A method for shortening the gas nitriding process time of alloy structural steel

A technology of alloy structural steel and process time, applied in the direction of metal material coating process, coating, solid-state diffusion coating, etc., can solve the problems of low production efficiency, long nitriding time, etc., and achieve increased driving force and increased surface Nitrogen concentration, the effect of accelerating the spreading speed

Active Publication Date: 2016-07-27
HARBIN TURBINE +1
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problem of long nitriding time and low production efficiency in the nitriding process of existing alloy structural steel, and to provide a method for shortening the gas nitriding process time of alloy structural steel

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0019] Specific implementation mode 1: This implementation mode is a method for the nitriding process of alloy structural steel, which is specifically completed according to the following steps:

[0020] 1. Mix the infiltration agent and dry sand evenly to obtain the infiltration agent / sand mixture, and then put the infiltration agent / sand mixture into the iron drum;

[0021] The mass ratio of the quality of the infiltrating agent described in step 1 to the dry sand is 1:(2~3);

[0022] 2. Put the alloy structural steel workpiece and the iron drum containing the infiltration agent / sand mixture in the nitriding tank, seal the furnace cover, and feed ammonia gas until the volume fraction of ammonia gas in the nitriding tank is 90%. Heating evenly until the temperature of the nitriding tank is 530°C-540°C, then keeping the ammonia decomposition rate at 20%-35% and the temperature at 530°C-540°C for 20 hours, then cooling naturally with the furnace until the temperature is lower t...

specific Embodiment approach 2

[0034] Embodiment 2: The difference between this embodiment and Embodiment 1 is that the osmotic agent described in step 1 is granular or powdery. Other steps are the same as in the first embodiment.

specific Embodiment approach 3

[0035] Embodiment 3: This embodiment differs from Embodiment 1 or Embodiment 2 in that: the penetrating agent described in step 1 is polyvinyl chloride. Other steps are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
depthaaaaaaaaaa
hardnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for shortening the gas nitriding process time of alloy structural steel, which relates to a method for shortening the gas nitriding process time of steel. The purpose of the invention is to solve the problem of long nitriding time and low production efficiency in the existing nitriding process of alloy structural steel. Method: 1. Put the infiltrating agent / sand mixture into the iron drum; 2. Put the alloy structural steel workpiece and the iron drum containing the infiltrating agent / sand mixture in the nitriding tank, seal the furnace cover, and put it into Ammonia, until the volume fraction of ammonia in the nitriding tank is 90%, and then uniformly heated until the temperature of the nitriding tank is 530°C-540°C, and then the ammonia decomposition rate is 20%-35% and the temperature is 530°C-540 ℃ for 20 hours, and then naturally cooled with the furnace until the temperature is lower than 150 ℃, it can be taken out of the furnace, and a nitrided alloy structural steel workpiece with a nitrided layer depth of ≥0.3mm can be obtained. The invention can obtain a method for nitriding process of alloy structural steel.

Description

technical field [0001] The invention relates to a method for shortening the process time of steel gas nitriding. Background technique [0002] Nitriding belongs to chemical heat treatment. The process of infiltrating nitrogen into the metal surface is called nitriding, also called nitriding. Nitriding can improve metal surface hardness (up to HV900-1200, equivalent to HRc65-72), wear resistance, fatigue strength and corrosion resistance. It also has the advantages of low nitriding temperature and small deformation. The commonly used temperature is 500-600°C. The disadvantage of nitriding is that the permeation layer is shallow and the process time is long. The depth of the nitriding layer is between 0.15 and 0.75 mm, and the nitriding time is between 10 and 100 hours. Such a long process time will inevitably result in low production efficiency and high energy consumption. Therefore, accelerating the nitriding speed and shortening the process time has been one of the imp...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C23C8/26
Inventor 高枝森王淑新盛昆川梁小丹周策李应新曹利峰林延伟马春斌王立伟
Owner HARBIN TURBINE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com