Wear-resistant oil-resistant flame-retardant polyvinyl chloride wire and cable material and preparation method thereof

A flame-retardant polyvinyl chloride, wire and cable material technology, applied in the direction of insulating cables, cables, circuits, etc., can solve the problems of not too high degree of polymerization, limited use, failure to meet wear resistance and oil resistance requirements, etc.

Inactive Publication Date: 2015-03-11
HUIZHOU LTK ELECTRONICS CABLE +3
View PDF2 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since the polyvinyl chloride used in the wire and cable industry is soft polyvinyl chloride, the degree of polymerization cannot be too high, and because it is relatively hard, it needs to be softened in order to meet the needs of wire and cable, and in order to meet the requirements of heat resistance, low temperature resistance, Migration resistance and other properties and to meet the processing requirements, a certain amount of plasticizer must also be added, which makes it unable to meet the requirements of wear resistance and oil resistance. Therefore, the use in industries such as automobile machinery and minerals that require wear resistance and oil resistance has been greatly restricted.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0052] This embodiment discloses a wear-resistant, oil-resistant and flame-retardant polyvinyl chloride wire and cable material, the formula of which is by weight:

[0053] 100 parts of polyvinyl chloride (PVC);

[0054] 60 parts of trioctyl trimellitate (TOTM);

[0055] 5 parts of epoxy soybean oil (EPOXY);

[0056] Composite stabilizer 5 parts;

[0057] 5 parts of antimony trioxide;

[0058] Composite flame retardant 15 parts;

[0059] 20 parts of silicon aluminum ore powder;

[0060] 10 parts of nitrile rubber;

[0061] 0.6 parts of stearic acid.

[0062] This embodiment also discloses a method for preparing the above-mentioned wire and cable material, the characteristic steps are as follows:

[0063] 1) Add substance a into the high-speed mixer, then add powder or oily substance c, run the high-speed mixer at low speed and mix for 1 minute, then add half of the components of substance b, and the high-speed mixer changes from low speed to high speed Run and mix for ...

Embodiment 2

[0073] This embodiment discloses another kind of wear-resistant, oil-resistant and flame-retardant polyvinyl chloride wire and cable material of another formula, and its formula is as follows in parts by weight:

[0074] 100 parts of polyvinyl chloride (PVC);

[0075] Dioctyl terephthalate (DOTP) 70 parts;

[0076] Composite stabilizer 7 parts;

[0077] 30 parts of calcium carbonate;

[0078] 6 parts of antimony trioxide;

[0079] Composite flame retardant 4 parts;

[0080] 20 parts of magnesium hydroxide;

[0081] 15 parts of nitrile rubber;

[0082] 20 parts of vinyl chloride;

[0083] 0.4 parts of polyethylene wax.

Embodiment 3

[0085] This embodiment discloses another kind of wear-resistant, oil-resistant and flame-retardant polyvinyl chloride wire and cable material of another formula, and its formula is as follows in parts by weight:

[0086] 100 parts of polyvinyl chloride (PVC);

[0087] 60 parts of trioctyl trimellitate (TOTM);

[0088] Composite stabilizer 7 parts;

[0089] 8 parts of antimony trioxide;

[0090] Composite flame retardant 7 parts;

[0091] 25 parts of vinyl chloride;

[0092] Compound lubricant 0.6 parts.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of a polyvinyl chloride material used for making wire and cable and discloses a wear-resistant oil-resistant flame-retardant polyvinyl chloride wire and cable material. The formula of the material provided by the invention contains the following ingredients, by weight, 100 parts of polyvinyl chloride (PVC), 55-75 parts of one or more substances selected from trimellitate, polyester and an epoxy plasticizer, 5-10 parts of one or more substances selected from a compound stabilizer and an epoxy compound, 30-50 parts of one or more substances selected from antimonous oxide, magnesium hydroxide, a composite flame retardant and calcium carbonate, 10-35 parts of one or more substances selected from ethylene chloride and nitrile rubber, 0.5-0.8 part of one or more substances selected from stearic acid, polyethylene wax and a composite lubricant and 1-2 parts of color masterbatch. The wire and cable prepared by the technical scheme can have effects of wear resistance, oil resistance and flame retardation.

Description

technical field [0001] The invention relates to the field of polyvinyl chloride materials used for making wires and cables, in particular to a wear-resistant, oil-resistant and flame-retardant polyvinyl chloride wire and cable material and a preparation method thereof. Background technique [0002] Polyvinyl chloride is an excellent wire and cable insulation sheath material, light weight, translucent, shiny, not easily corroded by acid and alkali, good mechanical properties, excellent dielectric properties, and low price, so in The wire and cable industry has always occupied an important share. However, since the polyvinyl chloride used in the wire and cable industry is soft polyvinyl chloride, the degree of polymerization cannot be too high, and because it is relatively hard, it needs to be softened in order to meet the needs of wire and cable, and in order to meet the requirements of heat resistance, low temperature resistance, For properties such as migration resistance ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L9/02C08K13/02C08K5/12C08K5/1515C08K3/26C08K3/34C08K3/22C08K5/02C08K5/09H01B7/17
CPCC08L27/06C08L2201/02C08L2203/202C08L2205/03C08L2205/035H01B7/17
Inventor 林艺章杨中宝
Owner HUIZHOU LTK ELECTRONICS CABLE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap