High-temperature resistant fiber blended fabric

A technology of high-temperature-resistant fibers and blended fabrics, applied in textiles, textiles, papermaking, fabrics, etc., can solve the problems of not meeting the production efficiency of enterprises and high costs, and achieve low production costs, excellent high-temperature resistance, and high wearing safety. Effect

Inactive Publication Date: 2014-12-10
陈朝阳
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the existing protective clothing is made of polytetrafluoroethylene fiber. Although it has excellent performance in all aspects, the cost is relatively high, which does not meet the production efficiency of the enterprise.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] The preferred embodiments of the present invention are described in detail below, so that the advantages and features of the present invention can be more easily understood by those skilled in the art, so as to define the protection scope of the present invention more clearly.

[0010] The invention describes a high temperature resistant fiber blended fabric, the high temperature resistant fiber blended fabric is made of polybenzimidazole fiber, polyparaphenylene terephthalamide fiber, boron nitride fiber and polyamideimide fiber Blended and woven, the weight percentages of the fiber components in the high-temperature-resistant fiber blended fabric are respectively: the polybenzimidazole fiber accounts for 13%-17%, and the poly-p-phenylene terephthalamide The fiber accounts for 25%-29%, the boron nitride fiber accounts for 10%-14%, and the polyamideimide fiber accounts for 40%-52%.

[0011] Further, the percentage by weight of each fabric fiber component in the high-tem...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-temperature resistant fiber blended fabric. The high-temperature resistant fiber blended fabric is formed by blending polybenzimidazole fibers, poly-p-phenylene terephthamide fibers, boron nitride fibers and polyamide-imide fibers in a woven mode, and comprises, by weight, 13% to 17% of the polybenzimidazole fibers, 25% to 29% of the poly-p-phenylene terephthamide fibers, 10% to 14% of the boron nitride fibers and 40% to 52% of the polyamide-imide fibers. The high-temperature resistant fiber blended fabric is formed by blending the four fabric fibers including the polybenzimidazole fibers, the poly-p-phenylene terephthamide fibers, the boron nitride fibers and the polyamide-imide fibers in the woven mode, and the fabric formed in the woven mode has the excellent high-temperature resistance, the excellent chemical corrosion resistance, the excellent tensile strength and the excellent abrasion resistance, and is high in wearing safety performance and low in production cost.

Description

technical field [0001] The invention relates to a fabric, in particular to a high temperature resistant fiber blended fabric. Background technique [0002] With the continuous development of science and technology, textile fabrics that meet people's different needs emerge in an endless stream to meet the needs of consumers and play an increasingly important role in people's daily life. [0003] Existing various chemical factories are often accompanied by high-temperature production work, and at this time workers need to wear various protective clothing to operate. Most of the existing protective clothing is made of polytetrafluoroethylene fiber. Although it has excellent performance in all aspects, the cost is relatively high, which does not meet the production efficiency of the enterprise. Contents of the invention [0004] The purpose of the present invention is to provide a high temperature resistant fiber blended fabric with good high temperature resistance, good chem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/12D02G3/04D03D15/283D03D15/47D03D15/50D03D15/513D03D15/573D03D15/58
Inventor 陈朝阳
Owner 陈朝阳
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products