Special plastic gravure printing ink with high stability

A stable, plastic technology used in inks, applications, home appliances, etc. to achieve fast drying, excellent adhesion, and high hardness

Inactive Publication Date: 2016-03-02
王丽萍
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the domestic demand for gravure printing ink is increasing, and the requirements are getting higher and higher. The ink is required to hav

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A special ink for plastic gravure printing with high stability, which is made of the following raw materials in parts by weight:

[0011] 2.5 parts of MP resin solution, 0.15 parts of fumed silica, 3 parts of propylene glycol methyl ether, 2 parts of urea, 12 parts of epoxy resin, 8 parts of wetting and dispersing agent BYK-198 parts, 7 parts of methyl silicone oil, 5 parts of isopropanol, 6 parts of yellow ink, 4 parts of 1,4-butanediol diacrylate, 8 parts of hydroxyfluorosilicone resin, 5 parts of silver powder, 8 parts of vegetable oil, 1 part of silicon carbide, 5 parts of dimethyl phthalate, diphthalate 1 part of butyl ester, 1.5 parts of ethanolamine.

Embodiment 2

[0013] A special ink for plastic gravure printing with high stability, which is made of the following raw materials in parts by weight:

[0014] 4.6 parts of MP resin solution, 0.3 parts of fumed silica, 6 parts of propylene glycol methyl ether, 4 parts of urea, 16 parts of epoxy resin, 12 parts of wetting and dispersing agent BYK-1912, 13 parts of methyl silicone oil, 15 parts of isopropanol, 15 parts of yellow ink, 7 parts of 1,4-butanediol diacrylate, 14 parts of hydroxyfluorosilicone resin, 10 parts of silver powder, 14 parts of vegetable oil, 4 parts of silicon carbide, 7 parts of dimethyl phthalate, diphthalate 3 parts of butyl ester, 3.2 parts of ethanolamine.

Embodiment 3

[0016] A special ink for plastic gravure printing with high stability, which is made of the following raw materials in parts by weight:

[0017] 3.5 parts of MP resin solution, 0.22 parts of fumed silica, 4.5 parts of propylene glycol methyl ether, 3 parts of urea, 14 parts of epoxy resin, 10 parts of wetting and dispersing agent BYK-1910 parts, 10 parts of methyl silicone oil, 10 parts of isopropanol, 11 parts of yellow ink, 5.5 parts of 1,4-butanediol diacrylate, 11 parts of hydroxyfluorosilicone resin, 7.5 parts of silver powder, 11 parts of vegetable oil, 2.5 parts of silicon carbide, 6 parts of dimethyl phthalate, diphthalate 2 parts of butyl ester, 2.9 parts of ethanolamine.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A special plastic gravure printing ink with high stability is prepared from the following raw materials in parts by weight: 2.5-4.6 parts of MP resin liquid, 0.15-0.3 part of fumed silica, 3-6 parts of propylene glycol methyl ether, 2-4 parts of urea, 12-16 parts of epoxy resin, 8-12 parts of a wetting dispersant BYK-19, 7-13 parts of methyl silicone oil, 5-15 parts of isopropyl alcohol, 6-15 parts of a yellow printing ink, 4-7 parts of 1,4-butylene glycol diacrylate, 8-14 parts of hydroxyl fluorine silicon resin, 5-10 parts of silver powder, 8-14 parts of vegetable oil, 1-4 parts of silicon carbide, 5-7 parts of dimethyl phthalate, 1-3 parts of dibutyl phthalate and 1.5-3.2 parts of ethanolamine. The special plastic gravure printing ink has the benefits of high hardness, high high-temperature resistance, high water resistance, high drying speed, good stability and excellent adhesion.

Description

technical field [0001] The invention relates to a special ink for plastic gravure printing with high stability. Background technique [0002] Ink is an important material for printing packaging materials. It expresses patterns and characters on the substrate through printing. The ink includes main components and auxiliary components. They are evenly mixed and rolled repeatedly to form a viscous colloidal fluid. At present, the domestic demand for gravure printing inks is increasing, and the requirements are getting higher and higher. The inks are required to have the functions of high temperature resistance, wear resistance, and multiple functions, but the current inks on the market still need to be improved. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the problem to be solved by the present invention is to provide a special ink for plastic gravure printing with high stability, which has the effects of high hardness, high temperature res...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D11/102C09D11/107C09D11/06C09D11/03
CPCC09D11/102C09D11/03C09D11/06C09D11/107
Inventor 王丽萍
Owner 王丽萍
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap