Acid copper direct-electroplating solution for iron part
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A solution and acid copper technology, applied in the field of direct electroplating copper solution for iron parts, can solve the problems of health and cumbersome processes, and achieve the effect of good protection and good bonding force
Active Publication Date: 2015-07-22
崇辉半导体(深圳)有限公司
View PDF5 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0012] The purpose of the present invention is to overcome the health and cumbersome problems caused by the pretreatment of harmful substances cyanide in the prior art for electroplating iron parts, and to provide a method that does not contain harmful substances to the human body and the environment and can be obtained on the iron-based surface. Iron parts with good bonding force, bright and dense copper plating layer are directly electroplated with acid copper solution
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0035] The weight volume concentration of the basic solution components is:
[0036] Copper sulfate 100g / L
[0037] Sulfuric acid 40g / L
[0038] Hydrochloric acid 100mg / L
[0039] Complexing agent weight volume concentration is:
[0040] Ethylenediaminetetramethylenephosphonic acid 15g / L
[0041] The weight volume concentration of corrosion inhibitor is:
[0042] Thiourea 10mg / L
[0043] The weight volume concentration of reducing agent is:
[0044] Glyoxylic acid 20g / L
Embodiment 2
[0046] The weight volume concentration of the basic solution components is:
[0047] Copper sulfate 120g / L
[0048] Sulfuric acid 50g / L
[0049] Hydrochloric acid 120mg / L
[0050] Complexing agent weight volume concentration is:
[0051] Hydroxyethylidene diphosphonic acid 80g / L
[0052] Ethylenediamine tetramethylene phosphonic acid 12g / L
[0053] The weight volume concentration of corrosion inhibitor is:
[0054] Thiourea 10mg / L
[0055] The weight volume concentration of reducing agent is:
[0056] Formaldehyde 5g / L
Embodiment 3
[0058] The weight volume concentration of the basic solution components is:
[0059] Copper sulfate 150g / L
[0060] Sulfuric acid 60g / L
[0061] Hydrochloric acid 130mg / L
[0062] Complexing agent weight volume concentration is:
[0063] Tartaric acid 20g / L Citric acid 10g / L Hydroxyethylidene diphosphonic acid 80g / L
[0064] The weight volume concentration of corrosion inhibitor is:
[0065] Thiourea 30mg / L
[0066] Allylthiourea 6mg / L;
[0067] The weight volume concentration of reducing agent is:
[0068] Formaldehyde 10g / L
[0069] Glyoxylic acid 20g / L
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The invention discloses an acid copper direct-electroplating solution for an iron part. The acid copper direct-electroplating solution contains a basic solution capable of providing cupric ions, a complexing agent, a corrosion inhibitor and a reducing agent, wherein the complexing agent is one or more of tartaric acid, citric acid, etidronic acid and ethylenediaminetetramethylene phosphoric acid; the corrosion inhibitor is thiourea and / or allylthiourea; the reducing agent is formaldehyde and / or glyoxylic acid. The acid copper direct-electroplating solution for the iron part is free of a harmful substance cyanide for copper pre-plating, a copper pre-plating procedure is eliminated, and the iron part can directly be electroplated with copper to form a copper-plated layer which is strong in bonding strength, bright and compact on the surface of the iron part; moreover, compared with an iron substrate easily corroded by high-concentration sulfuric acid in a bright acid copper plating solution, the corrosion inhibitor of the acid copper direct-electroplating solution has the advantages that the iron part can be well protected, the iron part is prevented from being greatly corroded, and the influence on the dimensional accuracy of the iron part is eliminated.
Description
technical field [0001] The invention belongs to the field of electroplating, and in particular relates to a direct copper electroplating solution for iron parts. Background technique [0002] Generally, in copper sulfate (CuSO 4 ·5H 2 O) 160~220g / L, sulfuric acid (H 2 SO 4 98%) 60~80g / L, hydrochloric acid (HCl 36%) 30~120mg / L solution can obtain bright and good leveling copper plating, also known as bright acid copper plating. [0003] Since the bright acidic copper plating solution contains sulfuric acid (H 2 SO 4 98%) is higher, and the higher acidity is more corrosive to the iron substrate; under acidic conditions, copper ions are easily replaced, and a replacement copper layer is formed on the surface of the iron substrate, and the binding force between the replacement copper layer and the iron substrate is extremely poor, so Acceptable copper deposits cannot be obtained in bright acidic copper solutions without preplating. [0004] Iron parts must be pre-plated...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.