Method and device for preparing flake metal powder by dry ball milling

A flake metal and ball milling technology, applied in the field of electronic materials, can solve the problems of inability to enlarge production equipment, poor powder dispersion, low production efficiency, etc., and achieve good sealing and cooling effects, improved production efficiency, and no dust pollution.

Active Publication Date: 2018-07-24
SHENZHEN NONFEMET TECH
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the high speed, some cold welding will occur during the ball milling process, and the produced powder (such as flake zinc powder and flake aluminum powder) has poor dispersion and low uniformity, which cannot meet the requirements of high-grade flake zinc powder and flake aluminum powder. powder request
In addition, due to the limitation of sealing technology, the production equipment cannot be enlarged. The maximum volume of the ball mill is 100L, and only a dozen kilograms of metal powder can be ball-milled at a time. The output is low, resulting in low production efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method and device for preparing flake metal powder by dry ball milling
  • Method and device for preparing flake metal powder by dry ball milling

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] Put the mixed material containing 600 kg of zinc powder raw materials, 18 kg of ball milling aids and 2400 kg of 6mm, 3000 kg of 9.5mm, and 600 kg of 12mm steel balls into the 5M 3 In the new roller ball mill, through the atmosphere control system, the mixed atmosphere in which the proportion of nitrogen in the ball mill cylinder is controlled is 90% to 95%, and the ball is milled under airtight conditions, the ball milling speed is 34rpm, the ball milling time is 8 hours, and the ball milling temperature is 25°C. The zinc powder after ball milling enters the closed discharge system, the nitrogen pressure in the cylinder is 0.02MPa, the fan operation frequency is 40Hz, the ball mill speed is 32rpm, and the powder discharge time is 8min. After dispersing by dispersing equipment and grading by airflow, a flake zinc powder product with an average particle size of 13.24 μm, a bulk density of 1.04 g / mL and a sieving rate (-325 mesh) of 98% was obtained.

Embodiment 2

[0041] Put the mixture containing 500 kg of aluminum powder raw materials, 8 kg of ball milling aids and 2000 kg of 6mm, 2500 kg of 9mm, and 500 kg of 12mm steel balls into the 5M 3In the new roller ball mill, the atmosphere control system is used to control the mixed atmosphere with a nitrogen ratio of 95% to 98% in the cylinder, and the ball is milled under airtight conditions. The ball milling speed is 32rpm, the ball milling time is 10 hours, and the ball milling temperature is 20°C. The aluminum powder after ball milling enters the closed discharge system, the nitrogen pressure in the cylinder is 0.01MPa, the fan operation frequency is 40Hz, the ball mill speed is 30rpm, and the powder discharge time is 6min. After dispersing by dispersing equipment and grading by air flow, a flake aluminum powder product with an average particle size of 16.35 μm, a bulk density of 0.32 g / L, and a sieving rate (-325 mesh) of 99% was obtained.

Embodiment 3

[0043] Put the mixture containing 600 kg of atomized zinc powder, 9 kg of ball milling aids and 2500 kg of 6mm, 3000 kg of 9mm, and 500 kg of 12mm mixed steel balls into the 5M3 new roller ball mill, and control the nitrogen in the cylinder through the atmosphere control system A mixed atmosphere with a ratio of 97% to 98% is ball milled under airtight conditions with a ball milling speed of 30 rpm, a ball milling time of 8 hours, and a ball milling temperature of 20°C. The zinc powder after ball milling enters the closed discharge system, the nitrogen pressure in the cylinder is 0.02MPa, the fan operation frequency is 42Hz, the ball mill speed is 30rpm, and the powder discharge time is 10min. After dispersing by dispersing equipment and grading by air flow, a flake zinc powder product with an average particle size of 18.60 μm, a bulk density of 0.9 g / L, and a sieving rate (-325 mesh) of 96% was obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention provides a method for dry-type ball milling to prepare flake metal powder, comprising: uniformly mixing metal raw material powder and ball milling aids, and putting steel balls in proportion to ball milling in a new type of closed roller ball mill, and the ball milling process is circulated through cooling water The temperature of the ball mill is controlled by the system, and the ball mill atmosphere in the cylinder is adjusted by the ball mill atmosphere control system; the discharge adopts a closed discharge system, and a certain pressure of inert gas is introduced to start the exhaust fan and the ball mill, and the metal powder ground in the ball mill is blown and sucked. Blow and suck it out; put it into the dispersing equipment to disperse, and then classify it through the airflow grading equipment to get the finished product. And a device for realizing the above method. The method of the present invention has a high degree of automation in the whole process, no steel ball turnover, greatly reduces the labor intensity and workload of workers, and in addition has good sealing and cooling effects, no dust pollution, avoids the phenomenon of spontaneous combustion of powder oxidation in the process of powder discharge, and has a high yield Large, the production efficiency is greatly improved.

Description

technical field [0001] The invention belongs to the technical field of electronic materials, and in particular relates to a method and a device for preparing flake metal powder by dry ball milling. Background technique [0002] At present, there are two main methods for preparing scaly metal powders by ball milling: wet method and dry method. [0003] The patent application number is CN01103176.X discloses a production process of scaly metal powder, which is a wet process, which consists of grinding, sorting, filtering, drying, secondary drying and other processes. The raw material zinc powder is mixed with solvent, surface The coating agent is put into the ball mill for ball milling in proportion. After the ball milling, the slurry enters the storage tank for mixing. In the tank, the grinding medium is separated, and the filtered paste raw material is put into the bucket to stand still, and the solvent on the surface is sucked away. The obtained paste material is dried an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B22F9/04
Inventor 林兴铭李清湘邱刚陈云鹏师平乐刚周少强刘银向红印万良标程玉才
Owner SHENZHEN NONFEMET TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap