Halogen-free flame-retardant TPVC ( polyvinyl chloride elastomer) material and preparation method therefor

A technology of PVC resin and flame retardant, which is applied in the field of polymer composite materials and its preparation, can solve the problems of harm to human body, increase of flammability of TPVC material, decrease of mechanical properties of TPVC material, etc., and achieve good environmental protection and synergistic flame retardant Good resistance, the effect of improving cold resistance

Active Publication Date: 2015-11-11
无锡市明涛电缆科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing problems of TPVC materials mainly include: (1) In the process of manufacturing TPVC materials, a large amount of plasticizers need to be added, and most of the plasticizers are flammable substances, resulting in an increase in the flammability of TPVC materials (2) The plasticizers used are mainly phthalates, which are harmful to the human body; (3) The mechanical properties of TPVC materials added with flame retardants are greatly reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1)

[0026] The halogen-free flame-retardant TPVC material of the present embodiment is made of the following components by weight:

[0027] 100kg of SG-3 type PVC resin.

[0028] As a plasticizer, 30kg of dioctyl terephthalate (DOTP), 4.5kg of epoxy fatty acid methyl ester, 22.5kg of diphenyl-isooctyl phosphate (DPOP) and 3kg of chlorinated paraffin.

[0029] 6kg of calcium-zinc composite stabilizer.

[0030] 1 kg calcium stearate, 1.1 kg stearic acid and 1 kg polyethylene wax as lubricants.

[0031] 50kg active magnesium hydroxide, 6kg microcapsule red phosphorus, 4kg antimony trioxide and 5kg zinc borate as a halogen-free flame retardant.

[0032] The preparation method of the above-mentioned halogen-free flame-retardant TPVC material has the following steps:

[0033] ① Weigh SG-3 PVC resin, dioctyl terephthalate, epoxy fatty acid methyl ester, diphenyl-isooctyl phosphate, chlorinated paraffin, calcium zinc composite stabilizer, calcium stearate according to the above weight ...

Embodiment 2~ Embodiment 6)

[0039] The preparation method of each example is the same as that of Example 1, except for the formulation of the halogen-free flame-retardant TPVC material, see Table 1 for details.

[0040] Table 1

[0041]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a halogen-free flame-retardant TPVC ( polyvinyl chloride elastomer) material and a preparation method therefor. The halogen-free flame-retardant TPVC material is prepared from the following components in parts by weight: 100 parts of PVC resin, 50-100 parts of a plasticizer, 5-10 parts of a heat stabilizer, 2-4 parts of a lubricant and 40-100 parts of a halogen-free flame retardant; the plasticizer consists of dioctyl terephthalate, epoxy fatty acid methyl ester, diphenyl isooctyl phosphate and chlorinated paraffin in a weight ratio of 100 to (10-20) to (100-50) to (5-15); and the halogen-free flame retardant consists of magnesium hydroxide, microencapsulated red phosphorus, antimonous oxide and zinc borate in a weight ratio of 100 to (10-20) to (5-15) to (5-15). The halogen-free flame-retardant TPVC material disclosed by the invention has relatively good flame resistance and mechanical properties, and belongs to a green environment-friendly material which is harmless on a human body and environment.

Description

technical field [0001] The invention relates to a polymer composite material and a preparation method thereof, in particular to a halogen-free flame-retardant TPVC material and a preparation method thereof. Background technique [0002] PVC is a commonly used general-purpose plastic. It has the advantages of wide source, low price, high strength and corrosion resistance. It is widely used in construction, chemical industry, medical equipment and other fields, especially in the manufacture of PVC elastomer (TPVC for short). And the field of application is becoming more and more extensive. The main reason is that TPVC is convenient to manufacture, easy to form and process, has good elasticity, good low temperature resistance, and aging resistance, and has a tendency to replace traditional rubber manufacturing and processing. [0003] The existing problems of TPVC materials mainly include: (1) In the process of manufacturing TPVC materials, a large amount of plasticizers need ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L27/06C08L91/06C08K13/06C08K5/12C08K5/523C08K3/22C08K3/02C08K3/38C08K5/098C08K5/09B29C47/92B29C48/92
CPCB29C48/92B29C2948/92704C08L27/06C08L2201/02C08L2201/22C08L2205/03C08L91/06C08L23/06C08K13/06C08K5/12C08K5/1515C08K5/523C08K2003/2224C08K2003/026C08K3/2279C08K2003/387C08K5/098C08K5/09
Inventor 周健
Owner 无锡市明涛电缆科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products