Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A production system of passivated pure calcium cored wire

A pure calcium cored wire and production system technology, applied in the field of refining outside the steelmaking furnace, can solve the problems of reduced work efficiency, reduced production continuity, reduced core wire content, etc., to reduce calcium loss and safety accidents, slow down boiling and splash phenomenon, the effect of improving the yield

Active Publication Date: 2016-06-22
MAANSHAN XINGDA METALLURGICAL NEW MATERIAL
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to solve the problem that in the production and processing process of the existing passivated pure calcium cored wire, the calcium wire is passivated by manual smearing or by manually adding passivation solution into the passivation processor, which increases the labor cost of workers. Labor intensity reduces the continuity of production and greatly reduces work efficiency; and during the passivation process, due to the ratio of the passivation solution or the contact between the passivation solution and the air, the calcium wire is oxidized during the passivation process The phenomenon is still serious, so that the Ca content in the core wire is still reduced, reducing the passivation effect of the calcium wire, affecting the use effect and calcium yield of calcium treatment in steel plants, and increasing the production cost of calcium treatment in steel plants, etc. , providing a production system and production method of passivated pure calcium cored wire

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A production system of passivated pure calcium cored wire
  • A production system of passivated pure calcium cored wire
  • A production system of passivated pure calcium cored wire

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] Such as figure 2 As shown, a production system of passivated pure calcium cored wire in this embodiment includes a heater 1, an extruder 2, a cored wire unit 8, a passivation processor 3 and an automatic filling mechanism. Wherein, the heater 1 is located at the feed end of the extruder 2, the inlet end of the passivation processor 3 is located at the discharge end of the extruder 2, and the outlet end of the passivation processor 3 is provided with a cored wire unit 8. The pure calcium cored wire to be processed passes through the heater 1, extruder 2, passivation processor 3 and cored wire unit 8 in sequence, wherein the above extruder 2 is used to extrude calcium rods into calcium The passivation processor 3 is used to passivate the calcium filament. A liquid inlet is provided on the upper part of the passivation processor 3, and the inlet end and the outlet end of the passivation processor 3 are sealed soft joints, and the passivation processor 3 is used to hold p...

Embodiment 2

[0058] A kind of production method of passivated pure calcium cored wire of the present embodiment, its steps are:

[0059] Step 1, preparation of passivation solution

[0060]Weigh the methyl silicone oil and talcum powder according to the weight percentage of 90% and 10% respectively, place the weighed methyl silicone oil and talcum powder in a high-speed stirring tank and stir for 30 minutes to obtain the required passivation solution, And it is packed into passivation processor 3 and passivation liquid storage tank, the alkalinity PH of gained passivation liquid is 6.5;

[0061] Step 2. Heating and extrusion of calcium rods into filaments

[0062] Start the production system of passivated pure calcium cored wire, heat the pure calcium rod to be processed with heater 1, and place it in extruder 2 for extrusion after the calcium rod is heated to the plastic extrusion molding temperature , so that it is extruded into a metal calcium wire of Ф7mm, and the mass fraction of Ca...

Embodiment 3

[0069] A kind of production method of passivated pure calcium cored wire of the present embodiment, its steps are:

[0070] Step 1, preparation of passivation solution

[0071] Weigh the methyl silicone oil and talcum powder according to the weight percentage of 95% and 5% respectively, place the weighed methyl silicone oil and talcum powder in a high-speed stirring tank and stir for 25 minutes to obtain the required passivation solution, And it is packed into passivation processor 3 and passivation liquid storage tank, the alkalinity PH of gained passivation liquid is 6;

[0072] Step 2. Heating and extrusion of calcium rods into filaments

[0073] Start the production system of passivated pure calcium cored wire, heat the pure calcium rod to be processed with heater 1, and place it in extruder 2 for extrusion after the calcium rod is heated to the plastic extrusion molding temperature , so that it is extruded into a metal calcium wire of Ф8mm, and the mass fraction of Ca i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a production system and production method of a passivated pure calcium core-spun yarn, belonging to the technical field of steelmaking furnace external refining. The production system comprises a heater, an extruding machine, a core-spun yarn unit, a passivating treatment device and an automatic charging mechanism, wherein the automatic charging mechanism comprises a pressure sensor, a solenoid valve, a passivated liquid pump and a control unit; a liquid outlet of the passivated liquid pump is connected with a liquid inlet on the upper part of the passivating treatment device through a liquid delivery pipeline; the liquid delivery pipeline is provided with a solenoid valve; the pressure sensor is installed at the liquid inlet on the upper part of the passivating treatment device; a signal output end of the pressure sensor is connected with an input end of the control unit; a switch of the passivated liquid pump is connected with an output end of the control unit; and the liquid inlet of the passivated liquid pump is connected with a passivated liquid storage tank through a pipeline. By using the passivated pure calcium core-spun yarn, the oxidation loss of calcium lines is reduced, so that the calcium yield in the molten steel is greatly enhanced.

Description

technical field [0001] The invention belongs to the technical field of refining outside a steelmaking furnace, and more specifically relates to a production system and a production method of a passivated pure calcium cored wire. Background technique [0002] The high efficiency of modern steelmaking production and the rapid development of post-furnace refining technology, especially the wide application of post-furnace molten steel refining and feeding line technology, have made it possible to produce high-purity clean steel. Calcium treatment wire feeding technology is a high-efficiency technical means for the final refining treatment of high-quality steel with strict requirements on the shape and quantity of inclusions. It mainly feeds calcium cored wire to molten steel with the cooperation of argon blowing. Calcium treatment wire feeding technology not only has ideal effects in deoxidation, desulfurization of molten steel, change of inclusion form, etc., but also in fine-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21C7/00C21C7/06C21C7/064
Inventor 李国安王建国李寿全
Owner MAANSHAN XINGDA METALLURGICAL NEW MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com