Medium carbon steel chamfering copper plate continuous casting mold covering slag and preparation method thereof

A continuous casting mold and mold powder technology, which is applied in the field of medium carbon steel chamfering copper plate continuous casting mold mold powder and its preparation, can solve the problem of unsuitable chamfering continuous casting mold, unresolved billet corner cracks, narrow Problems such as the quality problems of the transverse cracks at the corners of the side bulge, etc., achieve the effect of reasonable chemical composition ratio, good heat transfer capacity, and solving the effect of longitudinal cracks

Active Publication Date: 2016-04-27
XIXIA LONGCHENG METALLURGICAL MATERIALS CO LTD
View PDF12 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, these patents still do not solve the quality problems of corner cracks, narrow side bulging, and corner transverse cracks of the slab, and are not suitable for chamfering continuous casting mold operations

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A medium carbon steel chamfering copper plate continuous casting mold powder, its chemical composition and weight percentage are: CaO: 40%, SiO 2 : 23%, MgO: 5.5%, Li 2 O: 1.5%, Al 2 o 3 : 5%, Na 2 O: 10%, F: 7% and C: 8%.

[0032] The preparation method of the above-mentioned medium carbon steel chamfering copper plate continuous casting mold powder comprises the following steps:

[0033] (1) Ingredients: Prepare various raw materials according to the above chemical composition and their weight percentages, such as: wollastonite, limestone, quartz sand, albite, alumina stone, magnesia, lithium carbonate, soda ash, fluorite, carbon Quality material carbon black, binder carboxymethyl cellulose sodium salt CMC;

[0034] (2) Melting: use an electric furnace to melt various raw materials except carbonaceous materials and adhesives;

[0035] (3) Water quenching: the molten slag directly enters the water pool to cool and solidify into a glass body;

[0036] (4) Drying:...

Embodiment 2

[0042] A medium carbon steel chamfering copper plate continuous casting mold powder, its chemical composition and weight percentage are: CaO: 41%, SiO 2 : 23%, MgO: 6.2%, Li 2 O: 2.2%, Al 2 o 3 : 4.6%, Na 2 O: 9.5%, F: 7% and C: 6.5%.

[0043] The preparation method of the above-mentioned medium carbon steel chamfering copper plate continuous casting mold powder comprises the following steps:

[0044] (1) Ingredients: Prepare various raw materials according to the above chemical composition and their weight percentages, such as: wollastonite, limestone, quartz sand, albite, alumina stone, magnesia, lithium carbonate, soda ash, fluorite, carbon carbon black and graphite, binder carboxymethylcellulose sodium salt CMC;

[0045] (2) Melting: use an electric furnace to melt various raw materials except carbonaceous materials and adhesives;

[0046] (3) Water quenching: the molten slag directly enters the water pool to cool and solidify into a glass body;

[0047] (4) Drying:...

Embodiment 3

[0053] A medium carbon steel chamfering copper plate continuous casting mold powder, its chemical composition and weight percentage are: CaO: 41.5%, SiO 2 : 24%, MgO: 7%, Li 2 O: 2.5%, Al 2 o 3 : 3.8%, Na 2 O: 8%, F: 6.2% and C: 7%.

[0054] The preparation method of the above-mentioned medium carbon steel chamfering copper plate continuous casting mold powder comprises the following steps:

[0055] (1) Ingredients: Prepare various raw materials according to the above chemical composition and their weight percentages, such as: wollastonite, limestone, quartz sand, albite, alumina stone, magnesia, lithium carbonate, soda ash, fluorite, carbon carbon black and graphite, binder dextrin;

[0056] (2) Melting: use an electric furnace to melt various raw materials except carbonaceous materials and adhesives;

[0057] (3) Water quenching: the molten slag directly enters the water pool to cool and solidify into a glass body;

[0058] (4) Drying: Dry the vitreous body until the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melting pointaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to medium carbon steel chamfering copper plate continuous casting mold covering slag and a preparation method thereof. The casting slag comprises, by weight, 40-45% of CaO, 19-25% of SiO2, 3-7% of MgO, 1-2.5% of Li2O, 2-5% of Al2O3, 7-10% of Na2O, 5-7% of F and 4-8% of C. The covering slag is obtained through the steps of proportioning, melting, water quenching, drying, smashing, preparation and spray granulation, the medium carbon steel chamfering copper plate continuous casting mold covering slag is rational and adequate in proportioning of chemical components, good in heat-transfer capability, high in heat transfer uniformity and good in lubricating effect, and quality defects such as corner crack, narrow-edge bulging and transverse corner cracks of casting blanks of medium carbon steel are avoided effectively.

Description

technical field [0001] The invention belongs to the technical field of steelmaking, and in particular relates to a medium-carbon steel chamfering copper plate continuous casting mold mold slag and a preparation method thereof. Background technique [0002] At present, most domestic steel mills use right-angle continuous casting molds for continuous casting operations. The existing right-angle continuous casting molds are generally composed of four copper plates, and the corners are called right angles. To make the shrinkage of the corners greater than the amount of taper compensation of the copper plate of the crystallizer, resulting in the formation of a large air gap in the off-angle part, especially the wide-face off-corner area, and the air gap thermal resistance accounts for more than 80% of the entire thermal resistance, which further leads to The temperature at the off-corner area of ​​the slab is too high, forming a hot spot area, and a large transverse stress tensio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B22D11/111
CPCB22D11/111
Inventor 王正英彭会志张福梁冠东王旭阳庞炎
Owner XIXIA LONGCHENG METALLURGICAL MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com