Root-resisting TPO (thermoplastic polyolefin) waterproof coating and preparation process thereof

A waterproof coating and root-blocking technology, applied in the direction of coating, etc., can solve the problems of poor weather resistance, loss of waterproof effect when separated from the base layer, easy air bubbles, etc., and achieve the effect of good mixing performance, easy processing, and low volatility

Inactive Publication Date: 2014-06-25
王勇
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the construction of this kind of coating is simple, its weather resistance is poor. It is easy to bubble after being soaked in alkaline substances for a long time, and it loses its waterproof effect when it is separated from the base layer.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A root-blocking TPO waterproof coating, its components and mass ratio are: TPO: 40%; EPPE: 20%; root-blocking agent: 7%; active calcium: 10%; anti-aging agent: 3%; aromatic oil: 20%; plasticizer DOP: 3%.

Embodiment 2

[0019] Embodiment 2: a kind of preparation technology of root resistance TPO waterproof coating, the steps are as follows:

[0020] 1) According to the mass ratio, select the appropriate metering raw materials, the raw materials are as follows: TPO, EPPE, root inhibitor, active calcium, anti-aging agent, aromatic oil, plasticizer DOP.

[0021] 2) Add the above-mentioned raw materials into the batching mixing tank, and heat to an appropriate temperature for sufficient stirring.

[0022] 3) After the raw materials in the mixing tank come out, they enter the colloid mill for grinding to ensure that the raw materials are pure, hygienic and pollution-free.

[0023] 4), the raw materials from step 3) enter the cooling and stirring tank to make a root-resistant TPO waterproof coating.

[0024] 5), the waterproof coating that comes out in step 4) is inspected and tested, packed and stored in storage, and made into a root-blocking TPO waterproof coating that meets the standards.

[0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a root-resisting TPO (thermoplastic polyolefin) waterproof coating and a preparation process thereof. The root-resisting TPO waterproof coating comprises the following components in percentage by weight: 30-50 percent of TPO (thermoplastic polyolefin), 10-30 percent of EPPE (Easy Processing Polythene), 4-8 percent of root resisting agent, 5-15 percent of active calcium, 1-5 percent of anti-aging agent, 10-35 percent of aromatic hydrocarbon oil and 1-4 percent of plasticizer DOP (Dioctyl-Phthalate). The root-resisting TPO waterproof coating has the advantages of convenient construction, good aging resistance, high tensile strength, large elongation, no need of a protection layer during exposure, and low cracking rate of a coating layer after the coating is cured; and a good waterproof effect can be kept for a long time.

Description

technical field [0001] The invention belongs to the field of waterproof coatings, in particular to a root-blocking TPO waterproof coating. Background technique [0002] Waterproof materials are widely used in the field of building material protection. After coating the building with waterproof coating, the building can be isolated from the external environment, thereby preventing the intrusion of rainwater, groundwater and other corrosive liquids and moisture in the air into the building. corrosion caused by building materials and prolong the service life of building materials. [0003] Waterproof materials mainly include waterproof coatings and waterproof membranes. Among them, waterproof membranes mainly include asphalt waterproof membranes, modified asphalt waterproof membranes, polymer waterproof membranes, etc. The construction process of waterproof membranes is complicated, and the requirements for construction personnel are high, so the application range is narrow. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D123/00C09D201/00C09D5/00C09D7/12
Inventor 王勇
Owner 王勇
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap