Device and process for realizing amorphous metal continuous wire cladding by virtue of extrusion
An amorphous metal and amorphous alloy technology, applied in metal extrusion dies, metal extrusion mandrels, etc., can solve the problem of high price of amorphous alloys, improve production efficiency, facilitate disassembly, and speed up Effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0058] The material of the wire is copper wire with a diameter of 4 mm; the amorphous alloy coated on the outer layer of the copper wire is Zr58.5Cu15.6Ni12.8Al10.3Nb2.8. The glass transition temperature and crystallization temperature of the amorphous alloy Zr58.5Cu15.6Ni12.8Al10.3Nb2.8 are 385°C and 470°C respectively. When the heating temperature is 405°C, it can be kept for 30 minutes without crystallization. Meet the requirements of the coating process. When cladding the amorphous alloy, the heating temperature of the extrusion cylinder and the shaping sleeve is controlled at 403°C to 407°C by a temperature controller. The traction force used for cladding was 500N.
PUM
Property | Measurement | Unit |
---|---|---|
length | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com