Toughened regenerated modified granule manufactured through polyolefin of waste medical plastic transfusion container

A technology of toughening modification and infusion container, which is applied in the resource recycling of medical waste plastics and waste resource recycling. It can solve the problems of performance impact of modified materials, high production cost, and high price, so as to improve the impact strength. , easy to process, and realize the effect of resource recycling

Inactive Publication Date: 2014-11-12
BEIJING CENT FOR PHYSICAL & CHEM ANALYSIS
View PDF2 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] However, in the prior art, a large amount of elastomer needs to be added for toughening, and the production cost is high due to its high price.
In addition, the selection of parameters such as the particle size of the calcium carbonate filler will also have a great impact on the performance of the modified material.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Toughened regenerated modified granule manufactured through polyolefin of waste medical plastic transfusion container
  • Toughened regenerated modified granule manufactured through polyolefin of waste medical plastic transfusion container

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) 75 parts by weight of discarded medical plastic infusion container polypropylene material, 15 parts by weight of ethylene octene copolymer (ENGAGE8150 Dow Plastics), 10 parts by weight of active calcium carbonate (5 microns in particle size), 0.1 part by weight of stearic acid Calcium (purchased from Gaomi Dongfang Chemical Co., Ltd.), 3 parts by weight of POE-g-MAH (CMG5805, Nantong Rizhisheng Molecular New Material Technology Co., Ltd.), 0.1 parts by weight of antioxidant 1010 (purchased from Tixiai ( Shanghai) Chemical Industry Development Co., Ltd.) and 0.2 parts by weight of antioxidant 168 (purchased from TCI (Shanghai) Chemical Industry Development Co., Ltd.) etc. are placed in the mixer, the speed of the mixer is 30rpm, high-speed mixing 3min;

[0030] (2) Put the mixture in step (1) into a twin-screw extruder at an extrusion temperature of 180-230° C., a screw rotation speed of 180 rpm, and a feeding speed of 40 rpm for melt mixing, extrusion injection moldi...

Embodiment 2

[0034] (1) 70 parts by weight of discarded medical plastic infusion container polypropylene material, 10 parts by weight of ethylene octene copolymer (ENGAGE8150 Dow Plastics), 20 parts by weight of active calcium carbonate (5 microns in particle size), 0.2 parts by weight of stearic acid Calcium (purchased from Gaomi Dongfang Chemical Co., Ltd.), 3 parts by weight of POE-g-MAH (CMG5805, Nantong Rizhisheng Molecular New Material Technology Co., Ltd.), 0.1 parts by weight of antioxidant 1010 (purchased from Tixiai ( Shanghai) Chemical Industry Development Co., Ltd.) and 0.2 parts by weight of antioxidant 168 (purchased from TCI (Shanghai) Chemical Industry Development Co., Ltd.) etc. were placed in a mixer.

[0035] (2) Put the neutralized mixture in step (1) into a twin-screw extruder at an extrusion temperature of 180-230° C., a screw speed of 180 rpm, and a feeding speed of 40 rpm for melt mixing, extrusion, injection molding, cutting and granulation.

[0036] Measure the te...

Embodiment 3

[0038](1) 70 parts by weight of discarded medical plastic infusion container polypropylene material, 10 parts by weight of ethylene octene copolymer (ENGAGE8150 Dow Plastics), 20 parts by weight of active calcium carbonate with a particle diameter of 5 microns, 0.2 parts by weight of calcium stearate (purchased from Gaomi Dongfang Chemical Co., Ltd.), 3 parts by weight POE-g-MAH (CMG5805, Nantong Sunrise Molecular New Material Technology Co., Ltd.), 0.1 parts by weight β-crystal rare earth nucleating agent WBG-2 (purchased From Guangdong Weilinna Materials Co., Ltd.), 0.1 parts by weight of antioxidant 1010 (purchased from Ticiai (Shanghai) Chemical Industry Development Co., Ltd.) and 0.2 parts by weight of antioxidant 168 (purchased from Ticiai (Shanghai) Chemical Industry Development Co., Ltd.) Industrial Development Co., Ltd.) etc. are placed in a mixer, the speed of the mixer is 30rpm, and the mixture is mixed at a high speed for 3min.

[0039] (2) Put the mixture in step ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention discloses a toughened regenerated modified material manufactured through polyolefin materials of a waste medical plastic transfusion container and a manufacturing method and purpose of the toughened regenerated modified material. The toughened regenerated modified material is good in tenacity, easy to process, low in cost and suitable for manufacturing cold-resistant and shock-resisting materials.

Description

technical field [0001] The invention belongs to the field of waste resources reuse, in particular to the field of resource reuse of medical waste plastics. Specifically, the invention relates to toughened, regenerated and modified pellets prepared from polypropylene materials from waste medical plastic infusion containers. The invention also relates to its preparation method and use. Background technique [0002] At present, a large number of disposable plastic products are used in medical infusion container products, and the number of disposable plastic infusion containers (including disposable plastic bottles and plastic soft bags) and disposable plastic syringes is very large. However, while its use brings convenience, it also produces a large amount of waste, and the production of these plastic products requires a large consumption of petroleum resources. If these discarded medical plastic infusion containers are only landfilled and incinerated, it will not only waste r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/08C08L51/06C08K3/26C08K5/098
CPCC08L23/12C08K2201/003C08L2205/025C08L2205/035C08L2205/08C08L2205/242C08L2207/20C08L23/0815C08L51/06C08K13/02C08K2003/265C08K5/098C08K5/1345C08K5/526
Inventor 兰巧锋高峡刘伟丽
Owner BEIJING CENT FOR PHYSICAL & CHEM ANALYSIS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap