SAPO-18 molecular sieve, method for synthesizing SAPO-18 molecular sieve and method for preparing olefin from methanol

A technology of SAPO-18, synthesis method, applied in molecular sieve and alkali exchange phosphate, molecular sieve characteristic silicoaluminophosphate and other directions, can solve problems such as unsatisfactory catalyst service life, increase production cost, reduce production efficiency, etc. The effect of thermal crystallization time, improving production efficiency, and prolonging the service life of one pass

Active Publication Date: 2016-01-27
CHNA ENERGY INVESTMENT CORP LTD +1
View PDF9 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when SAPO-34 molecular sieve is used in the reaction of methanol to light olefins, the single-pass service life of the catalyst is not ideal, and the regeneration cycle is short. On the one hand, the production efficiency is reduced, and on the other hand, the production cost is increased.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • SAPO-18 molecular sieve, method for synthesizing SAPO-18 molecular sieve and method for preparing olefin from methanol
  • SAPO-18 molecular sieve, method for synthesizing SAPO-18 molecular sieve and method for preparing olefin from methanol
  • SAPO-18 molecular sieve, method for synthesizing SAPO-18 molecular sieve and method for preparing olefin from methanol

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0024] According to the first aspect of the present invention, the present invention provides a kind of synthetic method of SAPO-18 molecular sieve, and this method comprises the following steps:

[0025] (1) provide a kind of mixed solution, described mixed solution contains aluminum source, phosphorus source, silicon source, templating agent and water;

[0026] (2) aging the mixed solution;

[0027] (3) hydrothermal crystallization of the aged mixed solution;

[0028] (4) The mixture obtained by hydrothermal crystallization is subjected to solid-liquid separation, and the obtained solid phase is dried and optionally calcined.

[0029] According to the method of the present invention, the template is a composite template, comprising a first template and a second template, the first template is N,N-diisopropylamine, and the second template is At least one of triethylamine, diethylamine and isopropylamine, and the molar ratio of the first templating agent to the second templa...

Embodiment 1

[0052] 13.15g pseudo-boehmite and 29.76g deionized water are mixed and stirred, and a mixed solution of 16.60g phosphoric acid (concentration is 85wt%) and 14.88g deionized water is added with vigorous stirring, and 7.20g silica sol (SiO 2 Content is the mixed solution of 40wt%) and 14.88g deionized water. After stirring at room temperature for 1 hour, 10.32 g of N,N-diisopropylethylamine (99 wt%) and 8.09 g of triethylamine were added, stirred for 2 hours, and the formed jelly was aged at room temperature (25° C.) for 2 hours. The aged mixed solution was put into a stainless steel crystallization kettle, and hydrothermally crystallized at 180° C. for 96 hours. The mixture obtained by hydrothermal crystallization was filtered, and the obtained solid phase was washed with deionized water, dried at 120° C. for 5 hours, and then calcined at 650° C. for 8 hours in an air atmosphere. The obtained molecular sieve is carried out X-ray diffraction analysis (results such as figure 1 ...

Embodiment 2

[0054] The molecular sieve was prepared by the same method as in Example 1, except that the amount of N,N-diisopropylethylamine (99 wt%) was 18.61 g, and the amount of triethylamine was 1.62 g. The obtained molecular sieve is carried out X-ray diffraction analysis (results such as figure 1 Shown), confirmed to be SAPO-18 molecular sieve. The molecular sieve yields and relative crystallinity are listed in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for synthesizing a SAPO-18 molecular sieve. According to the method, a composite template agent is adopted, and N,N-diisopropylethylamine is combined with at least one template agent of triethylamine, diethylamine and isopropylamine for use, so that the time of hydrothermal crystallization is shortened, and the yield of the molecular sieve is increased. The SAPO-18 molecular sieve has a regular appearance and a relatively high crystallinity. The invention further provides a method for preparing olefin from methanol. In the method, the SAPO-18 molecular sieve serving as a catalyst has a high selectivity of light olefins, and has a long single-pass service life.

Description

technical field [0001] The invention relates to a SAPO-18 molecular sieve and a synthesis method thereof, and also relates to a method for producing olefins from methanol. Background technique [0002] Low carbon olefins (C 2 -C 4 Olefins), especially ethylene and propylene are important basic organic chemical raw materials. With the development of the chemical industry, the demand for low-carbon olefins is increasing day by day. At present, the main production route of light olefins is still by catalytic cracking / cracking reaction of naphtha or light oil from petroleum. However, as the shortage of oil resources in the world is becoming more and more serious, researchers are paying more and more attention to the technology of producing low-carbon olefins from non-petroleum resources, and the methanol-to-olefins technology has emerged as the times require. [0003] The methanol-to-olefins technology uses coal or natural gas as a raw material to produce synthesis gas, from...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01B39/54C01B37/08
Inventor 郭磊朱伟平李飞薛云鹏孙先勇孙琦
Owner CHNA ENERGY INVESTMENT CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com