High-speed cutting resin grinding wheel and preparing method thereof

A resin grinding wheel, high-speed technology, applied in the field of grinding wheels, can solve the problems of affecting the performance of friction materials, high brittleness of pure phenolic resin, insufficient heat resistance, etc., and achieve the effect of reducing porosity, less volatile substances, and high grinding efficiency

Inactive Publication Date: 2016-03-09
WUHU HONGKUN AUTO PARTS
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, pure phenolic resin has defects such as high brittleness, poor toughness, high hardness, insufficient heat resistance, low strength, and high noise during use, which greatly affect the performance of friction materials. Therefore, modifying phenolic resin is to improve its comprehensive performance. effective method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] A kind of high-speed cutting resin emery wheel, it is made up of the raw material of following parts by weight:

[0024] CBN abrasive 410, white corundum powder 70, 35% formaldehyde solution 96, boric acid 5, hexamethylenetetramine 2, aniline 13, potassium oxide 2, phenol 90, sodium fluorosilicate 3.6, pentaerythritol 0.6.

[0025] A kind of preparation method of described high-speed cutting resin emery wheel, comprises the following steps:

[0026] (1) Add the above-mentioned white corundum powder into 10mol / l sodium hydroxide solution and soak for 1 hour, filter, wash with water, dry, mix with 10% of the weight of the above-mentioned sodium fluorosilicate, and calcinate at 300°C for 40 minutes, Cool naturally, mix with potassium oxide, and ball mill evenly to become white corundum abrasive;

[0027] (2) Add the remaining sodium fluorosilicate to 17 times deionized water and stir evenly;

[0028] (3) Mix 68% of the weight of the above phenol and 70% of the weight of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thermal decomposition temperatureaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-speed cutting resin grinding wheel. The high-speed cutting resin grinding wheel comprises, by weight, 410-500 parts of CBN abrasive, 70-100 parts of white corundum powder, 96-110 parts of 34-40% of formaldehyde solution, 5-7 parts of boric acid, 2-6 parts of hexamethylene tetramine, 13-20 parts of aniline, 2-3 parts of potassium oxide, 90-100 parts of phenol, 3.6-4 parts of sodium fluosilicate and 0.6-1 part of pentaerythritol. The high-speed cutting resin grinding wheel is particularly suitable for high-speed cutting, and the grinding efficiency is high.

Description

technical field [0001] The invention relates to the technical field of grinding wheels, in particular to a high-speed cutting resin grinding wheel and a preparation method thereof. Background technique [0002] With the continuous improvement of the speed of automobiles and airplanes, the requirements for friction materials such as transmission and braking are more stringent, and the matrix, as an important part of friction materials, has always been the focus of development and research. Phenolic resin, epoxy resin, styrene-butadiene rubber and polytetrafluoroethylene can be used as the matrix of friction materials, but epoxy resin, styrene-butadiene rubber and polytetrafluoroethylene have poor wear resistance, heat resistance and Adhesive properties limit its application in friction materials. The advantages of phenolic resin in heat resistance, bonding performance, mechanical properties, molding performance and cost make it the most commonly used binder matrix material f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B24D3/28B24D3/34B24D18/00C08G16/02C08G16/04C08K3/22C08K3/34
CPCB24D3/285B24D3/344B24D18/0009C08G16/02C08G16/04C08K3/22C08K3/34C08K2003/2227
Inventor 黄浩
Owner WUHU HONGKUN AUTO PARTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com