Inorganic fiber heat-insulating paste material and preparation method thereof

A technology of inorganic fiber and paste, applied in the direction of coating, etc., can solve the problems of poor fireproof performance, achieve stable performance, low thermal conductivity, and convenient construction

Inactive Publication Date: 2015-12-30
SHANGHAI LEIEN ECONOMY ENERGY BUILD MATERIAL CO LTD
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Organic insulation materials include EPS board, XPS insulation board, polyurethane foam insulation board and phenolic board, etc., which have good thermal insulation performance and thermal insulation performance, but poor fireproof performance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inorganic fiber heat-insulating paste material and preparation method thereof
  • Inorganic fiber heat-insulating paste material and preparation method thereof
  • Inorganic fiber heat-insulating paste material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0115] Take 20 kg of vitrified microspheres, 5 kg of sepiolite fiber, 5 kg of fly ash above grade 2, 5 kg of colored sand, 0.2 g of polypropylene fiber, 8 kg of acrylic emulsion, 0.6 kg of film-forming aid, cellulose ether 0.5 kg, 0.1 kg of defoamer, 55.6 kg of water.

[0116] Vitrified beads are produced by Xinyang Shenhui Bentonite Co., Ltd. (the main chemical composition is SiO 2 、Al 2 o 3 , CaO), sepiolite is produced by Leibao Sepiolite Processing Co., Ltd., Wolong District, Nanyang City (a magnesium-rich silicate fiber mineral, whose physical and chemical formula is MgO[Si 12 o 30 ](OH) 4 12H 2 O), the fly ash above grade two is produced by Shanghai Xinghuo Company, the colored sand is the natural colored sand (mainly composed of silica) produced by Shanghai Aobo, and the polypropylene fiber is DL-1 produced by Shanghai Dalu Industrial Co., Ltd. fiber, which plays the role of anti-cracking, the acrylic emulsion is RS-992 emulsion produced by Shanghai Bardford, whic...

Embodiment 2

[0122] Take 25 kg of vitrified microspheres, 8 kg of sepiolite fiber, 8 kg of fly ash above grade 2, 3 kg of colored sand, 0.3 g of polypropylene fiber, 10 kg of acrylic emulsion, 0.8 kg of film-forming aid, cellulose ether 0.3 kg, 0.05 kg of defoamer, 42.55 kg of water.

[0123] Vitrified beads are produced by Xinyang Shenhui Bentonite Co., Ltd. (the main chemical composition is SiO 2 、Al 2 o 3 , CaO), sepiolite is produced by Leibao Sepiolite Processing Co., Ltd., Wolong District, Nanyang City (a magnesium-rich silicate fiber mineral, whose physical and chemical formula is MgO[Si 12 o 30 ](OH) 4 12H 2 O), the fly ash above grade two is produced by Shanghai Xinghuo Company, the colored sand is the natural colored sand (mainly composed of silica) produced by Shanghai Aobo, and the polypropylene fiber is DL-1 produced by Shanghai Dalu Industrial Co., Ltd. fiber, which plays the role of anti-cracking, the acrylic emulsion is RS-992 emulsion produced by Shanghai Bardford, w...

Embodiment 3

[0128] Take 30 kg of vitrified microspheres, 5 kg of sepiolite fiber, 3 kg of fly ash above grade 2, 3 kg of colored sand, 0.5 g of polypropylene fiber, 15 kg of acrylic emulsion, 1.0 kg of film-forming aid, cellulose ether 0.7 kg, 0.2 kg of defoamer, 44.4 kg of water.

[0129] Vitrified beads are produced by Xinyang Shenhui Bentonite Co., Ltd. (the main chemical composition is SiO 2 、Al 2 o 3 , CaO), sepiolite is produced by Leibao Sepiolite Processing Co., Ltd., Wolong District, Nanyang City (a magnesium-rich silicate fiber mineral, whose physical and chemical formula is MgO[Si 12 o 30 ](OH) 4 12H 2 O), the fly ash above grade two is produced by Shanghai Xinghuo Company, the colored sand is the natural colored sand (mainly composed of silica) produced by Shanghai Aobo, and the polypropylene fiber is DL-1 produced by Shanghai Dalu Industrial Co., Ltd. fiber, which plays the role of anti-cracking, the acrylic emulsion is RS-992 emulsion produced by Shanghai Bardford, whi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thermal conductivityaaaaaaaaaa
Compressive strengthaaaaaaaaaa
Tensile bond strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an inorganic fiber heat-insulating paste material and a preparation method thereof. The inorganic fiber heat-insulating paste material is characterized by consisting of the following components: coal ash of secondary level or above, colored sand, sepiolite fibers, polyropylene fibers, an acrylic emulsion, cellulose ether, a film-forming additive, vitrified micro bubbles and the balance of water, and the total percent of the components is 100. The inorganic fiber heat-insulating paste material has the advantages of being the same in service life as a building, superior in fire resistance (A1-grade combustion level), low in heat conductivity, stable in performance, light in dry unit weight, good in sound-proof effect, free from influencing indoor secondary Guangzhou decoration, convenient and quick in construction, particularly remarkable in performance on specially-shaped walls, free from cracks, elastic, incombustible, fire-proof, air-permeable, hydrophobic, single-component, air-hardening, and convenient for construction, and truly avoiding water adding for blending on 'industrial processing' sites. As the raw materials are coal ash and other energy-saving and environment-friendly materials, the inorganic fiber heat-insulating paste material conforms to the national industrial policy and has a very good development prospect. The inorganic fiber heat-insulating paste material is used for heat insulation of civil and industrial building walls, and the thicknesses of the insulating layers are determined by thermotechnical computation according to the current building energy-saving design standards or the building energy-saving requirements and manufacturing technology requirement of the city.

Description

technical field [0001] The invention relates to an inorganic fiber thermal insulation paste and a preparation method thereof. Background technique [0002] my country's thermal insulation materials are roughly divided into two categories, namely inorganic thermal insulation materials and organic thermal insulation materials. Inorganic thermal insulation materials include glass wool, rock wool board, inorganic thermal insulation mortar, foamed cement board, etc. These materials have better thermal insulation and fire prevention performance. Organic insulation materials include EPS board, XPS insulation board, polyurethane foam insulation board and phenolic board, etc., which have good thermal insulation performance and thermal insulation performance, but poor fireproof performance. In recent years, the product structure of my country's thermal insulation industry has undergone significant changes, among which lightweight materials, green environmental protection materials an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D133/00C09D7/12C04B26/04
Inventor 陈光辉陈伟达杜丽娜
Owner SHANGHAI LEIEN ECONOMY ENERGY BUILD MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com