Process for producing glass fiber-triploid Chinese white poplar wood composite material (five-layer)

A composite material and production process technology, which is applied in the direction of glass/slag layered products, layered products, wood layered products, etc., can solve the problems of decreased water absorption thickness expansion rate and decreased internal bonding strength, etc.

Inactive Publication Date: 2015-09-30
张双保 +6
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The test results show that: the static bending strength and elastic modulus of the particleboard (plywood) reinforced by alkali-free plain glass fiber cloth (thin felt) have increased, the water absorption thickness expansion rate has decreased, and the internal bonding strength has decreased.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for producing glass fiber-triploid Chinese white poplar wood composite material (five-layer)

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0023] attached figure 1 It is the structure diagram of the glass fiber reinforced triploid poplar wood composite material (five layers).

[0024] The present invention adopts the W-F-W-F-W structure form, F is glass fiber cloth, W is wood particle board, and technological process is as follows:

[0025] (1) Coat the surface of glass fiber with PF resin. Obtained from the glass fiber workshop of Beijing No. 251 Factory. The glass fibers used to make composite materials are usually alkali-free glass fibers, which contain a large amount of oxides of aluminum, boron, and silicon, so they are called aluminoborosilicate glass fibers; composite materials made of glass fibers, mechanics It has good performance and is mostly used in the defense industry, aircraft and other fields with special requirements, but the cost of the product is high. Considering the application range of wood processing products and the practicability and economy of the research, this study uses ordinary al...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of molding of wood composite materials and particularly relates to a process for producing a glass fiber reinforced triploid Chinese white poplar wood composite material (five-layer). According to the process, the composite material is prepared from triploid Chinese white poplars and a glass fiber reinforcing material, which serve as main raw materials, through adopting low-toxicity PF resin BN-1 of Beijing Forestry University as an adhesive, adopting a paraffin emulsion BZ-1 of Beijing Forestry University as a water repellent, adopting BZ-2 of Beijing Forestry University as a surface treating agent and adopting BZ-3 of Beijing Forestry University as a demolding agent. The optimal production process effect is achieved through controlling the glue spread of a substrate, hot pressing temperature, hot pressing time, unit pressure, target density and the amount of the added surface treating agent. Meanwhile, the properties of the prepared composite material can reach or exceed the standard requirements of European-Community oriented strand boards (PrEN300-94OSB / 4), so that the prepared composite material can serve as an engineering structure material.

Description

Technical field: [0001] The invention relates to the technical field of wood composite material mold manufacturing, in particular to a preparation process for the production of glass fiber reinforced triploid poplar tomentosa wood composite material (five layers). Background technique: [0002] Timber is one of the indispensable important materials in the national economy. Today, the supply and demand of timber is very tight. In order to alleviate this contradiction, my country has adopted a large number of measures to increase timber resources by building artificial forests. At present, the area of ​​artificial forests has ranked first in the world, but due to Its material is difficult to meet the requirements of various timber fields, resulting in the underutilization of plantation timber. Therefore, how to rationally utilize existing plantation timber to produce high value-added wood composite materials has become one of the most important frontier research topics in the cu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): B32B37/12B32B37/10B32B37/06B32B17/02B32B17/06B32B21/00
Inventor 张双保于雪斐王翠翠宋伟王丹丹侯国君于争争
Owner 张双保
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com