A kind of preparation method of polyhedral nano-oxide for catalysis

A technology of nano-oxides and polyhedrons, applied in chemical instruments and methods, metal/metal oxide/metal hydroxide catalysts, chemical/physical processes, etc., can solve serious powder agglomeration, poor catalytic performance, and oversized particles and other problems, to achieve the effect of good crystal morphology, improved performance of catalytic degradation of organic pollutants, and low synthesis temperature

Active Publication Date: 2016-08-17
上海泛翌新材料有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to provide a method for preparing polyhedral nano-oxides for catalysis in order to solve the problems of the existing copper oxide powder synthesis technology, such as too large particles, too serious powder agglomeration, etc., and the problems of poor catalytic performance caused thereby.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of polyhedral nano-oxide for catalysis
  • A kind of preparation method of polyhedral nano-oxide for catalysis
  • A kind of preparation method of polyhedral nano-oxide for catalysis

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The invention discloses a preparation method of nano polyhedral oxide for catalysis, that is, nano copper oxide.

[0031] The copper salt used in the preparation is Cu(NO 3 ) 2 ·3H 2 O, the alkali source used is NH 3 ·H 2 O, the molten salt used is KNO 3 , NaNO 3 .

[0032] Weigh 15.1gCu(NO 3 ) 2 ·3H 2 O, dissolved in 125ml deionized water to form a 0.5mol / l solution, add NH dropwise 3 ·H 2 O until the pH of the solution is between 6-8, stir on a constant temperature magnetic stirrer at 60°C for 1.5h at a constant temperature, filter and wash two to three times after a precipitate is formed, and put it in an oven to dry. Weigh the dried precursor and take a certain amount of KNO 3 and NaNO 3 , and put them together into a ball mill jar for ball milling for 2h.

[0033] KNO used above 3 and NaNO 3 The molar ratio of the substance is 1:1, the mass ratio of the dried product to the molten salt is 45:55, and the ball:material:alcohol in the ball mill tank is...

Embodiment 2

[0037] The invention discloses a preparation method of nano polyhedral oxide for catalysis, that is, nano copper oxide.

[0038] The copper salt used in the preparation is CuCl 2 2H 2 O, the alkali source used is NH 3 ·H 2 O, the molten salt used is KNO 3 , NaNO 3 .

[0039] Weigh 10.655g CuCl 2 2H 2 O, dissolved in 125ml deionized water to form a 0.5mol / l solution, add NH dropwise 3 ·H 2O until the pH of the solution is between 6-8, stir on a constant temperature magnetic stirrer at 60°C for 1.5h at a constant temperature, filter and wash two to three times after a precipitate is formed, and put it in an oven to dry. Weigh the dried precursor and take a certain amount of KNO 3 and NaNO 3 , and put them together into a ball mill jar for ball milling for 2h.

[0040] KNO used above 3 and NaNO 3 The molar ratio of the substance is 1:1, the mass ratio of the dried product to the molten salt is 45:55, and the ball:material:alcohol in the ball mill tank is 2:1:0.6.

...

Embodiment 3

[0043] The invention discloses a preparation method of nano polyhedral oxide for catalysis, that is, nano copper oxide.

[0044] The copper salt used in the preparation is Cu(NO 3 ) 2 ·3H 2 O, the alkali source used is NaOH, and the molten salt used is KNO 3 , NaNO 3 .

[0045] Weigh 15.1gCu(NO 3 ) 2 ·3H 2 O, dissolve in 125ml deionized water to form a 0.5mol / l solution, add NaOH dropwise until the pH of the solution is between 6-8, then stir on a constant temperature magnetic stirrer at 60°C for 1.5h, and filter with suction after precipitation is formed Wash two to three times and place in the oven to dry. Weigh the dried precursor and take a certain amount of KNO 3 and NaNO 3 , and put them together into a ball mill jar for ball milling for 2h.

[0046] KNO used above 3 and NaNO 3 The molar ratio of the substance is 1:1, the mass ratio of the dried product to the molten salt is 45:55, and the ball:material:alcohol in the ball mill tank is 2:1:0.6.

[0047] Dry...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a method for preparing a catalytic polyhedral nano oxide, were prepared to give a powder of copper oxide nano polyhedral sodium source and potassium source is a molten salt Method molten salt, copper salt dissolved in water into a solution configured to alkaline source added dropwise until the pH of the solution between 6 and 8, the solution was put in a constant temperature 60 deg.] C temperature with a magnetic stirrer was stirred until a precipitate after filtration was washed generate two to three times, dried in an oven ; dried precursor with sodium and potassium salts together into a ball mill jar milling; milling the dried mixture is transferred into the crucible is calcined, and then cooled in air to room temperature, filtered, washed, dried, preparation to obtain nano-copper oxide powder polyhedral shape. Preparation process of the invention has a lower synthesis temperature, simple, uniform powder synthetic chemical components, good crystal morphology, etc., rhodamine B experiments showed degraded, compared to copper oxide nano goods, a substantial catalytic performance improve.

Description

technical field [0001] The invention relates to the technical field of preparation of polyhedral nano-oxides, in particular to a method for preparing polyhedral nano-oxides for catalysis. Background technique [0002] The nano-catalytic technology that has just started in my country, although only TiO 2 , ZnO, and a few varieties have been industrialized. But it has shown good prospects for development. At the nanotechnology seminar that ended at the end of 2004, experts believed that nanomaterials have unique crystal structures and surface properties, and their catalytic activity and selectivity are much higher than traditional catalysts, and can be used as new catalytic materials in the chemical industry. Undoubtedly, as the particle size of nanoparticles decreases, the surface area gradually increases, and the adsorption capacity and catalytic performance are also enhanced. These unique effects enable nano-catalysts to not only control the reaction speed, greatly impro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/72B01J35/02B01J35/00
Inventor 曾涛白杨刘伟景姚伟峰
Owner 上海泛翌新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com