Composite alginate hydrogel dressing as well as preparation method and application thereof

A composite hydrogel and alginate technology, applied in medical science, bandages, absorbent pads, etc., can solve the problems of difficult preparation of dressing products, difficult control, violent reaction, etc., to achieve controllable gel strength and simple method , the effect of stable quality

Inactive Publication Date: 2015-12-23
吴玉松
View PDF3 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the complexation reaction between water-soluble inorganic metals (such as calcium chloride and zinc chloride) and alginic acid is violent, and the gelation reaction speed is usually very fast, which is difficult to control, and it is difficult to prepare dressing products with uniform structure and regular shape

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Weigh 1.5 grams of sodium alginate, disperse in 98.3 grams of distilled water, and stir at 60oC until completely dissolved. Cool to room temperature, add 0.2 g of calcium alginate, stir until dissolved evenly, and form an amorphous composite hydrogel.

Embodiment 2

[0015] Weigh 0.1 g of potassium alginate, disperse in 99.8 g of distilled water, and stir at 60°C until completely dissolved. Cool to room temperature, add 0.2 g of carboxymethyl chitosan calcium, and stir until it dissolves evenly, which is the amorphous composite hydrogel of the present invention.

Embodiment 3

[0017] Weigh 1.0 g of sodium alginate, disperse in 98.7 g of distilled water, and stir at 60°C until completely dissolved. Cool to room temperature, add 0.3 g of carboxymethyl cellulose calcium, stir until dissolved evenly, and form an amorphous composite hydrogel.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a composite hydrogel material containing alginate as well as a preparation method thereof. The method comprises the following steps: adding polyvalent metal modified carboxyl-containing water soluble polysaccharide and derivatives thereof as a gel cross-linking agent to an alginate (potassium salt, sodium salt or ammonium salt) water solution in advance, mixing and stirring, and directly casting a film so as to obtain gel or further drying so as to obtain a film. The method is simple in technology, and the obtained gel is good in intensity controllability and good in stability; and the gel has effects of promoting wound healing and accelerating wound tissue repairing.

Description

technical field [0001] The invention relates to a preparation method and application of a composite hydrogel dressing containing alginate, belonging to the field of biological materials. Background technique [0002] Modern medical theory has proved that providing a relatively moist and closed environment to the wound is conducive to wound healing. Based on this "moist therapy" theory, many liquid-absorbing swelling (ie gel-type) dressings have emerged as the times require. As an efficient bioadhesive and pH-sensitive gel material, alginate has been increasingly studied in its application. Alginate is a polysaccharide that provides the main structural component of brown algae. Alginate is formed by linking two monomers, mannuronic acid (M) and guluronic acid (G). The affinity of alginic acid to metal ions and its gel-forming performance are related to the content of G monomer. When two G monomers are linked, they form a pair of polyvalent metal ions (Ca 2+ , Zn 2+ 、Al 3...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A61L15/28A61L15/42A61L15/18A61L15/44A61L15/46
Inventor 吴玉松
Owner 吴玉松
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com