Method for producing packaging steel

A technology for packaging and steel plates, used in the manufacture of tools, transportation and packaging, chemical instruments and methods, etc.

Active Publication Date: 2014-08-27
THYSSENKRUPP AG
View PDF10 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Furthermore, many known dual-phase steels have such high strengths that they cannot be cold-rolled with the equipment normally used to manufacture packaging steels

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing packaging steel
  • Method for producing packaging steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] Elaborate the present invention according to an embodiment below:

[0018] In order to produce the steel sheet according to the invention as an example of packaging steel, the steel strip produced by continuous casting and hot rolled and wound on the coil consists of a steel with the following composition:

[0019] -C: 0.1% max;

[0020] -N: 0.02% max;

[0021] - Mn: maximum 0.5%, preferably less than 0.4%;

[0022] - Si: maximum 0.04%, preferably less than 0.02%;

[0023] - Al: maximum 0.1%, preferably less than 0.05%;

[0024] - Cr: maximum 0.1%, preferably less than 0.05%;

[0025] -P: 0.03% max,

[0026] -Cu: 0.1% max,

[0027] -Ni: 0.1% max,

[0028] -Sn: 0.04% max,

[0029] -Mo: 0.04% max,

[0030] -V: 0.04% max;

[0031] - Ti: maximum 0.05%, preferably less than 0.02%;

[0032] - Nb: maximum 0.05%, preferably less than 0.02%;

[0033] -B: 0.005% max

[0034] - and other alloy constituents, including impurities: max. 0.05%;

[0035] - The rest is iron....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
yield pointaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for producing packaging steel consisting of a cold-rolled steel sheet made of unalloyed or low-alloy steel having a carbon content of less than 0.1%. In order to provide high-strength packaging steel that has good formability and high corrosion resistance and can be produced in as energy-saving a manner as possible, the steel sheet according to the invention is first coated with a metallic coating and then annealed in a recrystallising manner at a heating rate of more than 75 K / s and preferably more than 100 K / s to temperatures of more than 700 DEG C, such that the metallic coating melts. The coated and annealed steel sheet is then quenched to normal temperature at a cooling rate of at least 100 K / s.

Description

technical field [0001] The invention relates to a method for producing packaging steel from a cold-rolled steel sheet according to the preamble of claim 1 . Background technique [0002] Thin-walled steel products in the form of plates or strips and a method for their production are known from CH 469 810, which can be used for the production of tinplate with higher strength. Steel articles made of unalloyed steel with a carbon content of 0.03% by weight to 0.25% by weight and having a manganese content of 0.2% by weight to 0.6% by weight and a silicon content of less than 0.011% by weight . The steel article is characterized by a microstructure consisting at least in part of martensite and ferrite and having a 2 Tensile strength and elongation at break of at least 1.5%. To develop this property, the steel product is first heated in a furnace to A 1 point and then quenched in a water bath. [0003] Higher demands are increasingly placed on the properties of the metallic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C21D8/02C22C38/00C23C2/26C23C2/28C23C2/06
CPCC23C2/28C21D2211/008C22C38/22C23C2/06C22C38/54B32B15/015C22C38/04C21D1/42C22C38/24C22C38/001C22C38/26Y10T428/12799B32B15/012C22C38/48Y10T428/12757C22C38/20B65D1/12Y10T428/12972C22C38/44Y10T428/12854C22C38/06C22C38/004B32B15/01C21D2211/005C21D1/26C22C38/32C21D2211/001C22C38/008C22C38/28C21D8/0273C22C38/002B32B15/013C21D8/0236C21D9/52C22C38/18C22C38/02C22C38/46C23F17/00Y10T428/12C22C38/42C21D9/46C23C2/26C22C38/50Y10T428/12722C21D2211/002C21D1/18Y02P10/25
Inventor 阿妮卡·塞斯尼赫尔穆特·奥伯霍费尔马丁·施卢普迪尔克·马图舍克赖纳·绍尔
Owner THYSSENKRUPP AG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com