A Low Refractive Index Optical Fiber Coating Resin

A resin-coated, low-refractive-index technology, which is applied in the field of low-refractive-index optical fiber coating resins, can solve the problems of high price, few specifications, and obstacles to the development of special optical fibers in China, so as to improve curing activity, prevent breakage, and avoid The effect of significantly increasing the refractive index of the resin

Active Publication Date: 2017-06-13
武汉长盈鑫科技有限公司
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are very few low-refractive index optical fiber coating resins available in the market, and the price is quite expensive. At the same time, due to military reasons, foreign countries restrict purchases from China, which seriously hinders the development of special optical fibers in China.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A Low Refractive Index Optical Fiber Coating Resin
  • A Low Refractive Index Optical Fiber Coating Resin
  • A Low Refractive Index Optical Fiber Coating Resin

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] A low refractive index optical fiber coating resin, the content of each component is: prepolymer A 50%, prepolymer B 20%, 1H, 1H, 2H, 2H-perfluorohexyl acrylate 17.5%, octafluoro-1,6-hexanediol diacrylate 8%, photoinitiator TPO 1%, fluorinated modified photoinitiator 29592%, photoinitiator 1841%, vinyltriethoxysilane 0.5 % for a total of 100%.

[0049] The preparation method of the above-mentioned optical fiber coating resin is: according to the above-mentioned ratio, weigh each raw material component, use a disperser to stir at a speed of 1000 rpm at about 40 ° C for 60 minutes, and after the photoinitiator is completely dissolved, use 1500 Filter through a mesh filter, place in a 40°C oven for degassing for 1 day, and then get the finished product.

[0050] The viscosity of the optical fiber coating resin prepared in this embodiment is 4323mpa.s (25°C), the elongation at break is 24%, the specific modulus (2.5% elongation) is 156MPa, the tensile strength is 12.2MPa, ...

Embodiment 2

[0052] A low refractive index optical fiber coating resin, the content of each component is: prepolymer A65%, 1H,1H,2H,2H-perfluorodecyl acrylate 28.7%, octafluoro- 1,6-hexanediol diacrylate 3%, photoinitiator 8190.3%, fluorinated modified photoinitiator 29592%, heptadecafluorodecyltriethoxysilane 1%, total 100%.

[0053] The preparation method of the above-mentioned optical fiber coating resin is: according to the above-mentioned ratio, weigh each raw material component, use a disperser to stir at a speed of 1000 rpm at about 40 ° C for 60 minutes, and after the photoinitiator is completely dissolved, use 1500 Filter through a mesh filter, place it in a 40°C oven for degassing for 1 day, and then get the finished product.

[0054] The optical fiber coating resin prepared in this example has a viscosity of 6234mpa.s (25°C), an elongation at break of 33.4%, a specific modulus (2.5% elongation) of 209.2MPa, and a tensile strength of 11.2MPa. Rate 1.353 (25°C).

Embodiment 3

[0056] A low refractive index optical fiber coating resin, the content of each component is: prepolymer A 35%, prepolymer B 35%, octafluoro-1,6-hexanediol diacrylate 25%, photoinitiator TPO 1%, 1843%, γ-methacryloxypropyltrimethoxysilane 1%, total 100%.

[0057] The preparation method of the above-mentioned optical fiber coating resin is: according to the above-mentioned ratio, weigh each raw material component, use a disperser to stir at a speed of 1000 rpm at about 40 ° C for 60 minutes, and after the photoinitiator is completely dissolved, use 1500 Filter through a mesh filter, place it in a 40°C oven for degassing for 1 day, and then get the finished product.

[0058] The viscosity of the fiber coating resin prepared in this example is 2387mpa.s (25°C), the elongation at break is 20.4%, the specific modulus (2.5% elongation) is 121MPa, the tensile strength is 13.3MPa, and the refractive index 1.394 (25°C).

[0059] The resin described in the present invention has moderat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to low-refractive optical fiber coating resin. The low-refractive optical fiber coating resin is prepared from, by weight, 30-65% of prepolymer A, 0-40% of prepolymer B, 2-8% of a photoinitiator, 20-40% of an active diluent and 0.5-2% of a silane coupling agent, and the sum of the weight percentages of all the components is 100%. The low-refractive optical fiber coating resin is high in adhesive power, optical fiber is not likely to be broken when bent, and the low-refractive optical fiber coating resin is low in refractive rate and can enlarge the digital transmission aperture of the optical fiber.

Description

technical field [0001] The invention belongs to the field of optical fiber and optical fiber coating, in particular to a low refractive index optical fiber coating resin. Background technique [0002] With the development of the characteristic optical fiber industry, there are more and more requirements for optical fiber coating resin, and the optical fiber coating resin has become one of the bottlenecks in the progress of characteristic optical fiber. Generally, the refractive index of the inner coating resin of ordinary optical fibers is 1.48-1.50. However, special optical fibers used in some military and medical fields (such as active optical fibers, large core diameter optical optical fiber, etc.) must use a low-refractive-index optical fiber coating resin with a lower refractive index. At present, some high-performance energy-transmitting optical fibers require that the refractive index of the optical fiber coating resin be less than 1.355. However, there are very few...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D175/16C09D7/12C08G18/67C08G18/50C08G18/12C08G18/10
Inventor 崔丽云余晓梦皮亚斌万欢黄星陶杜桂振东皮广
Owner 武汉长盈鑫科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com