A filler, electronic cigarette technology, applied in fiber processing, textiles and papermaking, etc., can solve the problem that the surface modification of fibers without flocculent fillers enhances antibacterial properties and adsorption/desorption performance, adsorption/desorption performance needs to be improved, There are no problems such as antibacterial properties, and the effect of not easy to breed bacteria, simple and reliable preparation method, and good adsorption/desorption performance

Active Publication Date: 2016-01-20
CHINA TOBACCO GUANGXI IND
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These materials have good thermal properties and high reliability, but the fibers themselves are not antibacterial and the adsorption / desorption performance needs to be improved
At present, there is no effective method to modify the surface of floc filler fibers to enhance their antibacterial properties and adsorption / desorption properties.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method for improved electronic cigarette flocculent filler fiber
  • Preparation method for improved electronic cigarette flocculent filler fiber
  • Preparation method for improved electronic cigarette flocculent filler fiber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A method for making modified floc filler fibers for electronic cigarettes, comprising the following steps:

[0028] Step 1) Wash the flocs of the electronic cigarette three times with toluene and acetone respectively, and ultrasonically clean the flocs washed with the organic solvent with distilled water for 2 hours.

[0029] Step 2) Dissolving 4-(2-aminoethyl)-1,2-benzenediol in distilled water to a concentration of 1 mg / ml, and adjusting the pH of the solution to 7 with tris. Weigh 0.1 g of the washed electronic cigarette flocculent filler fiber and add it to 20ml of prepared 4-(2-aminoethyl)-1,2-benzenediol solution, react at room temperature for 24 hours, and dissolve the obtained flocculent The material was washed with distilled water and dried to obtain electronic cigarette floc filler fibers (such as figure 1 shown).

[0030] Step 3) Add the electronic cigarette floc filler fiber to 20ml of toluene diisocyanate in toluene solution, the concentration of the solu...

Embodiment 2

[0033] A method for making modified floc filler fibers for electronic cigarettes, comprising the following steps:

[0034] Step 1) The electronic cigarette flocs were washed three times with ethyl acetate and ethanol respectively, and the electronic cigarette floc filler fibers washed with an organic solvent were ultrasonically cleaned with distilled water for 2 hours.

[0035] Step 2) Dissolving 3,4 dihydroxyphenylalanine in distilled water, the concentration of the solution is 5 mg / ml, and then adjusting the pH of the solution to 8.5 with tris. Weigh 0.1 g of the washed e-cigarette flocculent filler fiber and add it to 20ml of the prepared 3,4 dihydroxyphenylalanine solution, react at room temperature for 24 hours, and wash the obtained e-cigarette flocculent filler fiber with distilled water ,drying.

[0036] Step 3) Add the electronic cigarette floc filler fiber to 20ml of bisphenol A epoxy resin in toluene solution, the solution concentration is 10mg / ml, and react at roo...

Embodiment 3

[0039] A method for making modified floc filler fibers for electronic cigarettes, comprising the following steps:

[0040] Step 1) Wash the flocs of the electronic cigarette three times with ethanol and acetone respectively, and ultrasonically clean the flocs washed with organic solvents with distilled water for 2 hours.

[0041] Step 2) 3 mg of 4-amino-1,2-catechol and 2 mg of 3,4-dihydroxyphenylalanine were dissolved in 1000 ml of distilled water, and the pH of the solution was adjusted to 9 with Tris . Weigh 0.1 g of the washed electronic cigarette floc filler fiber and add it to 20 ml of the prepared mixed solution of 4-amino-1,2-catechol and 4-dihydroxyphenylalanine, and react at room temperature for 24 hours. The resulting flocs were washed with distilled water and dried.

[0042] Step 3) Add the flocculent filler fiber of the electronic cigarette to the toluene solution of 4,4'-biphenyl ether dicarboxylic anhydride, the concentration of the solution is 10 mg / ml, and r...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
concentrationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method for improved electronic cigarette flocculent filler fiber, and particularly provides a method for preparing improved electronic cigarette flocculent filler fiber through antibacterial substances and mesoporous materials. Electronic cigarette flocculent substances which have the antibacterial property and high adsorption/desorption capacity are finally obtained mainly by arranging antibacterial agents with phenolic groups on the surfaces of fiber through oxidation polymerization, conducting connection through coupling agents and adding mesoporous materials to the flocculent substances. The preparation method is simple and reliable, prepared electronic cigarette flocculent filler has rough surfaces, a large number of mesoporous materials are adsorbed to the surfaces, the adsorption/desorption performance is enhanced, and the antibacterial performance is good.

Description

technical field [0001] The invention belongs to the technical field of electronic cigarette materials, and in particular relates to a method for modifying rough porous surface and antibacterial electronic cigarette flocs. Background technique [0002] E-cigarette is a product that atomizes the e-cigarette solution through an atomizer to deliver nicotine or other substances to the respiratory system. The flocculent filling of electronic cigarettes is the part of e-cigarettes that stores e-liquid, which has an important impact on the e-liquid content, reliability, and taste of an e-cigarette. It is required to have good adsorption / desorption performance for nicotine, solvents, flavors and fragrances in e-liquid, and it is not easy to breed bacteria during use, and it can withstand high temperature. [0003] At present, the main materials of floc fillers in electronic cigarettes include polyester fibers, polylactic acid fibers, cellulose, nylon, polypropylene fibers, polyureth...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M11/74D06M11/78D06M13/335D06M15/55D06M13/342D06M13/395D06M13/184
Inventor 张雨夏赵东元田兆福胡忠南陆漓温瑞恒黄忠辉霍冀臻唐晓林余英丰王萍娟
Owner CHINA TOBACCO GUANGXI IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap