Self-skinning compound material for heat-resistant polyurethane foaming tyre and preparation method thereof

A technology of polyurethane and heat resistance, which is applied in special tires, tire parts, transportation and packaging, etc., can solve problems that are rarely reported, and achieve the effect of improving heat resistance, excellent performance, and expanding the scope of use

Inactive Publication Date: 2015-10-28
SHANDONG INOV POLYURETHANE
View PDF3 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

CN103694448A provides a manufacturing formula for aging-resistant polyurethane elastomers, but there are few reports on the combination of heat resistance and polyurethane microcellular tires

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-skinning compound material for heat-resistant polyurethane foaming tyre and preparation method thereof
  • Self-skinning compound material for heat-resistant polyurethane foaming tyre and preparation method thereof
  • Self-skinning compound material for heat-resistant polyurethane foaming tyre and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] Component A: Weigh 80kg of polyether polyol (EP-330NG, product of Shandong Bluestar Dongda Chemical Co., Ltd.), 20kg of polymer polyol (POP93 / 28, product of Shandong Bluestar Dongda Chemical Co., Ltd.), 1 , 4-butanediol 13kg, ethylene glycol 4kg, diethylene glycol 4kg, cell opening agent (DK-12, product of Shandong Bluestar Dongda Chemical Co., Ltd.) 3kg, organosilicon foam stabilizer DC193 (American gas chemical products Co., Ltd.) 0.3kg, MOCA (Suzhou Xiangyuan Fine Chemical Co., Ltd.) 1kg, tertiary amines and organotin catalysts (A-33 and T-12) 0.5kg and 0.1kg respectively, blowing agent HCFC-141B 4kg, placed in a reaction kettle, mixed evenly, discharged, sealed and stored;

[0035] Component B: Weigh 100kg of polyester polyol (PE2420, product of Shandong Yinuowei Polyurethane Co., Ltd.), keep the temperature at 55°C, add 210kg of 4,4-diphenylmethane diisocyanate, heat up to 77°C and keep warm for reaction After 1.2 hours, 20 kg of carbonized diimide-modified MDI wa...

Embodiment 2

[0038] Component A: Weigh 60kg of polyether polyol (EP-3600, product of Shandong Bluestar Dongda Chemical Co., Ltd.), 40kg of polymer polyol (POP36 / 28, product of Shandong Bluestar Dongda Chemical Co., Ltd.) The sum of ether polyol and polymer polyol 100), 1,4-butanediol 13kg, ethylene glycol 6kg, MOCA (Suzhou Xiangyuan Fine Chemical Co., Ltd.) 3kg, cell opener (DK-12, Shandong Lanxingdong Da Chemical Co., Ltd.) 1kg, organosilicon foam stabilizer DC193 (American Gas Chemical Products Co., Ltd.) 1.5kg, tertiary amines and equilibrium catalysts (A-33 and C-225) were 0.9kg and 0.4kg, respectively. Foaming agent HCFC-141B 4kg, placed in the reaction kettle, mixed evenly, discharged, sealed for storage.

[0039] Component B: Weigh 100kg of polyester polyol (PE2420, product of Shandong Yinuowei Polyurethane Co., Ltd.), keep the temperature at 60°C, add 200kg of 4,4-diphenylmethane diisocyanate, heat up to 80°C and keep warm for reaction For 1 hour, add 40 kg of carbonized diimide-m...

Embodiment 3

[0042]Component A: Weigh 70kg of polyether polyol (EP-330NG, product of Shandong Bluestar Dongda Chemical Co., Ltd.), 30kg of polymer polyol (POP93 / 28, product of Shandong Bluestar Dongda Chemical Co., Ltd.), 1 , 4-butanediol 19kg, ethylene glycol 3kg, MOCA (Suzhou Xiangyuan Fine Chemical Co., Ltd.) 5kg, cell opening agent (DK-12, product of Shandong Bluestar Dongda Chemical Co., Ltd.) 5kg, silicone foam Agent AK-7703 (Shanghai Demei Shichuang Co., Ltd.) 0.8kg, tertiary amines and equilibrium catalysts (A-33 and C-225) were 0.9kg and 0.6kg respectively, blowing agent HCFC-141B 4kg, placed in the reaction In the kettle, after mixing evenly, discharge the material and keep it sealed.

[0043] Component B: Weigh 100kg of polyester polyol (PE2420, product of Shandong Yinuowei Polyurethane Co., Ltd.), keep the temperature at 50°C, add 170kg of 4,4-diphenylmethane diisocyanate, heat up to 75°C and keep warm for reaction After 1.5 hours, 50 kg of carbonized diimide-modified MDI was ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hydroxyl valueaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of polyurethane synthesis and concretely relates to a self-skinning compound material for a heat-resistant polyurethane foaming tyre and a preparation method thereof. The self-skinning compound material is prepared from a component A and a component B according to a mass ratio of 100: 80-90. The component A comprises polyether polyol, polymer polyol, a cross-linking agent and / or chain extender, a pore forming agent, a foam stabilizer, a catalyst and a foaming agent. The component B comprises polyester polyol and isocyanate. The self-skinning compound material can improve polyurethane heat resistance. The prepared tyre has excellent performances and can be used for a long time under conditions of loading and a high rate. The invention also provides a preparation method of the self-skinning compound material. The preparation method has reasonable processes.

Description

technical field [0001] The invention belongs to the field of polyurethane synthesis, and in particular relates to a self-skinning composite material for heat-resistant polyurethane foam tires and a preparation method thereof. Background technique [0002] Polyurethane microcellular elastomer has the advantages of high strength, good toughness, and light weight. Its excellent cushioning and shock absorption effect makes it gradually replace traditional rubber materials and is widely used in the preparation of vehicle soft parts, such as tires. [0003] Polyurethane microcellular elastomer foam tires have high bearing capacity and wear resistance. Different from traditional rubber tires, it has good cut and tear resistance, simple molding process, and low equipment investment; the tire does not need to be inflated, thus avoiding the concerns of air tire leakage and air leakage caused by sharp objects during use. , quite convenient to use. However, its internal molecular stru...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08G18/66C08G18/48C08G18/42C08G18/32C08G18/10C08J9/14B60C1/00
CPCC08G18/6607C08G18/10C08G18/4018C08G18/4072C08G18/632C08G18/6618C08G2380/00C08J9/144C08J2375/08C08G18/48C08G18/63C08G18/3206C08G18/3808
Inventor 李健孙清峰甘经虎王翠栾森
Owner SHANDONG INOV POLYURETHANE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com