Multifunctional inorganic diatom ooze coating and preparation method thereof

A diatom mud coating, multi-functional technology, applied in the direction of alkali metal silicate coatings, antifouling/underwater coatings, coatings, etc. Insufficient force, low water resistance of coatings and other problems, to achieve excellent storage stability, optimize brittleness, and improve bonding performance

Inactive Publication Date: 2015-03-04
佛山市南海万磊建筑涂料有限公司
View PDF6 Cites 63 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Existing coatings use potassium silicate solution as a film-forming substance. Potassium silicate provides excellent adhesion performance, but due to the existence of alkali metal ions, the adhesion of the coating is not enough. At the same time, due to the existence of alkali metal ions, the The water resistance of the paint is low; in addition, the existing film-forming substances have poor air permeability, so that the anti-corrosion, antibacterial, absorbent and other properties added to the paint cannot be fully utilized

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multifunctional inorganic diatom ooze coating and preparation method thereof
  • Multifunctional inorganic diatom ooze coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] A kind of multifunctional inorganic diatom mud coating, it is made of the following components by weight percentage:

[0042] Water 21.4%, hydroxypropyl cellulose 0.6%, mixture of potassium silicate and silica sol 20%, calcium stearate 0.3%, methyl amyl alcohol 0.2%, simethicone 0.2%, tributyl phosphate 0.4% , silver oxide 0.2%, titanium dioxide 10%, nano diatomite 13%, heavy calcium 18%, talcum powder 3%, medical stone 2%, nano negative ion powder 1%, nano titanium dioxide 1%, magnesium aluminum silicate 1.7% rubber powder, 6% pure flavor emulsion, 1% pigment; the mass ratio of the mixture of potassium silicate and silica sol to potassium silicate is 10:7, and the negative ion generation amount of the nano negative ion powder is 20000ionsS / CC, the particle size of the heavy calcium is 800 mesh.

[0043] Its preparation method comprises the following steps in turn:

[0044] a. Weigh each component according to the formula, add water and cellulose into the stirring co...

Embodiment 2

[0051] A multifunctional inorganic diatom mud coating, which is made of the following components by weight percentage: 11.3% water, 0.5% hydroxypropyl cellulose, 30% mixture of potassium silicate and silica sol, calcium stearate 0.3%, methyl amyl alcohol 0.2%, simethicone 0.2%, tributyl phosphate 0.3%, silver oxide 0.2%, titanium dioxide 15%, nano diatomite 10%, heavy calcium 22%, talc 4% , medical stone 2%, nano-anion powder 0.5%, nano-titanium dioxide 0.5%, magnesium-aluminum silicate gel powder 2%, net taste emulsion 0%, pigment 1%; the quality of the mixture of potassium silicate and silica sol The mass ratio with potassium silicate is 10:7, the negative ion generating capacity of the nano negative ion powder is 20000 ionS / CC, and the particle diameter of the heavy calcium is 800 mesh. Its preparation method is with embodiment 1.

Embodiment 3

[0053] A multifunctional inorganic diatom mud coating, which is made of the following components by weight percentage: 16% water, 0.6% hydroxypropyl cellulose, 25% mixture of potassium silicate and silica sol, calcium stearate 0.3%, methyl amyl alcohol 0.2%, simethicone 0.2%, tributyl phosphate 0.4%, silver oxide 0.2%, titanium dioxide 5%, nano diatomite 12%, heavy calcium 26%, talc 4% , medical stone 2%, nano-anion powder 1%, nano-titanium dioxide 0.6%, magnesium-aluminum silicate gel powder 1.5%, net taste emulsion 4%, pigment 1%; the quality of the mixture of potassium silicate and silica sol The mass ratio with potassium silicate is 10:7, the negative ion generating capacity of the nano negative ion powder is 20000 ionS / CC, and the particle diameter of the heavy calcium is 800 mesh. Its preparation method is with embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
Login to View More

Abstract

The invention relates to a multifunctional inorganic diatom ooze coating, which is prepared from the following components in percentage by mass: 10%-25% of water, 0.4%-0.8% of cellulose, 10-30% of a mixture of potassium metasilicate and silica sol, 0.2%-0.4% of a stabilizer, 0.1%-0.3% of a dispersing agent, 0.1%-0.3% of a silicon additive, 0.3%-0.5% of a defoaming agent, 0.1%-0.3% of an antibacterial agent, 0-20% of titanium dioxide, 5%-15% of nanometer kieselguhr, 10%-30% of coarse whiting, 2%-4% of talcum powder, 1%-3% of medical stone, 0-1.5% of anion, 0-2% of a nano-photocatalyst, 1%-2% of inorganic gel powder, 0-9% of an order-removing emulsion and 0-1.5% of pigment, wherein the sum of the components is 100%. The invention also provides a preparation method of the coating. The coating disclosed by the invention has the functions of sterilizing, preventing mold, purifying air and the like; and the preparation method disclosed by the invention is simple and easy to operate.

Description

technical field [0001] The invention relates to the field of coatings, in particular to a multifunctional inorganic diatom mud coating and a preparation method thereof. Background technique [0002] Coating is a material that can be coated on the surface of an object by different construction techniques to form a solid film with strong adhesion, certain strength and continuity. The film formed in this way is commonly called coating film, also known as paint film or coating, which is composed of three basic substances: film-forming substances, secondary film-forming substances and auxiliary film-forming substances. Existing coatings use potassium silicate solution as a film-forming substance. Potassium silicate provides excellent adhesion performance, but due to the existence of alkali metal ions, the adhesion of the coating is not enough. At the same time, due to the existence of alkali metal ions, the The water resistance of the paint is low; in addition, the existing film...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/04C09D1/00C09D5/14C09D7/12
Inventor 陈哈仔
Owner 佛山市南海万磊建筑涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com