Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of diamond grinding paste

A technology of diamond abrasive paste and diamond micropowder, which is applied in the direction of polishing compositions containing abrasives, other chemical processes, chemical instruments and methods, and can solve the problem of unsatisfactory microscopic geometry of abrasive materials and surface roughness that cannot meet technical requirements , Unsatisfactory composition of the abrasive paste, etc., to achieve good self-sharpening, reduced friction coefficient, and high self-lubrication

Active Publication Date: 2015-08-19
贵州荣清工具有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Special ceramics such as alumina ceramics, aluminum nitride ceramics, beryllium oxide ceramics, zirconia ceramics, and magnetic ceramics are widely used in military, electronics, communications, machinery and other industries after grinding and polishing. It is a common technical difficulty in the industry. There have always been problems that the surface roughness does not meet the technical requirements and the production yield is low. The key is that the current abrasive paste formula is not ideal, the particle dispersion characteristics are not good, and the microscopic geometry of the main abrasive materials The shape is not ideal, the volume size range of the abrasive material particles is too wide, and the lubricating properties of the components are not good, which makes the surface quality of special ceramics after grinding and polishing unsatisfactory, it is difficult to meet the quality requirements, and the product qualification rate is low

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Embodiment 1, the present invention is a kind of diamond abrasive paste, and it comprises following raw material, by weight, 20~50 parts of water, 5~30 parts of glycerin, 0.5~10 parts of polytetrafluoroethylene micropowder, 10~20 parts of diamond micropowder Part, its preparation method comprises the following steps:

[0020] (1) Accurately weigh each component according to the above parts by weight;

[0021] (2) Mix the components uniformly at a temperature of 80-100°C;

[0022] (3) Cool to -2-0°C to obtain the diamond grinding paste.

Embodiment 2

[0023] Embodiment 2, the present invention is a kind of diamond abrasive paste, and it comprises following raw material, by weight, 20~50 parts of water, 5~30 parts of glycerin, 0.5~10 parts of polytetrafluoroethylene micropowder, 10~20 parts of diamond micropowder parts, also including 10-40 parts of ethylene glycol or 20-50 parts of aviation kerosene, 20-50 parts of water-soluble stearic acid or 20-50 parts of engine oil, and its preparation method comprises the following steps:

[0024] (1) Accurately weigh each component according to the above parts by weight;

[0025] (2) Mix the components uniformly at a temperature of 90-100°C;

[0026] (3) Cool to -2-0°C to obtain the diamond grinding paste.

Embodiment 3

[0027] Embodiment 3, the present invention is a kind of diamond abrasive paste, and it comprises following raw material, by weight, 20~60 parts of water, 5~30 parts of glycerin, 0.5~10 parts of polytetrafluoroethylene micropowder, 10~20 parts of diamond micropowder parts, also including 15-30 parts of ethylene glycol or 30-40 parts of aviation kerosene, 25-40 parts of water-soluble stearic acid or 25-40 parts of machine oil, and its preparation method comprises the following steps:

[0028] (1) Accurately weigh each component according to the above parts by weight;

[0029] (2) Mix the components uniformly at a temperature of 80-100°C;

[0030] (3) Cool to -1-0°C to obtain the diamond grinding paste.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
surface roughnessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a diamond grinding paste and belongs to the technical field of grinding materials. The diamond grinding paste comprises the following raw materials in parts by weight: 20-50 parts of water, 5-30 parts of glycerin, 0.5-10 parts of Teflon micro powder and 10-20 parts of diamond micro powder. The diamond grinding paste is capable of improving dispersity of diamond micro powder and guaranteeing the grinding effect of special-type ceramic, and is applicable in oil and water mediums.

Description

technical field [0001] The invention relates to a diamond grinding paste, which belongs to the technical field of grinding materials. Background technique [0002] Special ceramics such as alumina ceramics, aluminum nitride ceramics, beryllium oxide ceramics, zirconia ceramics, and magnetic ceramics are widely used in military, electronics, communications, machinery and other industries after grinding and polishing. It is a common technical difficulty in the industry. There have always been problems that the surface roughness does not meet the technical requirements and the production yield is low. The key is that the current abrasive paste formula is not ideal, the particle dispersion characteristics are not good, and the microscopic geometry of the main abrasive materials The shape is not ideal, the volume size range of the abrasive material particles is too wide, and the lubricating properties of the components are not good, which makes the surface quality of special cera...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09G1/02C09K3/14
Inventor 张豪
Owner 贵州荣清工具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com