A high temperature resistant urban rail cable sheath material

A technology for cable sheathing and high temperature resistance, which is applied in the direction of plastic/resin/wax insulators, organic insulators, rubber insulators, etc. It can solve the problems of unsatisfactory demand and increased usage, so as to reduce usage, improve plasticity, and prevent scorching. burning effect

Inactive Publication Date: 2016-03-09
ANHUI HUALIAN CABLE GROUP
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the continuous development of the domestic economy and the acceleration of urbanization, urban rail transit, as a basic public welfare facility to solve urban travel convenience, has been widely recognized in many cities because of its fast, safe, comfortable, convenient, energy-saving and environmentally friendly features. With large-scale construction, urban rail cables have been widely used, among which the use of fire-resistant cables has increased significantly. In some important departments and public places, after a fire occurs, the packaging line can run normally for a period of time, which is of great help to rescue work. And can reduce casualties and property losses to a great extent. The outermost layer of the urban rail cable is a sheath, which is generally rubber or rubber synthetic sheath. The function of the sheath is to insulate and protect the cable from damage. Its fire resistance performance is the most important Good or bad plays a vital role in the safe operation of urban rail cables. Although a variety of fire-resistant cable sheath materials have been developed, they still cannot meet the needs. How to prepare a flame-retardant, environmentally friendly, and long-lasting urban rail Cable sheath material has become a technical problem that needs to be solved at present

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A high temperature resistant urban rail cable sheath material, including main materials and auxiliary materials:

[0015] The main material comprises by weight: 27 parts of epoxy resin, 13 parts of chloroprene rubber and 18 parts of natural rubber;

[0016] The auxiliary materials include by weight: 1.2 parts of zinc oxide, 0.8 parts of active agent iron oxide, 0.5 parts of barium oxide, 0.6 parts of stearic acid, 0.4 parts of methyl thiuram disulfide, 1.1 parts of N,N-di(ε -caprolactam) disulfide, 0.15 parts of ethylene thiourea, 0.8 parts of tetralead sulfate, 0.5 parts of dioctyl phthalate, 1.3 parts of microcrystalline paraffin, 0.7 parts of anti-aging agent IPPD, 0.7 parts of isoadipate Octydecyl ester, 0.22 parts of antioxidant 445, 3.4 parts of high wear-resistant carbon black, 8.7 parts of titanium dioxide, 4.5 parts of diatomaceous earth, 9.9 parts of calcium carbonate;

[0017] Put the main material into an open mill and mix evenly, the mixing temperature is ...

Embodiment 2

[0019] A high temperature resistant urban rail cable sheath material, including main materials and auxiliary materials:

[0020] The main material comprises by weight: 27 parts of epoxy resin, 15 parts of chloroprene rubber and 18 parts of natural rubber;

[0021] The auxiliary materials include by weight: 1.2 parts of zinc oxide, 0.6 parts of active agent iron oxide, 0.5 parts of barium oxide, 0.8 parts of stearic acid, 0.4 parts of methyl thiuram disulfide, 1.3 parts of N,N-di(ε -caprolactam) disulfide, 0.2 parts of ethylene thiourea, 0.8 parts of tetralead sulfate, 0.45 parts of dioctyl phthalate, 1.3 parts of microcrystalline paraffin, 0.9 parts of anti-aging agent IPPD, 0.5 parts of isoadipate Octydecyl ester, 0.2 parts of anti-aging agent 445, 4.4 parts of high wear-resistant carbon black, 8 parts of titanium dioxide, 3.5 parts of diatomaceous earth, 10 parts of calcium carbonate;

[0022] Put the main material into an open mill and mix evenly, the mixing temperature is...

Embodiment 3

[0024] A high temperature resistant urban rail cable sheath material, including main materials and auxiliary materials:

[0025] The main material comprises by weight: 28 parts of epoxy resin, 16 parts of chloroprene rubber and 13 parts of natural rubber;

[0026] The auxiliary materials include by weight: 1 part of zinc oxide, 1.1 part of active agent iron oxide, 0.5 part of barium oxide, 0.7 part of stearic acid, 0.4 part of methyl thiuram disulfide, 1.3 parts of N,N-di(ε -caprolactam) disulfide, 0.25 parts of ethylene thiourea, 0.8 parts of tetralead sulfate, 0.33 parts of dioctyl phthalate, 1.25 parts of microcrystalline paraffin, 0.9 parts of anti-aging agent IPPD, 0.68 parts of isoadipate Octydecyl ester, 0.24 parts of antioxidant 445, 4.4 parts of high wear-resistant carbon black, 8.8 parts of titanium dioxide, 3.55 parts of diatomaceous earth, 11 parts of calcium carbonate;

[0027] Put the main material into an open mill and mix evenly, the mixing temperature is 66°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-temperature resistant urban rail cable sheath material, which comprises major ingredients and auxiliaries, wherein the major ingredients comprise epoxy resin, chloroprene rubber and natural rubber; the auxiliaries comprise zinc oxide, a ferric oxide activating agent, barium oxide, stearic acid, methylthiuram disulfide N,N-bi(epsilon-caprolactam)disulfide, ethylene thiourea, tribasic lead sulfate, dioctyl phthalate, microcrystalline wax, an anti-aging agent IPPD, octyl decyl adipate, an anti-aging agent 445, high-abrasion resistance carbon black, titanium dioxide, diatomaceous earth and calcium carbonate. A preparation method for the high-temperature resistant urban rail cable sheath material comprises the following steps of uniformly mixing the major ingredients at mixing temperature of 63 to 67 DEG C in an open mill, adding the auxiliaries and uniformly mixing; vulcanizing the obtained material mixture on a flat vulcanizing machine to obtain the high-temperature resistant urban rail cable sheath material, wherein the vulcanizing temperature is 145 to 148 DEG C, and the vulcanizing time is 2 to 4 minutes. The high-temperature resistant urban rail cable sheath material is flame-retardant, environment-friendly and long in service life.

Description

technical field [0001] The invention relates to the technical field of urban rail cable sheath materials, in particular to a high-temperature-resistant urban rail cable sheath material. Background technique [0002] With the continuous development of the domestic economy and the acceleration of urbanization, urban rail transit, as a basic public welfare facility to solve urban travel convenience, has been widely recognized in many cities because of its fast, safe, comfortable, convenient, energy-saving and environmentally friendly features. With large-scale construction, urban rail cables have been widely used, among which the use of fire-resistant cables has increased significantly. In some important departments and public places, after a fire occurs, the packaging line can run normally for a period of time, which is of great help to rescue work. And can reduce casualties and property losses to a great extent. The outermost layer of the urban rail cable is a sheath, which i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L63/00C08L11/00C08L7/00C08K13/02C08K3/22C08K5/09C08K5/40C08K5/405C08K3/30C08K5/12C08K5/11C08K3/04C08K3/34C08K3/26B29C35/02H01B3/40H01B3/28
Inventor 毛爱民张学武梁继强卢英鹏范德俊翟德玉章少东
Owner ANHUI HUALIAN CABLE GROUP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com