Continuous carbon fiber sucker rod with wear-resistant protective layer and preparation method thereof

A technology of sucker rod and carbon fiber, which is applied in the direction of drill pipe, earthwork drilling, drilling equipment, etc., can solve the problems of partial wear of continuous sucker rod, and achieve the effect of ensuring continuity, high structural strength and prolonging the service life

Active Publication Date: 2016-02-03
SHANDONG UNIV
View PDF9 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the technical problems existing in the prior art, and to provide a continuous carbon fiber sucker rod with a wear-resistant protective layer and its preparation method, so as to solve the problem of continuous oil pumping with carbon fiber composite materials in current oil production equipment Rod eccentric wear problem

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Continuous carbon fiber sucker rod with wear-resistant protective layer and preparation method thereof
  • Continuous carbon fiber sucker rod with wear-resistant protective layer and preparation method thereof
  • Continuous carbon fiber sucker rod with wear-resistant protective layer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Preparation of wear-resistant layer prepreg tape: the reinforcing fiber used in the preparation of prepreg narrow tape is a hybrid fiber of basalt fiber and alumina fiber, the ratio of the two fibers is 2:1, and the reinforcing fiber fabric adopts "mesh cloth / unidirectional cloth / mesh The resin matrix used is polyurethane resin, and the polyurethane resin is made into a film in advance, and silicon carbide hard particles with a total content of 10% of the prepreg tape are pre-dispersed into the film, and the particle size is 0.5 microns. Lay the resin film of pre-mixed silicon carbide hard particles on the release paper, and apply the release paper with the resin film on the upper and lower surfaces of the laminated structure. The fiber fabric forms a prepreg tape, the final resin content of the prepreg tape is 40%, and the width of the prepreg tape is 90mm.

[0043] Such as figure 1 As shown, the preparation of a new type of continuous carbon fiber composite sucker ro...

Embodiment 2

[0045] Preparation of wear-resistant protective layer prepreg tape: the reinforcing fiber used in the preparation of prepreg narrow tape is a hybrid fiber of silicon carbide fiber and alumina fiber, the ratio of the two fibers is 4:1, and the "mesh cloth / plain weave / twill cloth / mesh cloth "Laminated structure, the resin matrix used is polyurethane resin, and the polyurethane resin is pre-made into a film, which is pre-dispersed into the film with silicon carbide hard particles with a total content of 15% of the prepreg tape, and the particle size is 0.4 microns. Lay the resin film with pre-mixed hard particles on the release paper, apply the release paper with the resin film on the upper and lower surfaces of the laminated structure, and combine the film and the fiber fabric by continuous hot-melt impregnation A prepreg tape is formed, the final resin content of the prepreg tape is 35%, and the width of the prepreg tape is 10 mm.

[0046] Preparation of new continuous carbon f...

Embodiment 3

[0048] Preparation of wear-resistant protective layer prepreg tape: the reinforcing fiber used in the preparation of prepreg narrow tape is a hybrid fiber of silicon carbide fiber and basalt fiber, the ratio of the two fibers is 1:3, and the "mesh cloth / plain cloth / satin cloth / mesh cloth Cloth” laminated structure, the resin matrix used is polyethylene resin, the polyethylene resin is made into a film in advance, and the film is pre-dispersed into the aluminum oxide hard particles with a total content of 15% of the prepreg tape, and the particle size is 0.2 microns . Lay the resin film with pre-mixed hard particles on the release paper, apply the release paper with the resin film on the upper and lower surfaces of the laminated structure, and combine the film and the fiber fabric by continuous hot-melt impregnation A prepreg tape was formed, the final resin content of the prepreg tape was 33%, and the width of the prepreg tape was 30 mm.

[0049] Preparation of new continuous...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Granularityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a continuous carbon fiber sucker rod with a wear-resistant protective layer and a preparation method thereof. The continuous carbon fiber sucker rod comprises a sucker rod body, a glass fiber layer coated on the surface of the sucker rod body, and a wear-resistant layer coated at the outer side of the glass fiber layer, wherein the wear-resistant layer comprises a fiber-reinforced fabric and a thermoplastic resin layer coated on the surface of the fiber-reinforced fabric, and hard wear-resistant particles are uniformly mixed in the thermoplastic resin layer, so that the hard wear-resistant particles are uniformly distributed on the surface of the wear-resistant layer. The hard wear-resistant particles are uniformly distributed on the surface of the sucker rod, and by virtue of the high hardness and high wear resistance of inorganic hard particles and the ball form formed with the mesh fabric structure, the eccentric wear resistance of the wear-resistant layer on the surface of the composite sucker rod is strengthened. Meanwhile, the part where the hard wear-resistant particles are in contact with the interface of the sucker rod body plays a role of interface mechanical meshing, thereby preventing the wear-resistant protective layer from slipping and layering from the surface of the sucker rod.

Description

technical field [0001] The invention belongs to the field of oil production equipment in the petroleum industry, and in particular relates to a continuous carbon fiber sucker rod with a wear-resistant protective layer and a preparation method thereof. The processed carbon fiber composite continuous sucker rod surface has high-hardness inorganic particles to improve the overall durability Abrasive, it can be applied to different working conditions of various oil wells, and has a long service life. Background technique [0002] With the development of the oil extraction industry and the increase in the scale of adoption, the depth of the oil well and the complexity of the downhole environment are increasing. Rods are gradually replaced by sucker rods made of composite materials. Composite materials belong to multi-phase composite materials. At present, the composite material sucker rods used in China mainly include glass fiber reinforced resin matrix composite material sucker...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): E21B17/00E21B17/10B29C70/34B29C70/52
Inventor 朱波曹伟伟王永伟乔琨赵圣尧
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com