Aqueous protective coating material, application thereof and titanium ingot production method

A protective coating, water-based technology, applied in the direction of coating, etc., can solve the problems of unsatisfactory protection of titanium ingots, achieve the effects of increasing production costs and production time, reducing production costs, and reducing the formation of dissolved oxygen layers

Active Publication Date: 2014-08-20
PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
View PDF2 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the defect that the existing water-based protective coating is not ideal for the protection of titanium ingots, to provide a new water-based protective coating and its application and production method for titanium ingots

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous protective coating material, application thereof and titanium ingot production method
  • Aqueous protective coating material, application thereof and titanium ingot production method
  • Aqueous protective coating material, application thereof and titanium ingot production method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0029] There is no special requirement for the preparation method of the water-based protective coating of the present invention, and various methods commonly used in the art can be used, as long as the components are mixed uniformly. However, the inventors of the present invention found in their research that the following method can be used to prepare the water-based protective coating, which can make the components mix more uniformly. The specific method is: under stirring, slowly add the oxidation protection agent into the water-soluble film-forming agent, when the amount of the oxidation protection agent is added in half, start to slowly add 3-5% of water, and make the oxidation protection agent and 3-5 % of water is added together, then add curing agent, stir evenly, then add dispersant, stir until the liquid is in a uniform and stable phase, then add thickener, stir evenly and then add the remaining water.

[0030] In the second aspect, the present invention provides th...

Embodiment 1

[0045] This embodiment is used to illustrate the production method of water-based protective coating and titanium ingot of the present invention.

[0046] (1) At normal temperature and pressure (25°C, 0.1MPa), weigh 100g of styrene-acrylic emulsion (solid content 50% by weight) and place it in a container;

[0047] (2) Weigh 800g Al powder, 50g Sn powder and 50g Cu powder, and slowly add them into the container under stirring. Powder, Sn powder, Cu powder and water are added together;

[0048] (3) Weigh 1g SiO 2 , add to the container, and stir evenly;

[0049] (4) Weigh 0.5g polyvinyl alcohol (purchased from Qingdao Anmao International Trade Co., Ltd., Z-200) into the container, stir until the liquid is in a uniform and stable phase;

[0050] (5) Weigh 1 g of carboxymethyl cellulose (purchased from Hebei Xingtai Cellulose Co., Ltd., XTHPMC10) into a container, stir evenly, add water to make the volume to 1 L, and obtain water-based protective coating A1.

[0051] The meas...

Embodiment 2

[0054] This embodiment is used to illustrate the production method of water-based protective coating and titanium ingot of the present invention.

[0055] (1) At normal temperature and pressure (25°C, 0.1MPa), weigh 54g of styrene-acrylic emulsion (solid content 40% by weight) and place it in a container;

[0056] (2) Weigh 770g of Al powder, 40g of Sn powder and 40g of Cu powder, and slowly add them into the container under stirring. Powder, Sn powder, Cu powder and water are added together;

[0057] (3) Weigh 1.7g SiO2 2 , add to the container, and stir evenly;

[0058] (4) Weigh 0.68g of polyvinylpyrrolidone (purchased from Guangzhou Batai Chemical Co., Ltd., PVPK90) into the container, stir until the liquid is in a uniform and stable phase;

[0059] (5) Weigh 3.4 g of hydroxyethyl cellulose (purchased from Hebei Xingtai Cellulose Co., Ltd., YLT-999) into a container, stir evenly, add water to make the volume to 1 L, and obtain water-based protective coating A2.

[0060...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses an aqueous protective coating material. The aqueous protective coating material is obtained after a raw material mixture is uniformly mixed, wherein the raw material mixture contains an oxidation protecting agent, a water-soluble film forming agent and water; the oxidation protecting agent contains Al powder, Sn powder and Cu powder which are in the weight ratio of 1: (0.01-0.1): (0.01-0.1). The invention further discloses application of the aqueous protective coating material in titanium ingot production and a titanium ingot production method. The aqueous protective coating material disclosed by the invention has the advantages that the condition that the surface of a titanium ingot is not subjected to oxidation cracking under the condition that the titanium ingot is subjected to constant temperature for 8 hours at the high temperature of 1,000 DEG C can be guaranteed, and the formation of an oxygen dissolved layer can be greatly reduced; the aqueous protective coating material has an environmental-friendly effect; the preparation process is simple; a variety of coating manners can be adopted. The titanium ingot production method disclosed by the invention has good economic and social benefits and has relatively broad popularization and application prospects in titanium plate and titanium tube production industries.

Description

technical field [0001] The invention relates to the field of metal high-temperature-resistant coatings, in particular to a water-based protective coating, the application of the water-based protective coating in the production of titanium ingots, and a production method for titanium ingots. Background technique [0002] Titanium ingots generally undergo annealing treatment during the production process. Annealing is generally carried out at a high temperature of about 900°C. At high temperatures, oxygen will enter the surface of the titanium ingot to form a hard dissolved oxygen layer. The titanium ingot is heated at 900°C for 4 hours. Deep cracks with a depth of about 20mm will appear on the above surface. In order to ensure the subsequent rolling of titanium tubes and the surface quality of hot-rolled titanium plates, it is necessary to cut and grind the titanium ingots during the rolling process to remove cracks and dissolved oxygen layers, which results in large losses. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D7/12C21D1/68
Inventor 许哲峰李军王莹彭琳肖聪
Owner PANZHIHUA IRON & STEEL RES INST OF PANGANG GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com