A kind of cemented carbide composite forming method

A cemented carbide and composite forming technology, applied in the field of material forming, can solve the problems of inaccessible net forming of parts and complex shape cavity, and achieve the effect of low processing cost, small processing allowance and convenient forming.

Active Publication Date: 2016-05-04
SEED TECH CORP LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of the present invention is to provide a cemented carbide composite molding method to solve the problem that the parts with complex shapes, internal pores and multi-flow channels are difficult to achieve near-net molding.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cemented carbide composite forming method
  • A kind of cemented carbide composite forming method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The cemented carbide composite molding method provided by the invention comprises the following steps:

[0034] S1. Preparation of the mixture: mixing binder, molding agent, and cemented carbide raw material particles with different particle sizes to form a mixture;

[0035] S2. Combined mold design: According to the shrinkage coefficient of the product, use the mold design tool to design the combined mold. The combined mold includes the lower runner mold, the inner concave cavity mold, the cavity disappearing mold and the upper covering mold;

[0036] S3. One-time extrusion molding: inject the mixture into the mold cavity of the lower runner mold and the inner concave cavity mold, and then extrude the mixture after induction heating from bottom to top to form the bottom runner and concave cavity;

[0037] S4. Secondary extrusion molding: After cooling and decompressing the lower runner mold and the inner concave cavity mold, put it into the cavity disappearing mold and...

Embodiment 2

[0045] Preferably, the above-mentioned embodiment 1 of the present invention may also include step S6 between steps S1 and S2, smelting, rolling and crushing of the mixture: heating the mixture into a viscous state, rolling, and then crushing, specifically, The mixture is heated in sections at a heating temperature of 120°C to 160°C. After heating, the mixture becomes viscous, and the viscous mixture is rolled to make the thickness reach 0.15-0.2mm. Repeat 2-4 times. And then broken. This can eliminate the bubbles caused by the expansion of the molding agent when the raw materials are mixed, improve the solid density of the mixture, and ensure that the subsequent injection of the mixture is more uniform and the filling is more compact.

[0046] Specifically, in the above-mentioned embodiment 1, in step S2, three-dimensional three-dimensional software is used to design the combined mold, and through analog analysis and finite element analysis, the design scheme of the optimal p...

Embodiment 3

[0050] Preferably, the above embodiment 1 or embodiment 2 of the present invention further includes step S7 between steps S4 and S5,

[0051] S7. Removal of forming agent: degumming and degreasing the green body obtained in step S4, so as to remove the forming agent in the green body and make the mold cavity in the green body disappear.

[0052] Specifically, the step S7 includes steps S71 and S72,

[0053] S71. Low-temperature degumming: Soak the green body in gasoline at 70-90°C for 28 hours. Of course, the soaking time can be between 25 hours and 30 hours. This low-temperature soaking method can remove 2%~ of the total amount of molding agent. 2.5%;

[0054] S72. High-temperature degreasing: put the green body soaked in gasoline into a vacuum degreasing furnace, raise the temperature in the first section to above 400°C, and keep it warm for 15 minutes. Cooling out of the oven, the remaining molding agent in the product body is completely removed.

[0055] Preferably, in ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
crystal sizeaaaaaaaaaa
Login to view more

Abstract

A hard alloy composite molding method comprises: mixture preparation; design of a modular mold; primary extrusion molding; secondary extrusion molding; and vacuum sintering molding. The advantages of mold pressing, warm pressing and induction heating are combined, so that a part having a complex shape and cavity and an internal multi-pore and multi-runner combination can be molded in a near-net way as a whole once.

Description

technical field [0001] The invention relates to the technical field of material forming, in particular to a cemented carbide composite forming method. Background technique [0002] Generally, cemented carbide has excellent properties such as wear resistance, heat resistance, corrosion resistance, high hardness, good strength and toughness, especially its high hardness and wear resistance make cemented carbide materials not only used in knives and tools Instead, it has expanded to more modern high-tech fields, such as the application of key components in industries such as petrochemical, marine engineering, aviation engineering, and high-speed rail transit engineering. These key parts often have complex shapes and cavities, and the internal structure is a combination of porous and multi-flow channels. Cemented carbide brings difficulties in forming and processing due to its inherent high hardness. How to solve the problem of such complex cavities and special-shaped parts The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/05C22C29/08B22F3/20
CPCB22F3/20C22C1/05C22C29/08
Inventor 徐跃华王玉鹏
Owner SEED TECH CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap