Motor slot wedge high-performance epoxy resin insulating material preparation method

A technology of epoxy resin and insulating materials, applied in the field of insulating materials, can solve the problems of low shrinkage, poor heat resistance, impact resistance and water resistance, and achieve strong resistance and absorption, good electrical properties, and improved strength The effect of impact resistance

Active Publication Date: 2016-01-13
SUSONG HUANRAN ELECTROMECHANICAL
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Epoxy resin is one of the most widely used matrix resins in polymer-based composite materials. As a thermosetting resin, it has excellent adhesion, wear resistance, mechanical properties, electrical insulation, chemical stability and low shrinkage. The advantages of easy processing and molding are widely us...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] A kind of preparation method of high-performance epoxy resin insulating material for motor slot wedge proposed by the present invention comprises the following steps:

[0024] S1. Mix 3 parts of naphthenic acid, 2 parts of zinc oxide, 2 parts of phenylglycidyl ether and 0.1 part of pyromellitic anhydride in parts by weight, heat up to 135°C, react for 5 hours, place for 3 hours to separate layers, and take the upper layer The liquid is vacuum dehydrated, and then 1 part of 2,4,6-tris(dimethylaminomethyl)phenol is added and mixed evenly to obtain component A;

[0025] S2, mix 10 parts of nano-silicon nitride, 3 parts of nano-titanium dioxide, 8 parts of polypropylene short fiber, 2 parts of nano-mica, 12 parts of nano-aluminum hydroxide, and 3 parts of nano-zinc oxide by weight, and then add 10 parts of coupling Add 50 parts of bisphenol A epoxy resin, 50 parts of o-cresol novolac epoxy resin, 2 parts of chlorinated polyethylene, 20 parts of bisphenol A polycarbonate, 2 ...

Embodiment 2

[0029] A kind of preparation method of high-performance epoxy resin insulating material for motor slot wedge proposed by the present invention comprises the following steps:

[0030] S1. Mix 1 part of naphthenic acid, 5 parts of zinc oxide, 0.5 part of phenylglycidyl ether and 1 part of pyromellitic anhydride in parts by weight, heat up to 120°C, react for 8 hours, leave for 1.5 hours to separate layers, and take The upper liquid was vacuum dehydrated, and then 2.5 parts of 2,4,6-tris(dimethylaminomethyl)phenol was added and mixed uniformly to obtain component A;

[0031] S2. Mix 3 parts of nano-silicon nitride, 10 parts of nano-titanium dioxide, 2 parts of polypropylene short fiber, 12 parts of nano-mica, 3 parts of nano-aluminum hydroxide, and 5 parts of nano-zinc oxide by weight, and then add 2 parts of coupling Add 70 parts of bisphenol A epoxy resin, 30 parts of o-cresol novolac epoxy resin, 5 parts of chlorinated polyethylene, 5 parts of bisphenol A polycarbonate, 5 parts ...

Embodiment 3

[0035] A kind of preparation method of high-performance epoxy resin insulating material for motor slot wedge proposed by the present invention comprises the following steps:

[0036] S1. Mix 2.3 parts of naphthenic acid, 3.2 parts of zinc oxide, 1.6 parts of phenylglycidyl ether and 0.5 part of pyromellitic anhydride in parts by weight, heat up to 132°C, react for 6.5 hours, leave for 3 hours to separate layers, and take The upper liquid was vacuum dehydrated, then 1.8 parts of 2,4,6-tris(dimethylaminomethyl)phenol was added and mixed uniformly to obtain component A;

[0037] S2, mix 9 parts of nano-silicon nitride, 5 parts of nano-titanium dioxide, 5 parts of polypropylene short fiber, 6 parts of nano-mica, 9 parts of nano-aluminum hydroxide, and 3.5 parts of nano-zinc oxide by weight, and then add 6 parts of coupling agent, stirred for 17 minutes and then heated to 93°C, added 58 parts of bisphenol A epoxy resin, 44 parts of o-cresol novolac epoxy resin, 3.2 parts of chlorin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses a motor slot wedge high-performance epoxy resin insulating material preparation method, which comprises: uniformly mixing naphthenic acid, zinc oxide, phenyl glycidyl ether and pyromellitic dianhydride, carrying out a reaction at a temperature of 120-135 DEG C, adding 2,4,6-tris(dimethylaminomethyl)phenol to obtain a component A, mixing nanometer silicon nitride, nanometer titanium dioxide, polypropylene staple fibers, nanometer mica, nanometer aluminum hydroxide, nanometer zinc oxide, a coupling agent, a bisphenol A epoxy resin, a o-methyl phenolic epoxy resin, chlorinated polyethylene, a bisphenol A type polycarbonate, polytetrafluoroethylene, epoxy-terminated polydimethylsiloxane, phenyl glycidyl ether, ethylene glycol diglycidyl ether, polysulfide rubber, tricyclodecane dimethanol diacrylate and diphenylsilanediol to obtain a material A, uniformly mixing methyl tetrahydrophthalic anhydride, N-phenyl-2-naphthylamine, 1,4-phenylene diamine and the component A to obtain a material B, and curing the material A and the material B.

Description

technical field [0001] The invention relates to the technical field of insulating materials, in particular to a method for preparing a high-performance epoxy resin insulating material for motor slot wedges. Background technique [0002] Bamboo is a commonly used material for existing motor slot wedges. Because bamboo has the defects of poor heat resistance and flame retardancy, the motor slot wedges made of it have defects of not very ideal heat resistance and flame retardancy. In order to meet the needs of motor slot wedges for motors of various types and insulation levels, people have continuously developed various new insulating materials for making motor slot wedges. Polymers are indispensable and important materials in insulating materials. Epoxy resin is one of the most widely used matrix resins in polymer-based composite materials. As a thermosetting resin, it has excellent adhesion, wear resistance, mechanical properties, electrical insulation, chemical stability and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L63/00C08L63/04C08L23/28C08L69/00C08L27/18C08L83/06C08L81/04C08L23/12C08K13/02C08K3/34C08K3/36C08K3/22C08G59/62C08G59/58
Inventor 吴德海
Owner SUSONG HUANRAN ELECTROMECHANICAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap