Foaming concrete panel and preparation method thereof

A foamed concrete and wallboard technology, applied in the field of concrete wallboard materials, can solve the problems of reducing the amount of cement, poor fly ash quality, poor sound insulation effect, etc., and achieve the effects of improving quality, long fire resistance time and good sound insulation effect

Active Publication Date: 2015-09-09
GUIZHOU ANKAIDA IND
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] However, when wastes such as fly ash and blast furnace slag are added, although it can reduce the amount of cement and reduce production costs, due to the large amount of harmful substances remaining in fly ash and blast furnace slag, the waste of fly ash The quality is poor and the radiation is large, which leads to the poor quality of the produced products, poor thermal insulation performance, poor sound insulation effect, and also brings pollution to the air. For this reason, the researchers combined fly ash and blast furnace water The colloidal substances contained in the slag, and the existence of these colloidal substances can increase the strength of the product, reduce the amount of cement, and even eliminate the use of cement, and then obtain a slurry similar to concrete, and then make the slurry into Wall products, and then can obtain higher strength, longer time refractory materials, and then provide a new way for the field of foamed concrete wall material production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032]A foamed concrete wallboard, its raw material components, by weight, are 20kg of fly ash, 10kg of blast furnace slag, 10kg of river sand, 2kg of foaming agent, 1kg of fiber, and 4kg of fly ash foaming agent. The silicon content in the fly ash is 27%. Described river sand is 80 orders. The foaming agent is a mixture of hydrogen peroxide, coconut oil fatty acid diethanolamide and water in a weight ratio of 40:1:90. The preparation method of described whipping agent is that hydrogen peroxide, coconut oil fatty acid diethanolamide are added according to proportioning in the stirrer that stirring speed is 800r / min and stir treatment 20min, then adjust stirring speed to be 300r / min stirring, and to Water was added therein, and after stirring for 0.5 h, the temperature was adjusted to 40° C. for 3 min. The preparation method of the fly ash foaming agent is that after the fly ash with a silicon element content of 21% is burned at a high temperature of 1000°C, high-viscosity at...

Embodiment 2

[0040] A foamed concrete wallboard, the raw material components, in parts by weight, are 40kg of fly ash, 30kg of blast furnace slag, 20kg of river sand, 3kg of foaming agent, 3kg of fiber, and 7kg of fly ash foaming agent. The silicon content in the fly ash is 30%. Described river sand is 120 orders. The foaming agent is hydrogen peroxide, coconut oil fatty acid diethanolamide and water in a weight ratio of 50:1:100. The preparation method of described whipping agent is to join hydrogen peroxide, coconut oil fatty acid diethanolamide according to proportioning in the stirrer that stirring speed is 1000r / min and stir for 30min, then adjust stirring speed to be 600r / min stirring, and to Water was added therein, and after stirring for 1 hour, the temperature was adjusted to 50° C. for 7 minutes. The preparation method of the fly ash foaming agent is that after the fly ash with a silicon element content of 23% is burned at a high temperature of 1200°C, high-viscosity attapulgit...

Embodiment 3

[0049] A foamed concrete wallboard, its raw material components, by weight, are 30kg of fly ash, 20kg of blast furnace slag, 15kg of river sand, 2.5kg of foaming agent, 2kg of fiber, and 5.5kg of fly ash foaming agent.

[0050] The silicon content in the fly ash is 29%.

[0051] Described river sand is 100 orders.

[0052] The foaming agent is hydrogen peroxide, coconut oil fatty acid diethanolamide and water in a weight ratio of 45:2:95.

[0053] The preparation method of described foaming agent is that hydrogen peroxide, coconut oil fatty acid diethanolamide are added according to proportioning in the stirrer that stirring speed is 900r / min and stir treatment 25min, then adjust stirring speed to be 450r / min stirring, and to Water was added therein, and after stirring for 0.7 h, the temperature was adjusted to 45° C. for 5 min.

[0054] The preparation method of the fly ash foaming agent is to add high-viscosity attapulgite clay accounting for 5% of the weight of the fly as...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of concrete panel material, and especially relates to a foaming concrete panel and a preparation method thereof. According to the combination and ratio of fly ash, blast furnace water slag, river sands, a foaming agent, fiber and a fly ash foaming agent, a depolymerization reaction and a polymerization reaction are carried out on the raw material substances, raw material performance can be performed, raw materials performance can be combined for controlling, raw materials performance is better, foaming processing of the raw materials can be enhanced, restriction of fly ash, a foaming agent and a fly ash foaming agent can ensure the mutual modification processing of the raw materials, crosslinking effect of the raw materials are enhanced, flexural compressive strength of the products can be enhanced, foaming concrete panel quality is increased; subsequent preparation technology and technological parameter are combined, so that raw material performance can be improved, and product quality is increased.

Description

technical field [0001] The invention relates to the technical field of concrete wallboard materials, in particular to a foamed concrete wallboard and a preparation method thereof. Background technique [0002] With the popularization of building energy saving and the continuous improvement of people's demand for the comfort of living environment, thermal insulation materials have been paid more and more attention by people. As one of the house insulation materials, the room temperature non-fired foamed brick is mainly made of cement, slag powder, river sand, etc. as raw materials. After mixing, it is foamed by pressure air, and the air is forced into the mixed slurry to form micro-bubbles. The structural concrete is molded and made through autoclave reaction and other processes. It is a new type of wall material that is environmentally friendly, energy-saving, and stable in material. Because of its thermal insulation, sound insulation, fire prevention, and strength superior...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/02
Inventor 赵永宽杨旭
Owner GUIZHOU ANKAIDA IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com