Dry-method winding formation method for carbon fiber composite transmission axle tube

A transmission shaft tube and composite material technology, applied to tubular objects, other household appliances, household appliances, etc., can solve problems such as poor working environment, fiber wear, resin waste, etc., and achieve excellent mechanical properties, high specific strength, and satisfy torsion The effect of intensity

Active Publication Date: 2015-11-18
HENGSHEN
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a carbon fiber composite material transmission shaft tube dry winding molding method to solve the problems of poor working environment, serious waste of resin, and fiber wear when wet molding products exist in the prior art.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Dry-method winding formation method for carbon fiber composite transmission axle tube
  • Dry-method winding formation method for carbon fiber composite transmission axle tube
  • Dry-method winding formation method for carbon fiber composite transmission axle tube

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] use as image 3 The shown pin mold 7 realizes winding at a small angle through the hooking of the pins on the prepreg yarn 6 . After the winding is completed, the carbon fiber composite transmission shaft tube is surface treated with a silicone film or a PET film. After the curing is completed, cut a length near the inner side of the pin, such as 100mm-200mm, to obtain the carbon fiber / epoxy prepreg yarn 6 transmission shaft tube.

Embodiment 2

[0040] use as Figure 4 The shown head mold 8 achieves small-angle winding through the head. After the winding is completed, the carbon fiber composite transmission shaft tube is surface treated with a silicone film or a PET film. After the curing is completed, the head part is cut, and then demolded to obtain the carbon fiber / epoxy prepreg yarn 6 transmission shaft tube.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
thicknessaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
Login to view more

Abstract

The invention provides a dry-method winding formation method for a carbon fiber composite transmission axle tube. Pollutants on a mould are cleaned up through acetone, and the mould is heated after the whole mould is evenly coated with release agents; prepreg of a proper width is wound on the mould according to a certain line form at a proper winding speed under proper winding tension, so that a composite layer is formed; heating is stopped, and after the mould is cooled to a certain temperature, a layer of silica film or polythylene terephthalate (PET) film is wound on the surface of the composite layer; after surface treatment is finished, temperature rises to 180 DEG C at the temperature rising speed not higher than 3 DEG C / min and is kept for a period of time, and finally the mould is cooled to the room temperature, released and cut, so that the transmission axle tube is obtained. The carbon fiber or epoxy composite transmission axle tube manufactured through dry-method winding formation method has high specific strength and specific stiffness and good humidity resistance, the thermogravimetric analysis (Tg) is 220 DEG C, and good compactness, uniformity and size accuracy are also realized.

Description

technical field [0001] The invention relates to a carbon fiber composite transmission shaft tube dry winding forming method. Background technique [0002] With the application of composite transmission shafts in vehicles, ships, aerospace and other fields more and more widely, its manufacturing methods are attracting more and more attention. At present, the common methods for making composite transmission shaft tubes include pultrusion, table-rolling, stretch winding, RTM molding and winding molding, among which winding molding is the most widely used. Regardless of its production cost, degree of automation, or the flexibility of its products, including changes in size and layup angles, winding molding is the best choice for making composite transmission shaft tubes. [0003] There are mainly two types of winding molding: wet molding and dry molding. When wet molding products, there are disadvantages such as poor working environment, serious waste of resin, and abrasion of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C53/56B29C53/84B29L23/00
Inventor 陈明新张星星谢昌江冯光亮蔡德军
Owner HENGSHEN
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap