Medical quick-drying water-based antirust paint and preparation method thereof

A water-based technology for anti-rust coatings, applied in the direction of anti-corrosion coatings, shellac coatings, coatings, etc., can solve the problems of slow drying, salt spray resistance, etc., and achieve the effect of simple preparation method and simple and easy-to-obtain raw materials

Inactive Publication Date: 2015-09-02
SUZHOU BEC BIOLOGICAL TECH
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] The invention provides a medical quick-drying water-based anti-rust coating with fast drying and good salt resistance and a preparation method thereof, which solves technical problems such as slow drying and salt spray resistance of existing medical materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Step 1: Weigh 100 parts of acrylic emulsion, 30 parts of shellac copolymer emulsion, 0.5 part of zinc oxide, 15 parts of ethanol, 25 parts of phenol, 1 part of sodium metaborate, and 15 parts of light calcium carbonate according to the ratio of parts by mass. 8 parts of barium sulfate, 10 parts of iron oxide red, 5 parts of talcum powder.

[0021] Step 2: Put acrylic emulsion, shellac copolymer emulsion, zinc oxide, ethanol and sodium metaborate into the reaction kettle, heat to 55°C, and stir at 200r / min for 40min.

[0022] Step 3: Put the stirred liquid aside for 8 hours, add phenol, light calcium carbonate, barium sulfate, iron oxide red and talcum powder, mix well at 80°C, put it into a grinder for 4 hours, filter and pack.

[0023] Used for anti-rust and anti-corrosion of medical appliances, with deoxidation effect, the appearance of the coating film is iron red, the coating film is smooth, the viscosity is 60s, the hardness is 3; the adhesion is first-class, the w...

Embodiment 2

[0025] Step 1: Weigh 100 parts of acrylic emulsion, 50 parts of shellac copolymer emulsion, 2.5 parts of zinc oxide, 35 parts of ethanol, 45 parts of phenol, 5 parts of sodium metaborate, and 55 parts of light calcium carbonate according to the ratio of parts by mass. 12 parts of barium sulfate, 30 parts of iron oxide red, 25 parts of talcum powder.

[0026] Step 2: Put acrylic emulsion, shellac copolymer emulsion, zinc oxide, ethanol and sodium metaborate into the reaction kettle, heat to 75°C, and stir at 400r / min for 80min.

[0027] Step 3: Put the stirred liquid aside for 12 hours, add phenol, light calcium carbonate, barium sulfate, iron oxide red and talcum powder, mix well at 120°C, put it into a grinder for 6 hours, filter and pack.

[0028] Used for anti-rust and anti-corrosion of medical appliances, with deoxidation effect, the appearance of the coating film is iron red, the coating film is smooth, the viscosity is 65s, the hardness is 3.5; the adhesion is first-clas...

Embodiment 3

[0030] Step 1: Weigh 100 parts of acrylic emulsion, 45 parts of shellac copolymer emulsion, 2 parts of zinc oxide, 30 parts of ethanol, 40 parts of phenol, 4 parts of sodium metaborate, and 45 parts of light calcium carbonate according to the ratio of parts by mass. 11 parts of barium sulfate, 25 parts of iron oxide red, 20 parts of talcum powder.

[0031] Step 2: Put acrylic emulsion, shellac copolymer emulsion, zinc oxide, ethanol and sodium metaborate into the reaction kettle, heat to 55°C, and stir at 200r / min for 40min.

[0032] Step 3: Put the stirred liquid aside for 8 hours, add phenol, light calcium carbonate, barium sulfate, iron oxide red and talcum powder, mix well at 80°C, put it into a grinder for 4 hours, filter and pack.

[0033] It is used for anti-rust and anti-corrosion of medical appliances, has deoxidation effect, the appearance of the coating film is iron red, the coating film is smooth, the viscosity is 70s, and the hardness is 4; the adhesion is first-c...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a medical quick-drying water-based antirust paint and a preparation method thereof. The paint is prepared from an acrylic acid emulsion, a shellac copolymer emulsion, zinc oxide, ethanol, phenol, sodium metaborate, light calcium carbonate, barium sulfate, iron oxide red and talcum powder. When being used for resisting rust and corrosion for medical devices, the paint has the deoxidization effect. The coated film appears iron red and is smooth, the viscosity is 60-80s, and the hardness is 3-5. The adhesive force is first-grade; the paint has high water resistance, and does not have abnormity after being immersed in water; the impact strength is 500-700 N / cm; the paint has high salt tolerance, and can not discolor or blister after being immersed in a 3% sodium chloride water solution at 25 DEG C for 10-30 days; the surface drying time is 10-30 minutes; and the solid drying time is 2-6 hours. The paint has the advantages of simple preparation method and simple and accessible raw materials, and can be widely produced and continuously substituted for the existing materials.

Description

technical field [0001] The invention relates to the technical field of medical materials, in particular to a medical quick-drying water-based antirust coating and a preparation method thereof. Background technique [0002] Coatings that protect metal surfaces from chemical or electrochemical corrosion from the atmosphere, sea acrylic emulsions, etc. Coating anti-rust coatings on the metal surface can effectively prevent the direct invasion of various corrosive substances in the atmosphere, so as to maximize the extension of the service life of the metal. It can be divided into two categories: physical and chemical antirust paint. The former relies on the proper coordination of pigments and paints to form a dense paint film to prevent the intrusion of corrosive substances, such as iron red, aluminum powder, graphite antirust paint, etc.; the latter relies on the chemical antirust effect of antirust pigments, such as red Dan, zinc yellow antirust paint, etc. Used for rust ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D193/02C09D5/08C09D7/12
CPCC09D133/00C09D5/08C09D7/61C09D7/63C08L93/02C08K13/02C08K2003/2296C08K5/13C08K3/38C08K2003/265C08K2003/3045C08K3/34C08K2003/2272
Inventor 徐勤霞李苏杨
Owner SUZHOU BEC BIOLOGICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com