si: 9.3%, Cu: 1.4%, Mg: 0.2%, Fe: 0.3%, Zn: 1.3%, Ni: 0.3%, Sn: 0.2%, Sr : 1.8%, Ti: 2.3%, B: 2.3%, Sb: 1.3%, As: 0.4%, RE: 0.33%, LaCe: 0.9% and Pr: 0.4%, the balance is Al and unavoidable impurities, and Impurities ≤0.1%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an aluminum alloy ingot. The aluminum alloy ingot is prepared from, by weight percent, 7.2%-11.4% of Si, 1.2%-1.5% of Cu, 0.1%-0.3% of Mg, 0.2%-0.4% of Fe, 1.2%-1.4% of Zn, 0.2%-0.4% of Ni, 0.1%-0.3% of Sn, 1.2%-2.4% of Sr, 2.1%-2.4% of Ti, 2.1%-2.4% of B, 1.2%-1.4% of Sb, 0.3%-0.5% of As, 0.22%-0.44% of RE, 0.4%-1.4% of LaCe, 0.3%-0.5% of Pr and the balance Al and inevitable impurities, wherein the content of the impurities is not larger than 0.1%. The aluminum alloy ingot is good in comprehensive performance, resistant to corrosion and stable in performance.

Description

technical field [0001] The invention relates to the field of metal materials, in particular to an aluminum alloy ingot. Background technique [0002] Aluminum alloy is an alloy composed of aluminum as a matrix element and then adding one or more alloying elements. The density of aluminum alloy is low, but its strength is relatively high, and it has excellent electrical conductivity, thermal conductivity and corrosion resistance, etc., which makes aluminum alloy materials widely used in the power industry. [0003] Aluminum alloy is an extended product of pure aluminum. The density of pure aluminum is small (ρ=2.7g / m3), about 1 / 3 of that of iron, and its melting point is low, about 660°C. Aluminum has a face-centered cubic structure, so it has High plasticity (δ: 32-40%, ψ: 70-90%), so it is easy to process, can be made into various profiles and plates, and has good corrosion resistance. However, the strength of pure aluminum is very low, so it is not suitable for structura...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C21/02
CPCC22C21/02
Inventor 马革兰
Owner 肇庆南都再生铝业有限公司
Features
  • Generate Ideas
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com