Production technology of grooved metal gasket

A production process and gasket technology, which is applied in the field of toothed gasket production technology, can solve the problems of weak flexibility, poor wear resistance of gaskets, low wear resistance and low corrosion resistance

Inactive Publication Date: 2014-12-24
无锡市新颖密封材料厂
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The wear resistance and corrosion resistance of the existing sealing gasket fiber are not high, the flexibility is not strong, the gasket produced is not wear-resistant, and the service life is not long

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The toothed gasket production process includes the following steps:

[0019] 1) Evenly mix rubber, graphite powder and accelerator in a weight ratio of 5:2:2 for use;

[0020] 2) Put the mixture into the mold, and then put it into the heating furnace together with the mold. The temperature in the furnace is controlled below 200°C, raised to 500°C, and kept for 3 hours; continue to heat up to 1200°C, kept for 2 hours, and cooled to 750°C in the furnace ℃, and conduct a stable heat treatment in an argon atmosphere;

[0021] 3) Take out the pressed tablet, put it into a vulcanizer, and roll sulfur for 30 minutes at a temperature of 300°C;

[0022] 4) Rinse with tap water after taking it out, and then use air-inducing equipment to dry it.

Embodiment 2

[0024] The toothed gasket production process includes the following steps:

[0025] 1) Evenly mix rubber, graphite powder and accelerator in a weight ratio of 5:2:2 for use;

[0026] 2) Put the mixture into the mold, and then put it into the heating furnace together with the mold. The temperature in the furnace is controlled below 200°C, the temperature is raised to 500°C, and kept for 4 hours; continue to heat up to 1300°C, kept for 4 hours, and cooled to 750°C in the furnace ℃, and conduct a stable heat treatment in an argon atmosphere;

[0027] 3) Take out the pressed tablet, put it into a vulcanizer, and roll sulfur for 40 minutes at a temperature of 350°C;

[0028] 4) Rinse with tap water after taking it out, and then use air-inducing equipment to dry it.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a production technology of a grooved metal gasket. The production technology comprises the following steps: 1) uniformly mixing rubber and powdered graphite with an accelerant according to a weight proportion of 5:2:2 for future use; 2) placing the mixture in a mold, placing the mold in a heating furnace, controlling the initial furnace temperature to be lower than 200 DEG C, raising the temperature to 500 DEG C, keeping the temperature for 3-4 hours, continuously raising the temperature to 1200-1300 DEG C, keeping the temperature for 2-4 hours, cooling the mold in the furnace to 750 DEG C, and carrying out stabilized thermal treatment in an argon environment; 3) taking out the sheet, placing the sheet in a vulcanizing machine, rolling and vulcanizing for 30-40 minutes under a condition that the temperature is 300-350 DEG C; 4) taking out the vulcanized sheet, using running water to rinse the sheet, and drying the sheet with induced draught equipment. The production technology disclosed by the invention is simple to operate and ingenious in the technology; the produced sealing gasket is not liable to abrade and durable in use.

Description

technical field [0001] The invention relates to the field of sealing materials, in particular to a toothed gasket production process. [0002] Background technique [0003] Sealing material refers to the material that can withstand joint displacement to achieve airtight and watertight purposes and embedded in building joints is called sealing material. Seal materials include metallic materials (aluminum, lead, indium, stainless steel, etc.), non-metallic materials (rubber, plastic, ceramics, graphite, etc.), composite materials (such as rubber-asbestos board, airgel felt-polyurethane), but The most used is rubber-like elastomer material. The wear resistance and corrosion resistance of the existing sealing gasket fiber are not high, the flexibility is not strong, the gasket produced is not wear-resistant, and the service life is not long. Contents of the invention [0004] The object of the present invention is to provide a toothed gasket production process to solve the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L21/00C08K3/04C08J3/00
Inventor 陆峰
Owner 无锡市新颖密封材料厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com