A kind of mesoporous zirconium phosphate loaded nano-silver antibacterial polyester fiber and preparation method thereof

A nano-silver antibacterial and mesoporous zirconium phosphate technology, applied in the direction of single-component polyester rayon, can solve the problems of difficult continuous production, large addition amount, uneven distribution of antibacterial components, etc. Blank, low cost, no discoloration of performance

Active Publication Date: 2017-06-30
DONGHUA UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in this method, the addition amount is relatively large, and the distribution of antibacterial components is uneven, so it is difficult to realize continuous production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] A mesoporous zirconium phosphate-loaded nano-silver antibacterial polyester fiber, including a PET polyester matrix, Ag@mesoporous zirconium phosphate is dispersed in the polyester matrix, and the size of the Ag@mesoporous zirconium phosphate is 200~700nm. The mass ratio of the Ag@mesoporous zirconium phosphate to the polyester matrix is ​​3:97.

[0026] The preparation method of the above-mentioned mesoporous zirconium phosphate loaded nano-silver antibacterial polyester fiber, the specific steps are:

[0027] (1) Mesoporous zirconium phosphate is treated with oleum to obtain mesoporous zirconium phosphate with sulfonic acid groups on the surface. The specific steps for treating mesoporous zirconium phosphate with oleum are: oleum with a mass fraction of 98% and mesoporous zirconium phosphate The mass ratio of pore zirconium phosphate is 10:1, the reaction temperature is 40°C, and the reaction is 20 minutes.

[0028] (2) Take silver nitrate, ethylene glycol, and meso...

Embodiment 2

[0031] A mesoporous zirconium phosphate-loaded nano-silver antibacterial polyester fiber, including a PBT polyester matrix, Ag@mesoporous zirconium phosphate is dispersed in the polyester matrix, and the size of the Ag@mesoporous zirconium phosphate is 200~700nm. The mass ratio of the Ag@mesoporous zirconium phosphate to the polyester matrix is ​​3:97.

[0032] The preparation method of the above-mentioned mesoporous zirconium phosphate loaded nano-silver antibacterial polyester fiber, the specific steps are:

[0033] (1) Treat mesoporous zirconium phosphate with oleum to obtain mesoporous zirconium phosphate with sulfonic acid groups on the surface. The specific steps for treating mesoporous zirconium phosphate with oleum are: 50% oleum and mesoporous The mass ratio of pore zirconium phosphate is 10:1, the reaction temperature is 40°C, and the reaction is 80 minutes. .

[0034] (2) Take silver nitrate, ethylene glycol, and mesoporous zirconium phosphate with sulfonic acid ...

Embodiment 3

[0037] A mesoporous zirconium phosphate-loaded nano-silver antibacterial polyester fiber, including a PET polyester matrix, Ag@mesoporous zirconium phosphate is dispersed in the polyester matrix, and the size of the Ag@mesoporous zirconium phosphate is 200~700nm. The mass ratio of the Ag@mesoporous zirconium phosphate to the polyester matrix is ​​0.5:99.5.

[0038] The preparation method of the above-mentioned mesoporous zirconium phosphate loaded nano-silver antibacterial polyester fiber, the specific steps are:

[0039] (1) Mesoporous zirconium phosphate is treated with oleum to obtain mesoporous zirconium phosphate with sulfonic acid groups on the surface. The specific steps for treating mesoporous zirconium phosphate with oleum are: oleum with a mass fraction of 98% and mesoporous zirconium phosphate The mass ratio of pore zirconium phosphate is 10:1, the reaction temperature is 40°C, and the reaction is 20 minutes.

[0040] (2) Take silver sulfate, propylene glycol, and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
Login to view more

Abstract

Provided is a mesoporous zirconium-phosphate loaded nano-silver antibacterial polyester fiber and method for preparation thereof. The mesoporous zirconium-phosphate loaded nano-silver antibacterial polyester fiber comprises a polyester matrix; said polyester matrix has dispersed therein a Ag@ mesoporous zirconium phosphate. The method for preparing the mesoporous zirconium-phosphate loaded nano-silver antibacterial polyester fiber comprises: preparing a silver @ mesoporous zirconium phosphate sol precursor; the described silver @ mesoporous zirconium phosphate sol precursor, terephthalic acid (PTA), a diol, a stabilizing agent, and a catalyst are added in proportion to a polyester reactor; performing in situ polymerization and oxidation-reduction reaction to prepare a mesoporous zirconium phosphate-nano-silver antibacterial composite material, and drying and performing melt spinning to make a mesoporous zirconium-phosphate loaded nano-silver antibacterial polyester fiber.

Description

technical field [0001] The invention belongs to the field of preparation of antibacterial fibers, in particular to a mesoporous zirconium phosphate-loaded nano-silver antibacterial polyester fiber and a preparation method thereof. Background technique [0002] In today's society, the extreme environment, environmental pollution and other ecological environments have seriously deteriorated, and special living microenvironments such as confined spaces have led to an urgent need for functional protective textiles. At present, the fibers used to prepare textiles do not have antibacterial ability. Under certain conditions, they will provide an environment for bacteria to survive and reproduce, threatening human health. The main method to solve the antibacterial problem of fibers is to use antibacterial nanoparticles and polymer matrix for composite modification to prepare modified fibers with antibacterial effects. The fiber will gradually release antibacterial ingredients durin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/92D01F1/10
CPCC08G63/183D01F1/10D01F6/92
Inventor 朱美芳周家良俞森龙陈伟孙宾周哲
Owner DONGHUA UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap