Ceramic composite with high absorptive property and preparation method of ceramic composite

A ceramic composition and high adsorption technology, applied in the field of composite ceramic materials, can solve problems such as narrowing the application field, and achieve the effects of high flexural strength, low firing shrinkage rate and strong adsorption rate

Inactive Publication Date: 2015-02-18
华文蔚
View PDF7 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] However, the adsorption performance of the ceramic compositions disclosed in these patents still needs to be improved, which narrows its application field.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic composite with high absorptive property and preparation method of ceramic composite
  • Ceramic composite with high absorptive property and preparation method of ceramic composite
  • Ceramic composite with high absorptive property and preparation method of ceramic composite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Raw materials are configured by weight percentage: 9.3% of crystallized bamboo charcoal powder, 0.2% of graphene, 0.5% of titanium dioxide, 50% of tourmaline crystal particles, and 40% of clay. The crystallized bamboo charcoal powder used in this embodiment is fired at a high temperature above 1200° C., and the average particle size of the bamboo charcoal powder is 30 μm to 100 μm. The tourmaline powder used is high-purity tourmaline ore crystal, tourmaline crystallinity ≥ 95%, dynamic negative ion value ≥ 500ions / cm3, far-infrared radiation rate ≥ 90% with a wavelength of 4 μm to 14 μm. The average particle size of the tourmaline powder is 10 μm to 50 μm. After mixing, forming, drying, and slowly heating up to 600-800°C in a reducing atmosphere for calcination, pottery casserole and electric rice cooker liner are produced.

Embodiment 2

[0037] Raw materials are configured by weight percentage: 74% of crystallized bamboo charcoal powder, 0.5% of graphene, 5% of titanium dioxide, 10% of tourmaline crystal particles, and 10.5% of clay. The crystallized bamboo charcoal powder used in this embodiment is fired at a high temperature above 1200° C., and the average particle size of the bamboo charcoal powder is 30 μm to 100 μm. The tourmaline powder used is high-purity tourmaline ore crystal, tourmaline crystallinity ≥ 95%, dynamic negative ion value ≥ 500ions / cm3, far-infrared radiation rate ≥ 90% with a wavelength of 4 μm to 14 μm. The average particle size of the tourmaline powder is 10 μm to 50 μm. After mixing, molding, drying, and slowly heating up to 600-800°C in a reducing atmosphere for calcination, ceramic tea sets and tableware are produced.

Embodiment 3

[0039]Raw materials are configured by weight percentage: 25% of crystallized bamboo charcoal powder, 0.3% of graphene, 3% of titanium dioxide, 31.7% of tourmaline crystal particles, and 40% of clay. The crystallized bamboo charcoal powder used in this embodiment is fired at a high temperature above 1200° C., and the average particle size of the bamboo charcoal powder is 30 μm to 100 μm. The tourmaline powder used is high-purity tourmaline ore crystal, tourmaline crystallinity ≥ 95%, dynamic negative ion value ≥ 500ions / cm3, far-infrared radiation rate ≥ 90% with a wavelength of 4 μm to 14 μm. The average particle size of the tourmaline powder is 10 μm to 50 μm. After mixing, forming, drying, and slowly heating up to 600-800°C in a reducing atmosphere for calcination, a food preservation container is obtained.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a ceramic composite with high absorptive property. The ceramic composite is composed of the following components in percentage by weight: 9.3 to 74.5 percent of bamboo charcoal powder, 0.2 to 0.5 percent of graphene, 0.5 to 5 percent of tianium dioxide, 10 to 80 percent of tourmaline crystal particles and 10 to 80 percent of clay. The ceramic composite with high absorptive property has the advantages of large specific surface area and light self-cleaning capability, and is capable of effectively absorbing harmful gases such as formaldehyde and benzene, thereby purifying air; the preparation method is simple and suitable for industrial production.

Description

technical field [0001] The invention relates to the technical field of composite ceramic materials, in particular to a ceramic composition with high adsorption performance and a preparation method thereof. Background technique [0002] Tourmaline is a silicate mineral with a ring structure of aluminum, iron, sodium, magnesium, and lithium, which is characterized by boron. It is black or gray-black, and has a thick needle, bundle, or radial structure. Tourmaline has special pyroelectricity and piezoelectricity, has high far-infrared radiation and negative ion release ability, and contains a variety of trace elements beneficial to human health. It is widely used in drinking water activation, air purification, sewage treatment, Ceramics, building materials, daily chemicals, electronics, textiles, health care products, beauty cosmetics and other fields. [0003] Bamboo charcoal has a rich honeycomb microporous structure. This microporous structure makes bamboo charcoal have a l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/13C04B35/528C04B35/16C04B35/622
CPCC04B35/528C04B33/13C04B35/16C04B2235/3232C04B2235/3427C04B2235/349C04B2235/422C04B2235/425C04B2235/5436
Inventor 华文蔚
Owner 华文蔚
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products