Titanium belt continuous pickling method

A pickling and titanium strip technology, which is applied in the field of chemical surface treatment of non-ferrous metal materials, can solve the problems of titanium strip pickling surface quality, titanium strip yield to be further improved, weak controllability of pickling quality, cumbersome pickling process, etc. , to achieve the effects of good pickling quality controllability, scientific and reasonable methods, and reduced production costs

Inactive Publication Date: 2014-09-24
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the pickling method adopted in the patent application CN102409352A realizes the continuous pickling of the titanium strip, it continuously pickles through three pickling tanks during the pickling step, the pickling process is cumbersome, and the pickling quality is controllable The ability is weak, the surface quality of titanium strip pickling and the yield of titanium strip need to be further improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] This embodiment is used to illustrate the continuous pickling method of the titanium strip of the present invention.

[0047] The annealed and shot-peened titanium strip is continuously passed through the pre-cleaning, primary pickling, intermediate cleaning, secondary pickling, final cleaning and drying process sections at a speed of 2m / min. The specific steps are as follows:

[0048] (1) Pre-cleaning: introduce the annealed and shot-peened titanium strip into the pre-cleaning tank, spray desalted water on the upper and lower surfaces of the titanium strip through the nozzle on the spray beam device, and remove the metal powder on the upper and lower surfaces of the titanium strip and the metal powder brought out during shot blasting. The steel shot is cleaned, and the water on the surface of the titanium strip is squeezed out with a squeeze roller;

[0049] (2) One-time pickling: guide the titanium belt out of the pre-cleaning tank into the first acid tank. The titani...

Embodiment 2

[0056] This embodiment is used to illustrate the continuous pickling method of the titanium strip of the present invention.

[0057] The annealed and shot-peened titanium strip is continuously passed through the pre-cleaning, primary pickling, intermediate cleaning, secondary pickling, final cleaning and drying process sections at a speed of 6m / min. The specific steps are as follows:

[0058] (1) Pre-cleaning: introduce the annealed and shot-peened titanium strip into the pre-cleaning tank, spray desalted water on the upper and lower surfaces of the titanium strip through the nozzle on the spray beam device, and remove the metal powder on the upper and lower surfaces of the titanium strip and the metal powder brought out during shot blasting. The steel shot is cleaned, and the water on the surface of the titanium strip is squeezed out with a squeeze roller;

[0059] (2) One-time pickling: guide the titanium belt out of the pre-cleaning tank into the first acid tank. The titani...

Embodiment 3

[0066] This embodiment is used to illustrate the continuous pickling method of the titanium strip of the present invention.

[0067] The annealed and shot-peened titanium strip is continuously passed through the pre-cleaning, primary pickling, intermediate cleaning, secondary pickling, final cleaning and drying process sections at a speed of 4m / min. The specific steps are as follows:

[0068] (1) Pre-cleaning: introduce the annealed and shot-peened titanium strip into the pre-cleaning tank, spray desalted water on the upper and lower surfaces of the titanium strip through the nozzle on the spray beam device, and remove the metal powder on the upper and lower surfaces of the titanium strip and the metal powder brought out during shot blasting. The steel shot is cleaned, and the water on the surface of the titanium strip is squeezed out with a squeeze roller;

[0069] (2) One-time pickling: guide the titanium belt out of the pre-cleaning tank into the first acid tank. The titani...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a titanium belt continuous pickling method, and the method comprises the following steps: (1) precleaning, to be more specific, cleaning the upper and lower surfaces of a titanium belt treated by annealing and shot peening; (2) first pickling, to be more specific, using a nitric acid and hydrofluoric acid mixed acid liquid for continuous pickling of the precleaned titanium belt; (3) intermediate cleaning, to be more specific, cleaning the upper and lower surfaces of the firstly pickled titanium belt; (4) second pickling, to be more specific, using the nitric acid and hydrofluoric acid mixed acid liquid for continuous pickling of the intermediately cleaned titanium belt; (5) final cleaning, to be more specific, cleaning the upper and lower surfaces of the secondly pickled titanium belt; and (6) drying, to be more specific, drying the upper and lower surfaces of the finally cleaned titanium belt. The method can improve and control pickled surface quality of the titanium belt, the pickling soluble loss rate can be controlled in real time, and a win-win situation of the pickled surface quality of the titanium belt and yield of the titanium belt can be achieved.

Description

technical field [0001] The invention belongs to a method for chemically treating the surface of nonferrous metal materials, in particular to a continuous pickling method for titanium strips. Background technique [0002] Pickling is a means of chemical surface treatment of non-ferrous metal materials. Its principle is to remove scale and rust on the metal surface through acid solution, and it is a method of cleaning the metal surface. [0003] As a non-ferrous metal, titanium will produce a layer of oxide scale on its surface after thermal processing. The pickling of titanium belt is to dissolve the surface oxide scale with mixed acid solution, and at the same time carry out passivation treatment to prevent the dissolution from accelerating and maintain pickling. The surface of the metal is silver-white. Since TiO is easily formed during thermal processing of titanium 2 Mainly oxide scale, so its pickling method is different from that of steel, but similar to that of stain...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23G3/02C23G1/10
Inventor 肖聪李军彭琳许震徐信
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products