Active excitatory grinding aid for ferronickel slag and preparation method for active excitatory grinding aid

A technology of activity excitation and grinding aid, which is applied in the direction of climate sustainability, sustainable waste treatment, solid waste management, etc., can solve the problems of poor grindability and low activity of ferronickel slag, increase the output of the mill, and prepare The effect of simple process and low dosage

Active Publication Date: 2015-11-25
UNIV OF JINAN +1
View PDF4 Cites 14 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention is to provide an active stimulating grinding aid for ferronickel slag and a preparation method thereof. The active stimulating grinding aid can effectively solve the problems of poor grindability and low activity of ferronickel slag, and make ferronickel slag work as When used in cement mixture and concrete admixture, it has the function of plasticizing and strengthening
[0007] In order to solve the problems of poor grindability and low activity of ferronickel slag, the invention provides an activity-activated grinding aid for ferronickel slag and its preparation method:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Active excitatory grinding aid for ferronickel slag and preparation method for active excitatory grinding aid

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Add 1kg of calcined alumite, 5kg of water glass and 1kg of sodium rosinate into the stirring equipment, and stir for 5 minutes to obtain material A1; add 6kg of polymerized polyol, 15kg of coconut oil fatty acid diethanolamide, 10kg of ethyl acetate, and 1kg of sodium pyrophosphate 66kg of water was stirred for 10 minutes to obtain material A2; 2kg of material A1 was added to 98kg of material A2 and stirred for 5 minutes to obtain product 1 of the present invention.

Embodiment 2

[0018] Add 2kg of calcined alunite, 2kg of water glass and 3kg of sodium rosinate into the stirring equipment, and stir for 5 minutes to obtain material B1; add 15kg of polymerized polyol, 9kg of coconut oil fatty acid diethanolamide, 4kg of ethyl acetate, and 2kg of sodium pyrophosphate 65kg of water was stirred for 10 minutes to obtain material B2; 5kg of material B1 was added to 95kg of material B2, and stirred for 5 minutes to obtain product 2 of the present invention.

Embodiment 3

[0020] Add 4kg of calcined alunite, 1kg of water glass and 6kg of sodium rosinate into the stirring equipment, stir for 5 minutes to obtain material C1; add 20kg of polymerized polyol, 3kg of coconut oil fatty acid diethanolamide, 1kg of ethyl acetate, and 3kg of sodium pyrophosphate 65kg of water was stirred for 10 minutes to obtain material C2; 8kg of material C1 was added to 92kg of material C2, and stirred for 5 minutes to obtain product 3 of the present invention.

[0021] With the ferronickel slag that embodiment 1, embodiment 2, embodiment 3 make active stimulation type grinding aid, add 5kg mean particle diameter respectively in the ferronickel slag that is 1.70mm by 0.1%, in the standard of phi 500 * 500mm Grinding in the test mill for 60min. According to 70% of PI cement and 30% of nickel-iron slag powder, according to GB / T20491-2006 "Steel slag powder used in cement and concrete" to test the activity of nickel-iron slag, according to GB / T17671-1999 "Cement Mortar St...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an active excitatory grinding aid for ferronickel slag and a preparation method for the active excitatory grinding aid. The grinding aid is composed of polymeric glycol, cocoanut fatty acid diethanolamide, sodium pyrophosphate, ethyl acetate, an excitant and water, wherein the excitant is composed of calcined alunite, water glass and sodium abietate. The additive amount of the grinding aid in the ferronickel slag is 0.02-0.10% by mass of the ferronickel slag. The active excitatory grinding aid disclosed by the invention is sufficient in raw materials, simple to process and prepare, low in doping amount, stable in performance and high in cost performance. As the ferronickel slag which is ground is added, the problem that the ferronickel slag is poor in grindability can be solved. Under the condition that the grinding time is equal, the specific surface area of the ferronickel slag micropowder can be improved by 4.5-9%, the mill output is increased by over 15%, the energy consumption is remarkably reduced, and moreover, the active index of the ferronickel slag can be further improved by 10-35%.

Description

technical field [0001] The invention relates to the field of resource utilization of industrial waste slag, in particular to an active stimulating grinding aid for ferronickel slag and a preparation method thereof. Background technique [0002] In recent years, with the rapid development of my country's economic construction, a large amount of non-ferrous metallurgical waste residues have been produced in the process of industrial production. Ferronickel smelting waste slag from lateritic nickel ore (referred to as ferronickel slag) is a kind of granulated slag formed by refining nickel metal or the waste discharged during the smelting process of nickel-iron alloy, which is quenched in cold water. According to statistics, in 2013, my country's annual output of ferronickel reached 710,000 tons, accompanied by more than 45 million tons of ferronickel slag. By 2015, it is estimated that the total discharge of ferronickel slag will be close to 100 million tons, exceeding the to...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B18/14C04B5/06
CPCY02W30/91
Inventor 刘福田刘梁友宋南京赵洪义冯恩娟张丽君林奕
Owner UNIV OF JINAN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com