Process for producing calcium sulfate whiskers from chlorine-containing wastewater from titanium white by chlorination

A technology of calcium sulfate whisker and chloride method, which is applied in chemical instruments and methods, calcium/strontium/barium sulfate, single crystal growth, etc., can solve the problem that titanium white chlorine-containing wastewater is not economically feasible and has economic benefits Deal with technology and other issues to achieve the effect of improving the level of clean production, low cost and environmental friendliness

Active Publication Date: 2016-08-17
中信钛业股份有限公司
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So far, there is no economically feasible and economically beneficial treatment technology for chlorine-containing wastewater from chlorinated titanium dioxide.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Process for producing calcium sulfate whiskers from chlorine-containing wastewater from titanium white by chlorination

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] ①. Collect, settle, purify and filter the wastewater containing calcium chloride (mainly calcium chloride and sodium chloride) from chlorinated titanium white to make the Ca in the wastewater 2+ content ≥ 50g / L, Cl - content of ≥100g / L, content of ΣFe≤20ppm, Pb 2+ 、 Bi 3+ 、Cd 2+ content of ≤5ppm, store for future use;

[0023] ②, will produce vanadium pentoxide containing Na 2 SO 4 After the waste water is collected, settled, purified and filtered, the SO in the waste water 4 2- The content of ≥50g / L, the content of ΣFe≤20ppm, Cr 6+ content of ≤5ppm, store for future use;

[0024] ③. Ca in the solution obtained according to step ① 2+ and SO in the solution obtained in step ② 4 2- Molar ratio 1:1.5 Mix step ① and step ② solution to react, stir, heat to 80°C, add sulfuric acid to adjust to pH = 4; add magnesium chloride simultaneously and make accelerator, the add-on of described magnesium chloride is 3% of product calcium sulfate theoretical weight, and the r...

Embodiment 2

[0031] ①. Collect, settle, purify and filter the wastewater containing calcium chloride (mainly calcium chloride and sodium chloride) from chlorinated titanium white to make the Ca in the wastewater 2+ content ≥ 50g / L, Cl - content of ≥100g / L, content of ΣFe≤20ppm, Pb 2+ 、 Bi 3+ 、Cd 2+ content of ≤5ppm, store for future use;

[0032] ②. Dissolve Glauber's salt, a by-product of the production of red alum sodium, in vanadium pentoxide wastewater, settle, purify, and Cr 6+ After reduction to chromium hydroxide and filtration, the SO in the wastewater 4 2- The content of ≥100g / L, the content of ΣFe≤20ppm, Cr 6+ content of ≤5ppm, store for future use;

[0033] ③. Ca in the solution obtained according to step ① 2+and SO in the solution obtained in step ② 4 2- Molar ratio 1:1.15 Mix step ① and step ② solution to react, stir, heat to 60°C, add sulfuric acid to adjust to pH = 2; adding magnesium chloride simultaneously is made accelerator, and the add-on of described magnesi...

Embodiment 3

[0040] ①. Collect, settle, purify and filter the wastewater containing calcium chloride (mainly calcium chloride and sodium chloride) from chlorinated titanium white to make the Ca in the wastewater 2+ content ≥ 50g / L, Cl - content of ≥100g / L, content of ΣFe≤20ppm, Pb 2+ 、 Bi 3+ 、Cd 2+ content of ≤5ppm, store for future use;

[0041] ②. The subsidence waste liquid from the production of Haibo contains the main amount of Na 2 SO 4 , the rest Na 2 S 2 o 3 、Na 2 SO 3 , first put S 2 o 3 -2 , SO 3 -2 Oxidation to SO 4 2- Finally, after collecting, settling, purifying and filtering, the SO in the wastewater 4 2- The content of ≥200g / L, the content of ΣFe≤20ppm, Cr 6+ content of ≤5ppm, store for future use;

[0042] ③. Ca in the solution obtained according to step ① 2+ and SO in the solution obtained in step ② 4 2- The molar ratio is 1:1.25. Mix the solution of step ① and step ② for reaction, stir, heat to 100°C, add sulfuric acid to adjust the pH = 5; add ma...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
aspect ratioaaaaaaaaaa
whitenessaaaaaaaaaa
Login to view more

Abstract

A process for producing calcium sulfate whiskers from chlorine-containing wastewater from chlorinated titanium white. The chlorine-containing wastewater and sodium sulfate-containing wastewater from chlorinated titanium white are collected, settled, purified, and filtered, respectively, and then mixed. React, stir, heat, add sulfuric acid to adjust the pH value; at the same time, add magnesium chloride as a growth agent, put it in a crystallization tank for aging and crystallization to obtain calcium sulfate crystals, filter, add H2SO4 buffer and heat to boiling, heat filter and use deionization at the same time Wash with water to obtain calcium sulfate whiskers, send them to a fluidized bed dryer for drying and dehydration, and pack to obtain anhydrous calcium sulfate whiskers. The process is simple, the cost is low, industrialized production can be realized, and waste water can be comprehensively utilized.

Description

technical field [0001] The present invention relates to a process for producing calcium sulfate whiskers from chlorine-containing wastewater from chlorinated titanium white, in particular to a co-production process for producing calcium sulfate whiskers from chlorine-containing wastewater from chlorinated titanium white while recovering industrial sodium chloride . Background technique [0002] Calcium sulfate whiskers have excellent mechanical properties, good compatibility, excellent smoothness, and good regeneration performance. They are mainly used in papermaking, added components of composite materials, friction materials, environmental engineering filtration, asphalt modification and Improve the adhesion, temperature resistance and insulation of coatings and paints. At present, the production method of calcium sulfate whiskers is to use gypsum as the raw material and grow in the form of single crystals through artificial control. It is a fibrous (whisker-like) single ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C30B7/14C30B29/22C30B29/62C01F11/46
Inventor 齐牧崔传海刘长河韩艳芝任彤郭一冰杨洪岩崔小莉李继奎
Owner 中信钛业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap