Double-color thin-wall plastic tableware and processing method thereof

A plastic tableware and processing method technology, applied in the field of tableware, can solve the problems of simple and rough materials and processing methods of disposable tableware, the quality and sanitation of tableware cannot be guaranteed, and the use is prone to dents, etc., so as to prevent scald accidents and reduce production costs. Low, not easy to spill effect

Active Publication Date: 2015-11-11
宁波市森佰工贸有限公司
View PDF13 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Tableware can be divided into metal tableware, porcelain tableware, wooden tableware, and plastic tableware according to its material. Among them, tableware made of plastic materials are mostly bowls, plates, plates, etc. used to hold food. However, the existing tableware for holding food has the following technical problems: 1. The tableware is mostly made of a layer of plastic material, which has low strength and is prone to dents during use, resulting in inconvenient use and even making food 2. In order to control the cost, the material and processing method of the existing disposable tableware are almost simple and rough, and the quality and sanitation of the tableware cannot be guaranteed. ; 3. Disposable tableware is easy to cause garbage pollution after use; 4. Since the same tableware uses the same material, the inner and outer surfaces of these tableware are usually the same color, and the same color leads to the color of the tableware. Too single, it is difficult to attract customers to buy, and reduce the appetite of users, and as a decoration or decoration, its decorative effect is also poor

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double-color thin-wall plastic tableware and processing method thereof
  • Double-color thin-wall plastic tableware and processing method thereof
  • Double-color thin-wall plastic tableware and processing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Weigh the following plastic raw materials: PP resin: 60 parts, nano-SiO 2 : 5 parts, Nano CaCO 3 : 4 parts, compound antibacterial and anti-mildew auxiliary agent: 1 part, processing aid: 5 parts, antioxidant: 0.8 parts, wherein, the composite anti-bacterial and anti-mildew auxiliary agent is nano-silver ion antibacterial agent, and the processing aid is 1 part of paraffin wax , 1 part of stearic acid, 1 part of fatty acid and its esters, 2 parts of PP-g-ST; the antioxidant is 2,6-di-tert-butylphenol.

[0042] Mix the above plastic raw materials evenly and add 1 part of toner, dry for 3 hours under the conditions of temperature at 105°C, air volume at 1750 cubic meters per hour, and wind pressure at 1250Pa, and then masticated and extruded at 160°C. Sheets of various colors.

[0043] The multi-layer sheets are stacked together for blister molding, and the colors of the sheets constituting the upper surface layer and the lower surface layer are different. Finally, afte...

Embodiment 2

[0045] Weigh the following plastic raw materials: PP resin: 70 parts, nano-SiO 2 : 6 parts, Nano CaCO 3 : 3 parts, composite antibacterial and anti-mildew auxiliary agent: 1.2 parts, processing aid: 4 parts, antioxidant: 0.6 part, wherein, described composite anti-bacterial and anti-mold auxiliary agent is vanillin compound, and processing aid is 2 parts 1 part of talcum powder, 1 part of fatty acid and its esters, 1 part of PP-g-MAH; the antioxidant is one or more phenolic antioxidants.

[0046] Mix the above plastic raw materials evenly and add 1 part of toner, dry for 4 hours under the conditions of temperature at 102°C, air volume at 1780 cubic meters per hour, and wind pressure at 1220Pa, then masticate and extrude at 170°C. Sheets of various colors.

[0047] The multi-layer sheets are stacked together for blister molding, and the colors of the sheets constituting the upper surface layer and the lower surface layer are different. Finally, after cooling, demoulding, shea...

Embodiment 3

[0049] Weigh the following plastic raw materials: PP resin: 50 parts, nano-SiO 2 : 8 parts, Nano CaCO 3 : 5 parts, composite antibacterial and mildew-proof auxiliary agent: 2 parts, processing aid: 3 parts, antioxidant: 1 part, wherein, described composite antibacterial and anti-mildew auxiliary agent is 1 part of nano-silver ion antibacterial agent, 1 part Ethyl vanillin compounds, processing aids are 1 part of silane coupling agent, 1 part of organosilicon compound, 1 part of PP-g-ST; antioxidants are 0.5 part of antioxidant 1010, 0.5 part of antioxidant 1076.

[0050] Mix the above plastic raw materials evenly and add 0.5 parts of toner, dry for 5 hours under the conditions of temperature 100°C, air volume 1800 cubic meters per hour, and wind pressure 1200Pa, and then plasticize and extrude at 150°C. Sheets of various colors.

[0051] The multi-layer sheets are stacked together for blister molding, and the colors of the sheets constituting the upper surface layer and the ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to double-color thin-wall plastic tableware and a processing method thereof, and belongs to the technical field of tableware. The tableware comprises a body. The body comprises a round bottom in the middle and a conical flange extending to the periphery of the round bottom. The body is formed by multiple layers of sheets in a laminated mode and comprises an upper surface layer and a lower surface layer, the sheets are tightly attached to one another, the thickness of the sheets ranges from 0.2 mm to 0.7 mm, the sheets forming the upper surface layer and the lower surface layer have different colors, and the sheets are made of plastic, including polypropylene plastic (PP) and polystyrene plastic. Because the tableware is formed by the multiple layers of sheets of different colors in a combined mode, the tableware has high strength without becoming sunk easily, and is convenient to use and more novel and bright-colored in appearance; because the tableware is made of the polypropylene plastic (PP) or the polystyrene plastic with reasonable compatibility, on one hand, the long-lasting antibacterial and antifungal property and other properties of the cup are effectively guaranteed, and on the other hand, environmental pollution caused by disposable tableware can be reduced; because the tableware is processed through a plastic sucking moulding process with special parameters, the final properties of the tableware are improved.

Description

technical field [0001] The invention belongs to the technical field of tableware, and relates to a two-color thin-walled plastic tableware and a processing method thereof. Background technique [0002] Tableware refers to utensils and utensils for holding, distributing or ingesting food. Among them, tableware for holding food includes bowls, plates, saucers, cups and other types. [0003] Tableware can be divided into metal tableware, porcelain tableware, wooden tableware, and plastic tableware according to its material. Among them, tableware made of plastic materials are mostly bowls, plates, plates, etc. used to hold food. However, the existing tableware for holding food has the following technical problems: 1. The tableware is mostly made of a layer of plastic material, which has low strength and is prone to dents during use, resulting in inconvenient use and even making food 2. In order to control the cost, the material and processing method of the existing disposable t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): A47G19/00A47G19/02C08L23/12C08K13/02C08K3/36C08K3/26C08L25/06C08L3/02C08L51/00C08K5/098B32B27/06B32B27/30B32B27/18
Inventor 沈筱波
Owner 宁波市森佰工贸有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com