Adhesive layer with separator, method for producing same, polarizing film with adhesive layer with separator, method for producing polarizing film with adhesive layer with separator, and image display device

A technology of adhesive layer and manufacturing method, which is applied in the field of polarizing film, and achieves the effect of excellent processability

Active Publication Date: 2016-04-20
NITTO DENKO CORP
View PDF10 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In addition, in recent years, image display devices for mobile use such as mobile phones tend to become thinner and lighter as a whole, especially in terms of design and portability.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Adhesive layer with separator, method for producing same, polarizing film with adhesive layer with separator, method for producing polarizing film with adhesive layer with separator, and image display device
  • Adhesive layer with separator, method for producing same, polarizing film with adhesive layer with separator, method for producing polarizing film with adhesive layer with separator, and image display device
  • Adhesive layer with separator, method for producing same, polarizing film with adhesive layer with separator, method for producing polarizing film with adhesive layer with separator, and image display device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0152] Hereinafter, the present invention will be described more specifically by way of examples, but the present invention is not limited to these examples. Parts and % in each example are based on weight.

[0153]

[0154] The weight-average molecular weight of the hydroxyl group-containing (meth)acrylic polymer (A) is measured by GPC (gel permeation chromatography). Analytical device: HLC-8120GPC manufactured by Tosoh Corporation; column: G7000HXL+GMHXL+GMHXL manufactured by Tosoh Corporation; column dimensions: 7.8mmφ×30cm each, 90cm in total; column temperature: 40°C; flow rate: 0.8ml / min; injection volume: 100μl; eluent: tetrahydrofuran; detector: differential refractometer (RI); standard sample: polystyrene

[0155]

[0156] In order to produce a thin polarizer, first, a laminate formed by forming a PVA layer with a thickness of 9 μm on an amorphous PET substrate is assisted in stretching in an air atmosphere at a stretching temperature of 130°C to form a stretche...

manufacture example 1

[0164]

[0165] Add 99 parts of butyl acrylate, 1 part of 4-hydroxybutyl acrylate (HBA), and 100 parts of monomer (solid content) to a reaction vessel with a cooling pipe, nitrogen gas introduction pipe, thermometer and stirring device together with ethyl acetate. Parts are 1 part of AIBN as an initiator, reacted at 60° C. for 7 hours under a nitrogen stream, and then added ethyl acetate to the reaction solution to obtain a hydroxyl-containing (meth)acrylic acid with a weight average molecular weight of 1.6 million. A solution of a polymeroid (A-1) (solid content concentration: 30% by weight). Table 2 shows the compounding and molecular weight of the (meth)acrylic polymer (A-1).

manufacture example 2

[0167]

[0168] ( A solution of a meth)acrylic polymer (A-2). Table 2 shows the compounding and molecular weight of the (meth)acrylic polymer (A-2).

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Adhesionaaaaaaaaaa
Login to View More

Abstract

Provided are: an adhesive layer with a separator, which has excellent workability and durability, and wherein a separator exhibits adequate easy separability from an adhesive layer; and a method for producing this adhesive layer with a separator. A method for producing an adhesive layer with a separator, which comprises: a first step for forming a layer of an adhesive composition, which contains a (meth)acrylic polymer, a peroxide and a phenolic antioxidant, on the releasing surface of a separator, said surface having been subjected to a release treatment; and a second step for forming an adhesive layer by heating the adhesive composition after the first step so that the adhesive composition is crosslinked.

Description

technical field [0001] The present invention relates to an adhesive layer with a separator, a method for producing the same, a polarizing film with an adhesive layer with a separator, and a method for producing the same. Furthermore, the present invention relates to image display devices such as liquid crystal display devices, organic EL display devices, and PDPs using the polarizing film with an adhesive layer with a separator. Background technique [0002] Image display devices and the like must arrange polarizing elements on both sides of the liquid crystal cell due to their image forming methods, and generally stick a polarizing film. When affixing the above-mentioned polarizing film to a liquid crystal cell, an adhesive is usually used. In addition, since the bonding of the polarizing film and the liquid crystal cell generally reduces light loss, the materials are closely bonded using an adhesive. In this case, since there is no need for a drying process when the pola...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09J7/00B32B27/30C09J11/06C09J133/00C09J133/06C09J133/14G02B5/30G02F1/1335C09J7/10C09J7/22C09J7/38
CPCB32B27/30C09J133/06G02B5/305C08K5/13C08K5/14B32B7/12B32B2307/42B32B2307/734B32B2457/202C09J2203/318C08K5/005C09J7/38C09J7/22G02B1/14C09J2433/00G02B5/3033C09J2301/408C09J7/10C08L33/06C09J2301/302C09J5/06G02F1/133528
Inventor 喜多川丈治木田友树秋月伸介保井淳外山雄佑石井孝证
Owner NITTO DENKO CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com