Production method of equisetum ramosissimum straw activated carbon
A technology of straw activated carbon and knotgrass, which is applied in the field of preparation of knotgrass straw activated carbon, can solve the problems that others have not yet filed patent applications for activated carbon, and achieve good industrial application prospects, large specific surface area and wide distribution
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] The specific steps of the preparation method of Knotty straw activated carbon are as follows:
[0023] (1) Collect the stalks of stalks, wash them with tap water to remove dust and impurities, and then put them in a drying box and dry them at 105°C for 3 h. After cooling, they are crushed with a straw pulverizer to a particle size of 80 meshes. Knot grass straw scraps;
[0024] (2) Put the above-mentioned Jiejiecao straw scraps into a carbonization furnace, and carbonize it at a carbonization temperature of 310 ℃ for 30 min, to obtain the Jiejiecao straw carbonization scraps;
[0025] (3) Mix the carbonized scraps of the above-mentioned grass straw and the KOH solution with a mass percentage concentration of 20% at a ratio of alkali to carbon of 3, soak for 24 hours, and then dry at 105 ℃ to constant weight, and then at a temperature of 325 ℃ Activated for 3 hours and cooled to room temperature naturally to obtain a semi-finished product of activated carbon from the straw sta...
Embodiment 2
[0028] The specific steps of the preparation method of Knotty straw activated carbon are as follows:
[0029] (1) Collect the stalks of stalks, wash them with tap water to remove dust and impurities, then put them in a drying box and dry them at 105 ℃ for 3 hours, and then pulverize them with a straw pulverizer to a particle size of 100 meshes after cooling. Knot grass straw scraps;
[0030] (2) Put the above-mentioned stubble straw scraps into a carbonization furnace, and carbonize in a carbonization furnace at a temperature of 300 ℃ for 30 min to obtain stubble straw charring scraps;
[0031] (3) Mix the carbonized scraps of the above-mentioned grass stalks with the KOH solution with a mass percentage concentration of 25% at an alkali-to-carbon ratio of 2. After immersing for 24 h, dry at 105 ℃ to constant weight, and then at a temperature of 350 ℃ Activated for 2.5 hours and cooled to room temperature naturally to obtain a semi-finished product of activated carbon from the straw ...
PUM
Property | Measurement | Unit |
---|---|---|
iodine adsorption value | aaaaa | aaaaa |
iodine adsorption value | aaaaa | aaaaa |
iodine adsorption value | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
![application no application](https://static-eureka-patsnap-com.libproxy1.nus.edu.sg/ssr/23.2.0/_nuxt/application.06fe782c.png)
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com