Method for manufacturing high-niobium titanium-aluminum alloy material by adopting two-step pressure infiltration

A titanium-aluminum alloy and infiltration technology is applied in the field of intermetallic compound material preparation to achieve the effects of excellent material mechanical properties, improvement of high impurity content, and reduction of material production costs

Active Publication Date: 2015-05-20
UNIV OF SCI & TECH BEIJING
View PDF15 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are no relevant research reports on the application of infiltration technology to the preparation of high-niobium titanium-aluminum alloy materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for manufacturing high-niobium titanium-aluminum alloy material by adopting two-step pressure infiltration

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 4

[0026] -200 mesh Ti powder, -325 mesh Nb element powder and high-purity Al plate are used as raw materials, and the ratio is carried out according to the nominal composition Ti-45Al-8.5Nb. After mechanically mixing the Ti and Nb element powders uniformly, they were put into a Φ30 graphite mold, vibrated and pressed to obtain a green compact with a density of 68%. After polishing the surface of the wire-cut Al plate, place it on the powder compact in the mold, and then put the mold as a whole into a high-pressure infiltration furnace. The infiltration process is carried out under the protection of high-purity Ar gas, and the temperature is rapidly raised to 750°C at 10°C / min, and the heat preservation time is 60min. After 20min of heat preservation, an axial pressure of 20MPa is applied; °C / min. Slowly raise the temperature to 850 °C, keep the temperature for 120 min, and then continue to pressurize and cool to room temperature with the furnace to obtain a high-niobium titanium...

Embodiment 5

[0028]-500 mesh Ti, Nb element powder and high-purity Al plate are used as raw materials, and the ratio is carried out according to the nominal composition Ti-45Al-5Nb. After the Ti and Nb element powders were mechanically mixed, they were put into a Φ30 graphite mold and vibrated to obtain a powder green body with a density of 56%. After polishing the surface of the wire-cut Al plate, place it on the mixed powder in the mold, and then put the mold as a whole into a high-pressure infiltration furnace. Infiltration process in the vacuum degree ≤ 10 -1 Under the vacuum condition of Pa, the temperature is raised rapidly to 700°C at 5°C / min, and the heat preservation time is 40min, and the axial pressure of 30MPa is applied after 10min of heat preservation; the axial pressure is increased to 30MPa, and the temperature is slowly raised at 6°C / min To 1000 ℃, keep warm for 60 minutes, then continue to pressurize and cool to room temperature with the furnace, and then obtain high-nio...

Embodiment 6

[0030] -325 mesh Ti powder, -500 mesh Nb element powder and high-purity Al plate are used as raw materials, and the ratio is carried out according to the nominal composition Ti-45Al-10Nb. After the Ti and Nb elemental powders are mechanically mixed, they are put into a Φ30 graphite mold, vibrated and pressed to obtain a green compact with a density of 60%. The wire-cut Al plate is placed on the powder body in the mold, and then the whole mold is placed in a high-pressure infiltration furnace. The infiltration process is carried out under the protection of high-purity Ar gas, and the temperature is rapidly raised to 800°C at 7°C / min, and the heat preservation time is 120min. After 30min of heat preservation, an axial pressure of 10MPa is applied; °C / min. Slowly raise the temperature to 950 °C, hold the temperature for 80 minutes, and then continue to pressurize and cool to room temperature with the furnace, and then the high-niobium titanium-aluminum alloy infiltration green bo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
compression ratioaaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for manufacturing a high-niobium titanium-aluminum alloy material by adopting two-step pressure infiltration. The method includes the steps that Ti element powder, Nb element powder and the like are evenly mixed, then the mixture and a high-purity Al plate are put into a graphite mold, and the graphite mold is placed into a high-pressure infiltration furnace; the temperature rises to 700 DEG C-800 DEG C at the speed of 5-10 DEG C / min and then is kept for 30-60 min, and axial pressure of 10-30 MPa is exerted on the furnace; the temperature rises to 800 DEG C-1000 DEG C at the speed of 3-6 DEG C / min, pressure of 30-50 MPa is exerted on the furnace, the temperature is kept for 60-120 min, the pressure is continuously exerted, an infiltration blank is obtained by cooling the Al plate with the mixture in the furnace to the room temperature, heat treatment is carried out on the infiltration blank at the temperature of 1300 DEG C-1500 DEG C for 2-6 h, and the high-compactness high-niobium titanium-aluminum alloy block material can be obtained by cooling the infiltration blank in the furnace to the room temperature. The method is simple in technology, short in flow path, and low in cost and has the advantage of near-net forming, and the content of impurities is easy to control; the manufactured high-niobium titanium-aluminum alloy material is high in compactness, uniform in component formation and excellent in mechanical property.

Description

technical field [0001] The invention provides a method for preparing a high-niobium-titanium-aluminum alloy material by pressure infiltration, and belongs to the technical field of preparation of intermetallic compound materials. technical background [0002] TiAl-based intermetallic compounds, based on the long-range ordered arrangement of atoms and unique bonding between atoms, have the characteristics of low specific gravity, good high-temperature strength, excellent oxidation resistance, and creep resistance. Compared with other high-temperature alloys, they have more excellent high-temperature properties. Comprehensive performance, it is recognized as a new generation of lightweight high-temperature-resistant structural materials with the most application potential. The high-Nb-TiAl alloy developed by Academician Chen Guoliang in my country increases the limit service temperature of the alloy by 60-100 °C on the basis of maintaining the advantages of conventional TiAl...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F3/16B22F3/10C22C14/00C22C30/00C22C1/04
Inventor 路新刘程程曲选辉王涛温宏远佟健博章林
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com