Blank material use for preparing porous decorated porcelain by intermediate-temperature firing and porous decorated porcelain preparing method by intermediate-temperature firing

A through-flower porcelain, medium-temperature technology, used in applications, clay products, household appliances, etc., can solve the problems of whiteness, adverse effects of light transmittance, high impurity content, and limited addition of porcelain blanks, and achieve good decorative effects. Low firing temperature, the effect of lowering firing temperature

Active Publication Date: 2014-12-10
潮州市广嘉陶瓷制作有限公司
View PDF4 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

To reduce the firing temperature of ceramics, the usual method is to increase the proportion of flux components in the blank. Since the flux is a barren mineral, it will inevitably have an adverse effect on the plasticity and water retention of the blank; at the same time, due to the clay with good plasticity The content of impurities is high, which will cause adverse effects on the whiteness and light transmittance of the porcelain blank after adding, and the amount of addition is limited

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] 1) Preparation of blank: The blank is made of the following raw materials in parts by mass: 30 parts of quartz, 50 parts of high-alumina clay, 20 parts of synthetic flux, and 1 part of polyvinyl alcohol. The synthetic flux used is made of quartz, borax, spodumene , limestone, zircon and trace amounts of cobalt oxide are mixed, melted at a high temperature of 1300 ℃, and water-quenched into a frit, which contains the following chemical components in parts by mass: SiO 2 64 copies, B 2 o 3 13 copies, Al 2 o 3 6 parts, CaO 2 parts, Na 2 O 6 parts, Li 2 O 2 parts, ZrO 2 4 copies, Co. 3 o 4 0.1 part;

[0034] 2) Grouting molding: Pour the mud into the plaster mold, after standing for a period of time, when the thickness of the green body reaches 4mm, pour out the mud, and take out the green body when the moisture content of the green body is reduced to 18%;

[0035] 3) Engraving through the flower: press the pattern on the surface of the billet manually, and remove ...

Embodiment 2

[0043]1) Preparation of blank: The blank is made of the following raw materials in parts by mass: 25 parts of quartz, 60 parts of high-alumina clay, 15 parts of composite flux, and 1.5 parts of carboxymethyl cellulose. The synthetic flux used is made of quartz, borax, lithium After mixing pyroxene, limestone, zircon and a small amount of cobalt oxide, the frit is melted at a high temperature of 1300 ℃ and water quenched. It contains the following chemical components in parts by mass: SiO 2 64 copies, B 2 o 3 13 copies, Al 2 o 3 6 parts, CaO 2 parts, Na 2 O 6 parts, Li 2 O 2 parts, ZrO 2 4 copies, Co. 3 o 4 0.2 copies;

[0044] 2) Grouting molding: Pour the mud into the plaster mold, after standing for a period of time, when the thickness of the green body reaches 4mm, pour out the mud, and take out the green body when the moisture content of the green body is reduced to 18%;

[0045] 3) Engraving through the flower: press the pattern on the surface of the billet manua...

Embodiment 3

[0053] 1) Preparation of blank: The blank is made of the following raw materials in parts by mass: 30 parts of quartz, 55 parts of high-alumina clay, 15 parts of composite flux, and 1 part of carboxymethyl cellulose. The synthetic flux used is made of quartz, borax, lithium After mixing pyroxene, limestone, zircon and a small amount of cobalt oxide, the frit is melted at a high temperature of 1300 ℃ and water quenched. It contains the following chemical components in parts by mass: SiO 2 66 copies, B 2 o 3 12 copies, Al 2 o 3 8 parts, CaO 3 parts, Na 2 O 5 parts, Li 2 O 3 parts, ZrO 2 3 copies, Co. 3 o 4 0.15 copies;

[0054] 2) Grouting molding: Pour the mud into the plaster mold, after standing for a period of time, when the thickness of the green body reaches 4mm, pour out the mud, and take out the green body when the moisture content of the green body is reduced to 18%;

[0055] 3) Engraving through the flower: press the pattern on the surface of the billet manual...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a blank material use for preparing a porous decorated porcelain by intermediate-temperature firing and a porous decorated porcelain preparing method by intermediate-temperature firing. A synthetic flux is added into the blank material, a composite fluxing function is exerted by combination of a plurality of flux components, and the firing temperature is largely reduced under a circumstance of not increasing the using amount of the flux. The method includes steps of preparing the blank material, moulding by slip casting, sculpturing, making porous patterns, kneading and pasting porcelain patterns, glazing, firing in an oxidation atmosphere having a temperature of 1250-1280 DEG C, performing colored drawing, decorating and roasting at 750-800 DEG C. By tests and research on the synthetic flux, the blank material, glaze, and other formulas, the firing temperature of the porous decorated porcelain is largely reduced, the porous decorated porcelain can be prepared by oxidation and firing at an intermediate temperature of 1250 DEG C, and therefore coloring of all intermediate colorants can be stable, the color of the porous decorated porcelain is largely enriched, and the appearance is more beautiful. The firing temperature is low and the firing period is short. The method saves energy, reduces consumption, and increases the grade of quality of products.

Description

technical field [0001] The invention relates to a blank for medium-temperature firing through-flower porcelain and a preparation method for medium-temperature firing through-flower porcelain, belonging to the technical field of inorganic non-metallic material synthesis. Background technique [0002] Tonghua Porcelain is a kind of carved and hollowed out decorative art with unique local characteristics in Fengxi, Chaozhou. Using the art of three-dimensional hollowing out, engraving transparent geometric patterns on the porcelain body, posting flowers of different shapes hand-kneaded, after firing, there is an artistic effect of white as jade, thin as paper, and thin as silk. After being hand-painted or spray-painted, after roasting, it looks like a flower, and it is difficult to distinguish the true from the false. In order to meet the needs of carving hollows and hand-kneading flowers of different shapes, the blanks are required to have good plasticity and water retention. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B33/22C04B33/24
Inventor 邱伟志黄玉銮
Owner 潮州市广嘉陶瓷制作有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com