Coated magnesium alloy, aluminum alloy or plastic substrate and manufacturing method thereof

A technology of substrate production and aluminum alloy, which is applied in metal material coating process, sputtering coating, vacuum evaporation coating, etc., can solve the problems of not mentioning the bonding performance, easy to be worn through, and affecting the wear resistance of the product , to achieve the effects of easy operation, improved binding force, high wear resistance and light transmittance

Active Publication Date: 2015-12-23
ZHEJIANG XINGXING TECH CO LTD
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although it has a certain hardness, strength, corrosion resistance and scratch resistance, and at the same time, silicon dioxide is also mentioned as a transition layer, but it is mainly together with the diamond film layer, so that it can play an anti-reflection film system and The function of the high-reflection film system does not mention its requirements in terms of bonding performance; in addition, due to the influence of the light transmittance of the diamond-like carbon (DLC) layer itself, when used as a light-transmitting product, its thickness can only reach 5nm~20nm can ensure the light transmittance, and it is also because the thickness is too small, it is still easy to be worn out during use, which affects the overall wear resistance of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coated magnesium alloy, aluminum alloy or plastic substrate and manufacturing method thereof
  • Coated magnesium alloy, aluminum alloy or plastic substrate and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] According to the required size, select the substrate 1 made of magnesium alloy, aluminum alloy or plastic for cleaning, and use weakly alkaline sodium bicarbonate aqueous solution for alkaline cleaning for 15 minutes to remove oil stains on the surface of the substrate. , then rinsed with clean water until neutral, then dried and set aside; the substrate 1 includes the front and back; then, a layer of SiO is coated on the front of the substrate 1 by a conventional method 2 Film layer 2; this film layer is used for bonding;

[0030] coated with SiO 2 The substrate 1 of the film layer 2 is put into the coating chamber of the vacuum coating machine, and then the coating chamber is evacuated to make the vacuum degree in the coating chamber reach 5.0x10 -5 Torr, then feed argon and oxygen, and control the flow of argon to 400 sccm, the flow of oxygen to 400 sccm, preferably, control the temperature to 150 ° C ~ 170 ° C, and open the carbon target emission source at the same...

Embodiment 2

[0032] According to the required size, select the substrate 1 made of polycarbonate for cleaning, and use a weakly alkaline sodium bicarbonate aqueous solution for alkaline cleaning for 15 minutes to remove oil stains on the surface of the substrate. After the alkaline cleaning, clean it with water Rinse to neutral, then dry, and set aside; substrate 1 includes front and back sides; then, a layer of SiO is coated on the front side of substrate 1 by vapor deposition method. 2 Film layer 2; this film layer is used for bonding;

[0033] coated with SiO 2 The substrate 1 of the film layer 2 is put into the coating chamber of the vacuum coating machine, and then the coating chamber is evacuated to make the vacuum degree in the coating chamber reach 4.5x10 -5 Torr, and then feed argon and oxygen, and control the flow of argon to 350 sccm, the flow of oxygen to 500 sccm, preferably, control the temperature to 150 ° C ~ 170 ° C, and open the carbon target emission source at the same ...

Embodiment 3

[0035] According to the required size, select the substrate 1 made of aluminum alloy for cleaning, and use a weakly alkaline sodium bicarbonate aqueous solution for alkaline cleaning for 15 minutes to remove oil stains on the surface of the substrate. After the alkaline cleaning, rinse with water To neutral, then, dry, standby; Substrate 1 includes front and back; Then, adopt one layer of SiO2 on the front of substrate 1 by vapor deposition method 2 Film layer 2; this film layer is used for bonding;

[0036] coated with SiO 2 The substrate 1 of the film layer 2 is put into the coating chamber of the vacuum coating machine, and then the coating chamber is evacuated to make the vacuum degree in the coating chamber reach 4.0x10 -5 Torr, then feed argon and oxygen, and control the flow of argon to 400sccm, the flow of oxygen to 450sccm, and open the carbon target emission source at the same time, the carbon target emission source is a graphite target emission source, and the powe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a coated magnesium alloy, aluminum alloy or plastic substrate and a manufacturing method thereof, belonging to the technical field of material surface treatment. The invention aims to enhance the binding property, rub resistance and light transmittance of the substrate surface. The method comprises the following steps: carrying out alkali washing on the substrate prepared from magnesium alloy, aluminum alloy or plastic according to the required size, and drying for later use; SiO2 film coating: coating the SiO2 film on the front surface of the cleaned substrate prepared from magnesium alloy, aluminum alloy or plastic; and DLC-COX (diamond-like carbon-cyclooxygenase) layer coating: coating the nano DLC-COX film on the surface of the SiO2 film. The coated magnesium alloy, aluminum alloy or plastic substrate has higher rub resistance and light transmittance; and the technical process is simple and easy to operate.

Description

technical field [0001] The invention relates to a plated magnesium alloy, aluminum alloy or plastic substrate and a manufacturing method thereof, belonging to the technical field of material surface treatment. Background technique [0002] Most of the coating technologies in existing electronic products are applied to display panels, such as mobile phones, computers or LCD panels, which mainly consider the needs of light transmittance and hardness of the post-coating products. Coating on the surface of products such as metal or plastic is rarely considered. However, along with people's requirements for the overall aesthetics and performance of products, the performance requirements for other components other than the display screen are also continuously improved. On the other hand, due to its high hardness, wear resistance or high surface finish, its products are widely used in machinery, electronics, microelectronics and optics. Such as Chinese patent application (publica...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23C14/06C23C14/22C23C14/24C23C14/08
Inventor 王先玉夏永光
Owner ZHEJIANG XINGXING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap