Recoatable UV-curing colored one-step-coating aluminum powder paint and preparation method thereof

An ultraviolet light and coating technology, which is applied in polyester coatings, polyether coatings, epoxy resin coatings, etc., can solve the problems of directional arrangement of silver powder and metal texture problems.

Active Publication Date: 2014-12-10
YIXING HONGTAI CHEM
View PDF12 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of composition and preparation method of recoatable ultraviolet curing color-coating silver powder coating, to solve the problems of curing speed and deep layer curing existing in the prior art; problems; problems of rework and recoating adhesion and surface hardness; problems of wear resistance, scratch resistance and chemical resistance, can replace the traditional process of combining heat-cured silver powder paint and UV-cured varnish

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Recoatable UV-curing colored one-step-coating aluminum powder paint and preparation method thereof
  • Recoatable UV-curing colored one-step-coating aluminum powder paint and preparation method thereof
  • Recoatable UV-curing colored one-step-coating aluminum powder paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0060] See the table below for paint formulations.

[0061]

[0062] The preparation method comprises the following steps:

[0063] Step 1: soak and pre-disperse the aluminum powder with a solvent at a ratio of 1:5;

[0064] Step 2: Mix the aluminum powder directional agent with a solvent in a ratio of 1:3, and stir until completely dissolved;

[0065] Step 3: Mix the resin prepolymer and the monomer, heat and stir evenly, then add the photoinitiator, additive, pigment and the remaining solvent, mix and stir until completely dissolved;

[0066] Step 4: Mix the components of Step 1, Step 2 and Step 3 and disperse evenly;

[0067] Step 5: Filter the solution obtained in Step 4 to obtain a recoatable UV-curable color one-coat silver powder paint.

Embodiment 2

[0069] See the table below for paint formulations.

[0070]

[0071] The preparation method comprises the following steps:

[0072] Step 1: soak and pre-disperse the aluminum powder with a solvent in a ratio of 1:4;

[0073] Step 2: Mix the aluminum powder directional agent with a solvent in a ratio of 1:4, and stir until completely dissolved;

[0074] Step 3: Mix the resin prepolymer and the monomer, heat and stir evenly, then add the photoinitiator, additive, pigment and the remaining solvent, mix and stir until completely dissolved;

[0075] Step 4: Mix the components of Step 1, Step 2 and Step 3 and disperse evenly;

[0076] Step 5: Filter the solution obtained in Step 4 to obtain a recoatable UV-curable color one-coat silver powder paint.

Embodiment 3

[0078] See the table below for paint formulations.

[0079]

[0080] The preparation method comprises the following steps:

[0081] Step 1: soak and pre-disperse the aluminum powder with a solvent at a ratio of 1:5;

[0082] Step 2: Mix the aluminum powder directional agent with a solvent in a ratio of 1:3, and stir until completely dissolved;

[0083] Step 3: Mix the resin prepolymer and the monomer, heat and stir evenly, then add the photoinitiator, auxiliary agent and the remaining solvent, mix and stir until completely dissolved;

[0084] Step 4: Mix the components of Step 1, Step 2 and Step 3 and disperse evenly;

[0085] Step 5: Filter the solution obtained in Step 4 to obtain a recoatable UV-curable color one-coat silver powder paint.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glass transition temperatureaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a recoatable UV-curing colored one-step-coating aluminum powder paint and a preparation method thereof. The paint is prepared from the following components in parts by weight: 20-45 parts of photosensitive acrylate prepolymer, 15-25 parts of modified acrylate resin, 10-20 parts of reactive acrylate monomer, 3-7 parts of photoinitiator, 4-8 parts of aluminum powder, 3-7 parts of aluminum powder orienting agent, 0.3-0.7 part of assistant, 0-6 parts of pigment and 15-30 parts of mixed solvent. The paint can be used for ABS (acrylonitrile-butadiene-styrene), PC (polycarbonate), PE (polyethylene), PP (polypropylene), PVC (polyvinyl chloride) and other plastic substrates, and thus, has wide applicability; the paint has the characteristics of high UV curing speed, low VOC (volatile organic compound) content, energy saving and environment friendliness; the paint is simple in construction technique, does not need any additional curing agent, and can achieve the effects of favorable leveling property, orderly aluminum powder arrangement and the like; the coating has the advantages of high hardness, favorable wear resistance, favorable solvent resistance and bright and adjustable color, and can satisfy the demands for protection and decoration by one coating step; and the paint can be recoated repeatedly, and has excellent adhesive force and metal sensation.

Description

technical field [0001] The invention belongs to the field of coatings, and in particular relates to a recoatable ultraviolet light-curable color-coated silver powder coating and a preparation method thereof. Background technique [0002] Plastics have been widely used in automobiles, home appliances, and 3C. The decorative and protective coatings on plastic surfaces are mainly composed of traditional two-component polyurethane or thermoplastic acrylic resins. Such coatings have high energy consumption, heavy pollution, and poor scratch resistance. However, ultraviolet (UV) curing coatings have the advantages of fast response, good chemical resistance, and low odor. At the same time, silver powder coatings have gradually become the preferred choice for plastic coatings due to their beautiful decoration and low volatile organic compound (VOC) content. Application development direction. [0003] Generally speaking, UV curable coatings are colorless and transparent systems, add...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D171/00C09D167/06C09D163/00C09D5/38C08F220/26C08F220/68C08F220/36C08F216/14C08F8/00
Inventor 吴玉民陈朝岚舒航卢礼灿吴刚强
Owner YIXING HONGTAI CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com