Cu-containing high-conductivity and high-electromagnetic-shielding-property wrought magnesium alloy and preparation method thereof

A deformation magnesium alloy, electromagnetic shielding technology, applied in the field of magnesium alloys, to achieve the effect of increased electrical conductivity, excellent electrical conductivity, good electromagnetic shielding performance

Active Publication Date: 2014-06-11
CHONGQING UNIV
View PDF3 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] For the deficiencies of existing electromagnetic shielding materials, the purpose of the invention is to provide a kind of deformed magnesium alloy containing Cu with high conductivity and high electromagnetic shielding performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cu-containing high-conductivity and high-electromagnetic-shielding-property wrought magnesium alloy and preparation method thereof
  • Cu-containing high-conductivity and high-electromagnetic-shielding-property wrought magnesium alloy and preparation method thereof
  • Cu-containing high-conductivity and high-electromagnetic-shielding-property wrought magnesium alloy and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0038] A method for preparing a Cu-containing deformed magnesium alloy with high electrical conductivity and high electromagnetic shielding performance, the method comprises the steps of:

[0039] a) Melting ingot: in SF 6 +CO 2 Under the protection of gas, put the Mg ingot into the crucible and heat up to 740~760°C after melting, then add pure Zn ingot, Mg-30%Cu, Mg-28.54%Zr master alloy according to the ratio of the above-mentioned magnesium alloy composition; add The method is: preheat the pure Zn ingot, Mg-30%Cu, Mg-28.54%Zr master alloy at 140~220°C for 15~30 minutes, quickly press it into the molten Mg ingot below the liquid level, and after melting Stir, and start refining for 5-10 minutes when the temperature of the melt rises to 750°C. The stirred alloy melt is left to stand at 730-750°C for 10-30 minutes. Casting is carried out in an iron mold, and the casting temperature is 710~730°C;

[0040] b) Homogenization: surface turning the ingot obtained in step a) to re...

Embodiment 1

[0042] Embodiment 1: the Mg-Zn-Zr magnesium alloy containing Cu of the present embodiment, its composition is by weight percentage:

[0043] Zn: 4.96 wt.%;

[0044] Zr: 0.71 wt.%;

[0045] Cu: 0.37 wt.%

[0046] The balance is Mg and unavoidable impurities, the total amount of which is less than 0.06 wt.%.

[0047] According to above-mentioned proportioning and following preparation method, just can obtain the magnesium alloy of the present embodiment:

[0048] a) Smelting ingot: in SF 6 +CO 2Under gas protection, put the Mg ingot into the crucible and heat up to 740°C (or 750°C, 760°C) after melting, and add pure Zn ingot according to the composition ratio of Example 1, Mg-30%Cu, Mg-28.54% Zr master alloy; adding method: preheat the pure Zn ingot, Mg-30%Cu, Mg-28.54%Zr master alloy at 170°C (or 140°C, 210°C) for 25 minutes, and quickly press it into the Mg ingot to melt Below the liquid level after melting, stir after melting, start refining for 5-10 minutes when the me...

Embodiment 2

[0051] Embodiment 2: the Mg-Zn-Zr magnesium alloy containing Cu of the present embodiment, its composition is by weight percentage:

[0052] Zn: 5.01 wt.%,

[0053] Zr: 0.78 wt.%;

[0054] Cu: 0.82 wt.%;

[0055] %。 The balance is Mg and unavoidable impurities, the total amount of impurities is less than 0.06 wt.%.

[0056] The method of smelting ingot-homogenization-hot extrusion to obtain the magnesium alloy of this example is the same as that of Example 1, except that the composition ratio of the smelting alloy is different.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Conductivityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a Cu-containing high-conductivity and high-electromagnetic-shielding-property wrought magnesium alloy which comprises the following components in percentage by weight: 4.90-5.20% of Zn, 0.50-0.80% of Zr, 0.37-2.32% of Cu and the balance of Mg and unavoidable impurities. The preparation method comprises the steps of ingot smelting, homogenization, hot extrusion and the like, because the alloy contains Cu, and Cu, Mg and Zn are combined so as to generate a MgZnCu ternary phase, Zn solute atoms in a matrix are greatly reduced, the lattice distortion of the matrix decreases, and electron scattering is inhibited. Therefore, the alloy subjected to homogenization and extrusion has good conductivity, the electromagnetic shielding property of the alloy is markedly improved, and compared with alloys without containing Cu, the alloy has the advantages that the electromagnetic shielding effectiveness is increased by over 17db. The application scope of high-conductivity, high-electromagnetic-shielding-property and light-weight alloy materials in the fields of aerospace, military industry, microelectronics, and the like is effectively broadened.

Description

technical field [0001] The invention relates to a magnesium alloy, in particular to a deformed magnesium alloy containing Cu with high electrical conductivity and high electromagnetic shielding performance and a preparation method thereof. [0002] Background technique [0003] Electromagnetic radiation, also known as electronic smog, is composed of electric energy and magnetic energy transferred together in space, and the energy is generated by the movement of electric charges. In recent years, besides noise pollution, water pollution, air pollution, and solid waste pollution, electromagnetic radiation has become the fifth largest pollution. In commercial scientific electronic instruments, telecommunication systems, and military electronic instruments, how to shield electromagnetic radiation is a major problem, which seriously perplexes many contemporary researchers. Because it is invisible, intangible, and acts directly on objects, it is a serious "invisible killer". El...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C22C23/04C22C1/03C22F1/06
Inventor 陈先华潘复生刘莉滋
Owner CHONGQING UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com