Glossy unsaturated polyester finish paint

An unsaturated and polyester technology, applied in the field of coatings, can solve the problems of brittle paint film and color change of paint film, and achieve the effect of good gloss and hardness, strong scratch resistance and good transparency

Inactive Publication Date: 2015-11-18
CHENGDU ZHANCHEN PAINT
View PDF6 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a bright unsaturated polyester topcoat, which solves the problems of the existing unsaturated polyester paint film being brittle and the color of the paint film changing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] Embodiment 1 summer uses light unsaturated polyester topcoat

[0038] A component:

[0039] raw material name

Raw material consumption

raw material name

Raw material consumption

[0040] Modified unsaturated polyester resin 1:

45%,

Divinylbenzene:

8%

Modified unsaturated polyester resin 2:

25%,

Styrene:

10%

Modified unsaturated polyester resin 3:

6%,

Polymerization inhibitor:

0.03%

Defoamer

0.3%

Toluene:

3%,

Leveling agent 1:

0.2%,

Ethyl esters:

2.37%

Leveling agent 2:

0.1%

[0041] B component:

[0042] raw material name

Raw material consumption

raw material name

Raw material consumption

Ethyl esters:

20%

Butyl esters:

15%,

Toluene:

30%,

Cyclohexanone:

3%

Xylene:

17%,

Styrene

15%

[0043] C component: colorless accelerator ...

Embodiment 2

[0047] Embodiment 2 Winter with light unsaturated polyester topcoat

[0048] A component:

[0049] raw material name

Raw material consumption

raw material name

Raw material consumption

Unsaturated polyester resin 1:

40%,

Divinylbenzene:

10%

Unsaturated polyester resin 2:

30%

Styrene:

7%

Unsaturated polyester resin 3:

8%,

Polymerization inhibitor:

0.01%

Defoamer

0.5%

Toluene:

2%,

Leveling agent 1:

0.2%,

Ethyl esters:

2.19%

Leveling agent 2:

0.1%

[0050] B component:

[0051] raw material name

Raw material consumption

raw material name

Raw material consumption

Ethyl esters:

30%

Butyl esters:

10%,

[0052] Toluene:

24%,

Cyclohexanone:

1%

Xylene:

15%

Styrene

20%

[0053] C component: colorless accelerator

[0054] D component: white w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Hard work timeaaaaaaaaaa
Surface dry timeaaaaaaaaaa
Hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses glossy unsaturated polyester finish paint. The glossy unsaturated polyester finish paint comprises components A, components B, a component C and a component D. The components A include 1:35-50% of modified unsaturated polyester resin, 2:25-40% of modified unsaturated polyester resin, 3:5-8% of unsaturated polyester resin, 0.3-0.5% of antifoaming agent, 0.3-0.7% of flatting agent, 6-12% of divinyl benzene, 5-12% of styrene, 0-0.05% of polymerization inhibitor, 2-4% of toluene and 2-4% of ethyl ester, and the proportions of the components A are 100% totally. The components B include 10-30% of styrene, 20-45% of ethyl ester, 10-30% of toluene, 15-25% of xylene, 10-20% of butyl ester and 1-5% of cyclohexanone, and the proportions of the components B are 100% totally. The component C includes a colorless accelerator. The component D includes whitewater. During construction, construction is conducted according to the weight proportion that the components A:the components B:the component C:the component D=100:15-25:0.5-2:1-3. The cracking resisting effect is good, edge breakage is avoided, the color of a paint film is light, the ground color can be highlighted on the light color bottom, definition is high, and the overall appearance quality of a product can be improved.

Description

technical field [0001] The invention belongs to the field of coatings, in particular to a bright unsaturated polyester topcoat. Background technique [0002] Under the current general environment, high-solid water-based coatings have become a trend. Unsaturated polyester coatings have gradually attracted people's attention due to their high solid content and excellent performance. Compared with conventional solvent-based polyurethane coatings, It has the advantages of high solid content in construction, good fullness, high hardness, strong resistance to collapse, and thick coating at one time. However, due to the high cross-linking density, the paint film of polyurethane coatings is relatively brittle, and it is easy to cause chipping when trimming and drilling furniture products. Moreover, the conventional oxidation-reduction system catalyzes the curing, and the final paint film color is purple to green, which affects the final appearance of wood products. Contents of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D167/06C09D7/12
Inventor 兰春风陈寿生
Owner CHENGDU ZHANCHEN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products